A fluororubber composition comprising 5 to 30 parts by weight of carbon black having an iodine adsorption of 70 mg/g or more, 5 to 20 parts by weight of carbon fiber having an average fiber diameter of 5 to 20 μm and an aspect ratio of 2 to 10, and 3 to 20 parts by weight of PTFE, based on 100 parts by weight of fluororubber. The crosslinked molded article obtained from the fluororubber composition exhibits excellent effects of imparting oil film retention by using carbon fiber with specific properties, and improving abrasion resistance in unlubricated conditions by using the carbon fiber in combination with PTFE as a solid lubricant.

A fluororubber composition comprising 5 to 30 parts by weight of carbon black having an iodine adsorption of 70 mg/g or more, 5 to 20 parts by weight of carbon fiber having an average fiber diameter of 5 to 20 μm and an aspect ratio of 2 to 10, and 3 to 20 parts by weight of PTFE, based on 100 parts by weight of fluororubber. The crosslinked molded article obtained from the fluororubber composition exhibits excellent effects of imparting oil film retention by using carbon fiber with specific properties, and improving abrasion resistance in unlubricated conditions by using the carbon fiber in combination with PTFE as a solid lubricant.

A conduit, particularly flexible conduit comprises an inner tubular housing, at least one reinforcing layer at least partially disposed around the inner housing, an outer protective sheath at least partially disposed around the at least one reinforcing layer, and optionally a thermally insulating layer disposed between the at least one reinforcing layer and the outer protective sheath. At least one of the outer protective sheath and the thermally insulating layer comprises a thermoplastic vulcanizate composition.

A conduit, particularly flexible conduit comprises an inner tubular housing, at least one reinforcing layer at least partially disposed around the inner housing, an outer protective sheath at least partially disposed around the at least one reinforcing layer, and optionally a thermally insulating layer disposed between the at least one reinforcing layer and the outer protective sheath. At least one of the outer protective sheath and the thermally insulating layer comprises a thermoplastic vulcanizate composition.

The present disclosure provides a fluoroelastomer crosslinkable composition, the composition containing (a) a polyol-crosslinkable fluoroelastomer and (b) a cross-linking agent, wherein the cross-linking agent (b) is at least one selected from the group consisting of a compound represented by the general formula (b1) set forth in the description, a compound represented by the general formula (b2) set forth in the description, a compound represented by the general formula (b3) set forth in the description, and a salt of any of these compounds with an alkali metal, an alkaline earth metal, or an onium compound.

The invention relates to a hose having at least one barrier layer inner layer and an outer layer, wherein the barrier layer is obtainable by extrusion of a mixture comprising a) at least one thermoplastic fluoropolymer, b) at least one fluororubber and a crosslinking agent and/or at least one fluororubber elastomer and c) at least one carbon filler selected from carbon black, in particular conductivity carbon black, graphene, carbon nanofillers, in particular carbon nanotubes, carbon nanohorns, or a combination thereof in an amount of 0.05% by weight to 20% by weight of the carbon filler(s), or irradiated PTFE, and vulcanization. The hose exhibits a high fuel, diesel and oil stability and dynamic capability.

The invention relates to a hose having at least one barrier layer inner layer and an outer layer, wherein the barrier layer is obtainable by extrusion of a mixture comprising a) at least one thermoplastic fluoropolymer, b) at least one fluororubber and a crosslinking agent and/or at least one fluororubber elastomer and c) at least one carbon filler selected from carbon black, in particular conductivity carbon black, graphene, carbon nanofillers, in particular carbon nanotubes, carbon nanohorns, or a combination thereof in an amount of 0.05% by weight to 20% by weight of the carbon filler(s), or irradiated PTFE, and vulcanization. The hose exhibits a high fuel, diesel and oil stability and dynamic capability.

A foam composition comprises a recycled polyvinyl butyral in an amount from 5 wt % to 70 wt %; an ethylene-ester copolymer in an amount from 10 wt % to 70 wt %; a foaming agent in an amount from 0.5 wt % to 3.5 wt %; a peroxide crosslinking agent in an amount from 0.5 wt % to 3.0 wt %; and a hydrazide crosslinking agent in an amount from 0.1 wt % to 2.5 wt %, based on a total weight of the foam composition. A foam produced from the foam composition can avoid emitting an unpleasant odor of aldehydes, and the foam also has good mechanical properties and good resilience.

A foam composition comprises a recycled polyvinyl butyral in an amount from 5 wt % to 70 wt %; an ethylene-ester copolymer in an amount from 10 wt % to 70 wt %; a foaming agent in an amount from 0.5 wt % to 3.5 wt %; a peroxide crosslinking agent in an amount from 0.5 wt % to 3.0 wt %; and a hydrazide crosslinking agent in an amount from 0.1 wt % to 2.5 wt %, based on a total weight of the foam composition. A foam produced from the foam composition can avoid emitting an unpleasant odor of aldehydes, and the foam also has good mechanical properties and good resilience.

A large V-belt includes an endless rubber belt body including an adhesive rubber layer and a cord embedded in the adhesive rubber layer of the belt body. The large V-belt has a belt thickness of 15 mm or more and the belt width of 10 mm or more at the center, in a belt thickness direction, of a cord embedded position. The belt body further includes reinforced rubber layers made of a rubber composition having a type A durometer hardness of 92 or more, the reinforced rubber layers being stacked on a belt inner side and/or a belt outer side of the adhesive rubber layer in the belt thickness direction.