The present invention relates to a polyvinyl acetal resin film, comprising a polyvinyl acetal resin material, wherein the polyvinyl acetal resin film has a thickness of 10 to 350 μm, one surface has a 10-point average roughness Rz value of less than 2 μm and a friction angle of larger than 31° but 40° or smaller, the other surface has a 10-point average roughness Rz value of 2 μm to 7 μm and a friction angle of 20° to 31°, a viscosity of a toluene/ethanol (1:1, mass ratio) solution containing 10%-by-mass of a polyvinyl acetal resin contained in the polyvinyl acetal resin material, which is measured at 20° C. and 30 rpm using a Brookfield-type (B-type) viscometer, is 100 to 1,000 mPa.Math.s, and the amount of a plasticizer in the polyvinyl acetal resin film is 0 to 20% by mass based on a total mass of the polyvinyl acetal resin film.

The present disclosure relates to an interlayer film for laminated glass comprising: (a) polyvinyl butyral (PVB) resin having an average molecular weight (Mw) as measured by Gel Permeation Chromatography (GPC) from about 175,000 to about 210,000 Dalton; and (b) about 30 to about 50 parts per hundred (pph) of a plasticizer. The interlayer film interposed between two glass sheets forms laminated glass having a pummel adhesion value that is greater in an outer area of the laminated glass than in a middle area of the laminated glass after the laminated glass has been maintained at 50° C. and 95% relative humidity (RH) for 28 days. The laminated glass exhibits improved durability and does not delaminate over time, even in the presence of high temperature and humidity conditions.

An interlayer filling material for a touch panel which is used for filling an interlayer space between a touch panel and another component or an interlayer space between transparent conductive films included in the touch panel in production of a personal digital assistant, which is excellent in followability to steps of a decorative printing portion or wiring upon filling of an interlayer space (lamination) and also excellent in defoaming properties to release air bubbles entrapped during filling of an interlayer space (lamination) or air bubbles left near the steps, which is less likely to be whitened and less likely to deteriorate an ITO film even under a high-temperature and high-humidity environment. The present invention also aims to provide a laminate produced using the interlayer filling material for a touch panel. The interlayer filling material includes: a polyvinyl acetal; a plasticizer; and an organic acid.

The problem to be solved of the present invention is to provide a modified vinyl acetal resin for an interlayer film of laminated glass having excellent transparency, impact resistance, heat resistance and molding ability. The means for solving the problem is a modified vinyl acetal resin for an interlayer film of laminated glass comprising 25 to 60 mol % of ethylene units and 24 to 71% by mol of vinyl alcohol units, based on all the monomer units constituting the resin, and having the acetalization degree of 5 mol % or more and less than 40 mol %.

Embodiment relates to film for bonding, and a light-transmitting laminate including the same and the like, a film for bonding comprising an embossed surface, wherein the embossed surface has an A2/A1 value of 1 or less are disclosed. A film for bonding have improved in deairing stability during formation of a light transmitting laminate, an edge sealing characteristic, and the like by controlling characteristics of a embossed surface.

The present invention relates to a modified polyvinyl butyral material, comprising a polyvinyl butyral composite material, a filler, an anti-hydrolysis agent, a first plasticizer, zinc stearate, calcium stearate, and a polymeric dispersant; wherein the polyvinyl butyral composite material is obtained by plasticizing a composition comprising polyvinyl butyral and a second plasticizer. The present invention also relates to a preparation method of the modified polyvinyl butyral material, a modified polyvinyl butyral product comprising at least one modified polyvinyl butyral layer prepared from a material comprising the modified polyvinyl butyral material, and the preparation method of the modified polyvinyl butyral product.

Provided is an interlayer film for laminated glass which is excellent in sound insulation property and has improved sound insulation performance not only in a coincidence region but also in a mass-dominated region. The interlayer film for laminated glass includes a sound insulating layer which is formed from a composition (A) containing at least one resin (a1) selected from a thermoplastic resin and a thermosetting resin, wherein a tan δ obtained when a dynamic viscoelasticity of a sheet, which is obtained by molding the composition (A) to have a thickness of 0.8 mm, is measured at a frequency of 0.3 Hz in a tension mode has a maximal value at a temperature T.sub.A (° C.), T.sub.A (° C.) is in a range of −50 to 50° C., and the tan δ at T.sub.A (° C.) is 2.5 or more.

The present disclosure relates to a film for bonding including an embossed surface, wherein the embossed surface has a Sku value of 5 or less, wherein the embossed surface has Sk, Spk, and Svk values, and when a total sum of the Sk value, the Spk value, and the Svk value is 100%, a sum of the Sk value and the Spk value is 50% or more, wherein the embossed surface has a Sz value of 30 to 90 μm, and wherein the film includes a polyvinyl acetal resin and a plasticizer.

A foam composition comprises a recycled polyvinyl butyral in an amount from 5 wt % to 70 wt %; an ethylene-ester copolymer in an amount from 10 wt % to 70 wt %; a foaming agent in an amount from 0.5 wt % to 3.5 wt %; a peroxide crosslinking agent in an amount from 0.5 wt % to 3.0 wt %; and a hydrazide crosslinking agent in an amount from 0.1 wt % to 2.5 wt %, based on a total weight of the foam composition. A foam produced from the foam composition can avoid emitting an unpleasant odor of aldehydes, and the foam also has good mechanical properties and good resilience.

A gear is provided that has excellent continuous moldability for practical use, and both high slidability and high durability. The provided gear is a molded resin constructed of a resin composition comprising a thermoplastic resin (A) and cellulose nanofibers (B) with an average fiber diameter of 1000 nm or smaller, and having a number average molecular weight of the thermoplastic resin (A) in the range of 10,000 to 150,000, wherein a sliding surface of the gear with another gear teeth has an arithmetic mean surface roughness Sa of 3.0 μm or lower.