A molded body is produced from a molding material including a continuous phase and a dispersed phase by a three-dimensionalization step, a curing step, and a peeling step. The continuous phase of the molding material is a water phase containing a curable compound. In the three-dimensionalization step, the molding material is placed in a container. In the curing step, the curable compound is cured to form a cured product after the three-dimensionalization step. In the peeling step, the container and the cured product are separated after the curing step. In the dispersed phase removal step, the dispersed phase of the cured product is removed after the curing step.

A manufacturing method for a coating liquid, including: a preparing step of preparing aerogel particles, a water-soluble polymer having a hydrophobic group, and a liquid medium; and a mixing step of mixing the aerogel particles, the water-soluble polymer, and the liquid medium prepared in the preparing step and aggregating the aerogel particles to obtain a coating liquid containing aggregates of the aerogel particles, the water-soluble polymer, and the liquid medium.

A manufacturing method for a coating liquid, including: a preparing step of preparing aerogel particles, a water-soluble polymer having a hydrophobic group, and a liquid medium; and a mixing step of mixing the aerogel particles, the water-soluble polymer, and the liquid medium prepared in the preparing step and aggregating the aerogel particles to obtain a coating liquid containing aggregates of the aerogel particles, the water-soluble polymer, and the liquid medium.

A method for preparing a modified cellulose aerogel for glycoprotein separation is provided. In this method, cellulose aerogel is employed as a substrate. The cellulose aerogel is known to have a three-dimensional network structure with extremely high porosity and specific surface area and extremely low density. So, by using the cellulose aerogel as a substrate, it is possible to provide the glycoproteins to be separated with more binding sites. PEI dendrimer has abundant functional groups and can easily be modified. By modifying the cellulose aerogel substrate with the PEI dendrimer, it is possible to improve the density of the phenylboronic acid bound to the substrate, thereby leading to higher affinity toward the glycoproteins to be separated.

A method for preparing a modified cellulose aerogel for glycoprotein separation is provided. In this method, cellulose aerogel is employed as a substrate. The cellulose aerogel is known to have a three-dimensional network structure with extremely high porosity and specific surface area and extremely low density. So, by using the cellulose aerogel as a substrate, it is possible to provide the glycoproteins to be separated with more binding sites. PEI dendrimer has abundant functional groups and can easily be modified. By modifying the cellulose aerogel substrate with the PEI dendrimer, it is possible to improve the density of the phenylboronic acid bound to the substrate, thereby leading to higher affinity toward the glycoproteins to be separated.

The combined use of polyol esters and cationic polyelectrolytes as additives in cosurfactant-containing aqueous polymer dispersions for production of porous polymer coatings, preferably for production of porous polyurethane coatings, is described.

The combined use of polyol esters and cationic polyelectrolytes as additives in cosurfactant-containing aqueous polymer dispersions for production of porous polymer coatings, preferably for production of porous polyurethane coatings, is described.

A film is provided with void spaces having a porous structure with less cracks and a high proportion of void space as well as having strength. The film with void spaces includes one kind or two or more kinds of structural units that form a structure with minute void spaces, wherein the structural units are chemically bonded through catalysis. For example, the abrasion resistance measured with BEMCOT® is in the range from 60% to 100%, and the folding endurance measured by the MIT test is 100 times or more. The film with void spaces can be produced by forming the precursor of the silicone porous body using sol containing pulverized products of a gelled silicon compound and then chemically bonding the pulverized products contained in the precursor of the silicone porous body. The chemical bond among the pulverized products is preferably a chemical crosslinking bond among the pulverized products.

A film is provided with void spaces having a porous structure with less cracks and a high proportion of void space as well as having strength. The film with void spaces includes one kind or two or more kinds of structural units that form a structure with minute void spaces, wherein the structural units are chemically bonded through catalysis. For example, the abrasion resistance measured with BEMCOT® is in the range from 60% to 100%, and the folding endurance measured by the MIT test is 100 times or more. The film with void spaces can be produced by forming the precursor of the silicone porous body using sol containing pulverized products of a gelled silicon compound and then chemically bonding the pulverized products contained in the precursor of the silicone porous body. The chemical bond among the pulverized products is preferably a chemical crosslinking bond among the pulverized products.

The present invention concerns a solid nanocomposite material consisting of a polymer-matrix in which are dispersed alkali metal, hydronium or ammonium salts of polyanionic components, wherein the polymer-matrix comprises at least a linear or branched polymer or copolymer containing one or several poly(ethylene oxide) (PEO) chains, said polymer or copolymer being optionally crosslinked and each PEO chain having at least 4 ethylene oxide monomer units. The present invention relates also to a photonic, e.g. optoelectronic, device comprising such a nanocomposite material. Such material and device can be used as phosphorescence emitter, for crop growth lighting or for generating singlet oxygen.