Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.

Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

Disclosed herein is a high-strength plated steel sheet containing an internal oxidized layer, a soft layer including the internal oxidized layer, and a hard layer including a structure having metallic structure containing a low-temperature-transformation produced phase in a proportion of 70% or more by area of the whole of the metallic structure, in which polygonal ferrite is in a proportion of 0% or more by area, and 10% or less by area of the same, and retained austenite is in a proportion of 5% or more by volume of the same. The high-strength plated steel sheet satisfies the average depth D of the soft layer is 20 μm or more, the average depth d of the internal oxidized layer is 4 μm or more and less than D, and a tensile strength of 980 MPa or more.

A bolt of the present invention has a composition comprising: 0.50 mass % or greater and 0.65 mass % or less of carbon (C), 1.5 mass % or greater and 2.5 mass % or less of silicon (Si), 1.0 mass % or greater and 2.0 mass % or less of chromium (Cr), 0.2 mass % or greater and 1.0 mass % or less of manganese (Mn), 1.5 mass % or greater and 5.0 mass % or less of molybdenum (Mo), wherein a total amount of phosphorous (P) and sulfur (S) as impurities is 0.03 mass % or less, the remaining is iron (Fe), and the bolt comprises an iron based oxide film with a film thickness of 3 μm or greater and 20 μm or less on the surface thereof. The bolt has excellent delayed fracture resistance and reliably provides a fastening axial force.

An aspect of the present invention relates to a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4≤0.4*Cr+Si≤3.2 (wherein element symbols denote measurements of respective element contents by weight %).

A hot-rolled strip steel product is described having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.030%-0.10% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.010% S,<0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.30% Mo, 0%-0.15% Al, 0%-0.10% Nb, 0.10%-0.30% V, <0.020% Ti, 0%-0.0010% B, remainder being Fe and inevitable impurities, wherein the hot rolled strip steel product has a a microstructure comprising, in terms of volume percentages (vol. %), ferrite≥90, wherein the ferrite structure comprises bainite, at least 50% of polygonal ferrite and at most 10% quasi-polygonal ferrite, and wherein the steel strip product has an average hole expansion ratio≥50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ≥660 MPa and a tensile strength≥760 MPa.

A steel for mining chain and a manufacturing method thereof, wherein the steel has compositions by weight percentage: C: 0.20-0.28%, Si: 0.01-0.40%, Mn: 0.50-1.50%, P≤0.015%, S≤0.005%, Cr: 0.30-2.00%, Ni: 0.50-2.00%, Mo: 0.10-0.80%, Cu: 0.01-0.30%, Al: 0.01-0.05%, Nb: 0.001-0.10%, V: 0.001-0.10%, H≤0.00018%, N≤0.0150%, O≤0.0020%, and the balance is Fe and inevitable impurities. The manufacturing method comprises steps of smelting, refining and vacuum treatment, casting, heating, forging or rolling, and quenching and tempering heat treatment processes. The steel in the present invention has high strength and good impact toughness, good elongation and reduction of area. The steel can also resist stress corrosion cracking and have good weather resistance, wear resistance and fatigue resistance, which can be used in scenarios where the steel having high strength and toughness is required, such as construction machinery and marine engineering.

Method of hot press forming an article from zinc or zinc alloy coated steel, wherein the steel is a product obtained by: casting the molten steel into slabs; reheating the slabs; hot rolling the steel into a strip, preferably with an FRT above Ar3; coiling the hot rolled steel strip; pickling the hot rolled steel strip; continuous annealing the strip; hot dip coating the steel strip with the zinc or zinc alloy whilst: using a dipping time of 3 seconds or more; maintaining in the hot dip bath a bath temperature of 420° C. to 500° C.; wherein the zinc bath contains essentially zinc, at least 0.1% Al, and optionally up to 5% Al and optionally up to 4% Mg, the rest of the bath including further elements all individually less than 0.3%, and unavoidable impurities; hot press forming the article.

A hot rolled and annealed steel sheet having a composition including, by weight percent: C: 0.1-0.25%, Mn: 3.00-5.00%, Si: 0.80-1.60%, B: 0.0003-0.004%, S≤0.010%, P≤0.020%, N≤0.008% the remainder of the composition being iron and unavoidable impurities resulting from the smelting, and having a microstructure consisting of, in surface fraction: more than 20% of recrystallized ferrite, the balance being non-recrystallized ferrite, more than 15% of said recrystallized ferrite having grain size larger than 5 μm and a density of carbides at grain boundary of recrystallized ferrite less than 5 carbides per 10 μm of grain boundary length

A cold rolled and heat-treated steel sheet having a composition including, by weight percent C: 0.12-0.25% Mn: 3.0-8.0%, Si: 0.70-1.50%, Al: 0.3-1.2%, B: 0.0002-0.004%, S≤0.010%, P≤0.020%, N≤0.008%, the remainder of the composition being iron and unavoidable impurities resulting from the smelting, and having a microstructure consisting of, in surface fraction: between 5% and 45% of ferrite, between 25% and 85% of partitioned martensite, the partitioned martensite having a carbides density strictly less than 2×10.sup.6/mm.sup.2, between 10% and 30% of retained austenite, less than 8% of fresh martensite, a part of the fresh martensite being combined with retained austenite in the shape of martensite-austenite islands in total surface fraction less than 10%.