Method for the manufacture of a galvannealed steel sheet includes the following steps: A) the provision of a pre-coated steel sheet coated with a first coating comprising iron and nickel, such steel sheet having the following chemical composition in weight percent 0.10<C<0.40%, 1.5<Mn<3.0%, 0.7<Si<2.0%, 0.05<Al<1.0%, 0.75<(Si+Al)<3.0% and on a purely optional basis, one or more elements such as Nb≤0.5%, B≤0.005%, Cr≤1.0%, Mo≤0.50%, Ni≤1.0%, Ti≤0.5%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, B) the thermal treatment of such pre-coated steel sheet at a temperature between 600 to 1000° C., C) the hot-dip coating of the steel sheet obtained in step B) with a second coating based on zinc and D) an alloying treatment to form a galvannealed steel sheet.

A production method for a high-strength steel sheet having a tensile strength TS of 780 MPa or more is provided. The production method comprises: heating a steel slab having a predetermined chemical composition; hotrolling the steel slab; coiling the hot-rolled sheet; subjecting the hot-rolled sheet to pickling treatment; holding the hot-rolled sheet in a pre-determined temperature range for predetermined time; cold rolling the hot-rolled sheet to obtain a cold-rolled sheet; subjecting the cold-rolled sheet to first annealing treatment; cooling the cold-rolled sheet at a pre-determined average cooling rate; cooling the cold-rolled sheet to room temperature; reheating the clod-rolled sheet to perform second annealing treatment; cooling the cold-rolled sheet at a first average cooling rate; cooling the cold-rolled sheet at a second average cooling rate; reheating the cold-rolled sheet to a predetermined reheating temperature range; and holding the cold-rolled sheet in the reheating temperature range.

A preferable aspect of the present invention provides a high-strength high-toughness hot-rolled steel sheet and a manufacturing method therefor, wherein the hot-rolled steel sheet contains, by weight, 0.07-0.13% C, 0.20-0.50% Si, 0.5-0.9% Mn, 0.03% or less P, 0.02% or less S, 0.005-0.03% Nb, 0.3-0.6% Cr, 0.005-0.03% Ti, 0.1-0.35% Cu, 0.05-0.3% Ni, 0.01-0.15% Mo, 0.007% or less N, 0.001-0.006% Ca, 0.01-0.05% Al, and the balance Fe and other unavoidable impurities, the alloy elements satisfying the following relational formulas [Relational formula 1] 1.6≤(Mo/96)/(P/31)≤6, [Relational formula 2] 1.6≤(Ca/S)≤3, and [Relational formula 3] 3.5≤(3*C/12+Mn/55)*100≤5; wherein a microstructure comprises, by area fraction, 85% or more of polygonal ferrite and 15% or less of pearlite, the crystal grain size of the polygonal ferrite being 10 μm or less; and wherein a variation in yield strength in a width direction is 35 MPa or lower.

A preferable aspect of the present invention provides a high-strength high-toughness hot-rolled steel sheet and a manufacturing method therefor, wherein the hot-rolled steel sheet contains, by weight, 0.07-0.13% C, 0.20-0.50% Si, 0.5-0.9% Mn, 0.03% or less P, 0.02% or less S, 0.005-0.03% Nb, 0.3-0.6% Cr, 0.005-0.03% Ti, 0.1-0.35% Cu, 0.05-0.3% Ni, 0.01-0.15% Mo, 0.007% or less N, 0.001-0.006% Ca, 0.01-0.05% Al, and the balance Fe and other unavoidable impurities, the alloy elements satisfying the following relational formulas [Relational formula 1] 1.6≤(Mo/96)/(P/31)≤6, [Relational formula 2] 1.6≤(Ca/S)≤3, and [Relational formula 3] 3.5≤(3*C/12+Mn/55)*100≤5; wherein a microstructure comprises, by area fraction, 85% or more of polygonal ferrite and 15% or less of pearlite, the crystal grain size of the polygonal ferrite being 10 μm or less; and wherein a variation in yield strength in a width direction is 35 MPa or lower.

A sheet or strip made of a hardenable aluminum alloy, a vehicle part made therefrom, a use, and a method for producing the sheet or strip are disclosed. In order to insure a powerful paint bake response (PBR), it is proposed for the aluminum alloy to have from 4.0 to 5.5 wt % magnesium (Mg) and from 2.5 to 5.5 wt % zinc (Zn) and for it to be in the T4-FH state, wherein the wt % of magnesium (Mg) is greater than the wt % of zinc (Zn).

A steel sheet has a composition comprising 0.060%≤C≤0.085%, 1.8%≤Mn≤2.0%, 0.4%≤Cr≤0.6%, 0.1%≤Si≤0.5%, 0.010%≤Nb≤0.025%, 3.42N≤Ti≤0.035%, 0≤Mo≤0.030%, 0.020%≤Al≤0.060%, 0.0012%≤B≤0.0030%, S≤0.005%, P≤0.050%, 0.002%≤N≤0.007% and optionally 0.0005%≤Ca≤0.005%, the remainder of the composition being iron and unavoidable impurities. The microstructure consists of 34% to 80% bainite, 10% to 16% martensite, and 10% to 50% of ferrite. The surface fraction of unrecrystallized ferrite, with respect to the whole structure, is of less than 30%. The martensite consists of self-tempered martensite and fresh martensite, the surface fraction of self-tempered martensite being comprised between 4% and 10%.

An embodiment of the present invention provides a steel wire rod and a method for producing same, the steel wire rod comprising 0.3-0.5 wt % of C, 0.02-0.4 wt % of Si, 1.0-1.5 wt % of Mn, 0.3-0.7 wt % of Cr, 0.003 wt % or less of B, 0.03 wt % or less of Ti, 0.03 wt % or less of P, 0.01 wt % or less of S, 0.02-0.05 wt % of Al, and 0.001-0.01 wt % of N, with the balance being Fe and inevitable impurities, and having a microstructure in which the main phase thereof is a complex structure of ferrite+pearlite, and contains at most 5 area % (including 0 area %) of at least one of bainite or martensite, wherein the average pearlite colony size in a region extending from the ⅖ point to the ⅗ point of the diameter is at most 7 μm.

A hot-stamping formed body has a predetermined chemical composition and includes microstructure which includes residual austenite of which an area ratio is in a range of 20% to 30%. Among grain boundaries of crystal grains of bainite and tempered martensite in the microstructure, a ratio of a length of a grain boundary having a rotation angle in a range of 55° to 75° to a total length of a grain boundary having a rotation angle in a range of 4° to 12°, a grain boundary having a rotation angle in a range of 49° to 54°, and a grain boundary having a rotation angle in a range of 55° to 75° to the <011> direction as a rotation axis is 30% or more.

This steel sheet for a can is a steel sheet for a can containing, by mass %, C: 0.010% to 0.050%, Si: 0.020% or less, Mn: 0.10% to 0.60%, P: 0.020% or less, S: 0.020% or less, Al: 0.050% or less, N: 0.0100% or less, Nb: 0% to 0.03%, Ti: 0% to 0.03%, B: 0% to 0.0020%, and a remainder including Fe and an impurity, in which, when the number of carbides having an equivalent circle diameter of 2 μm or more and 5 μm or less is indicated by a, and the number of carbides having an equivalent circle diameter of 0.1 μm or more and less than 2 μm is indicated by b, a/b satisfies a range of the following formula (1), a fracture strain is 1.6 or more, and a sheet thickness is 0.10 to 0.30 mm.

a/b<0.12  (1)

A high-strength steel sheet with excellent delayed fracture resistance, having a tensile strength of 1700 MPa or larger, including a predetermined component composition, having a martensite structure whose ratio accounts for 95 area % or more of the entire metallographic structure, and having a transition metal carbide whose ratio accounts for 0.8 volume % or more of the entire metallographic structure.