Provided is a steel sheet having excellent image clarity after painting, including: carbon (C): 0.001% to 0.03%, silicon (Si): 0.001% to 0.35%, manganese (Mn): 0.05% to 2.2%, phosphorus (P): 0.003% to 0.1%, sulfur (S): 0.001% or 0.025%, aluminum (Al): 0.01% to 0.1%, nitrogen (N): 0.001% to 0.007%, and a remainder of iron (Fe) and inevitable impurities. The microstructure of the steel sheet mainly is ferrite phases. An R-cube texture of a surface layer of the steel sheet is 5% or less by area %.

The present disclosure provides a manufacturing method and a grain-oriented electrical steel sheet manufactured thereby, the manufacturing method comprising the steps of: heating a slab; hot rolling the heated slab so as to manufacture a hot-rolled sheet; cold rolling the hot-rolled sheet so as to manufacture a cold-rolled sheet; decarburizing and annealing the cold-rolled steel sheet; forming a ceramic coating layer on a portion or the whole of one surface or two sides of the decarburized and annealed cold-rolled sheet by using a chemical vapor deposition (CVD) process; and finally annealing the cold-rolled sheet on which the ceramic coating layer is formed.

A grain-oriented electrical steel sheet according to an embodiment of the present invention may comprise: by weight %, 2.0-4.0% of Si, 0.04-0.2% of Mn, 0.010% or less (exclusive of 0%) of N, 0.01-0.05% of Sb, 0.005% or less (exclusive of 0%) of C, 0.03-0.08% of Sn, 0.01-0.2% of Cr, and the balance of Fe and inevitable impurities; and precipitates which have an average particle size of 5-50 nm and contain at least one of AIN, (Al, Si)N, (Al, Si, Mn)N, Mns, and CuS.

A non-oriented electrical steel sheet according to an embodiment of the present invention includes, in wt %, Si: 2.1 to 3.8%, Mn: 0.001 to 0.6%, Al: 0.001 to 0.6%, Bi: 0.0005 to 0.003%, and Ge: 0.0003 to 0.001%, and the balance of Fe and inevitable impurities.

In a double-oriented electrical steel sheet according to an embodiment of the present invention, the fraction of crystal grains having an orientation within 15° from {100}<001> is 50 to 75%, and the fraction of crystal grains having an orientation within 15° from {100}<380> is 50 to 75%.

This hot-stamping formed body has a predetermined chemical composition and has a metallographic structure consisting of, by area ratio, a total of 10% to 30% of ferrite and granular bainite and a remainder in microstructure consisting of one or more of martensite, bainite, and tempered martensite, and, in textures of a surface layer region and an inside region, ratios between a pole density of an orientation group consisting of {001}<1-10> to {001}<−1-10> and a pole density of an orientation group consisting of {111}<1-10> to {111}<−1-12> are controlled.

The purpose of the present invention is to provide a method for manufacturing a grain-oriented electrical steel sheet, whereby it becomes possible to manufacture a grain-oriented electrical steel sheet having further improved iron loss properties stably. (Solution) According to one aspect of the present invention, a method for manufacturing a grain-oriented electrical steel sheet is provided, the method being characterized by comprising a re-heating step, a hot rolling step, a hot-rolled sheet annealing step, a cold rolling step, a decarburization annealing step and a final annealing step, wherein the decarburization annealing step includes a heating step of heating a cold-rolled sheet from an inlet side temperature T0° C. to a soaking temperature T2° C. and a soaking step of keeping the temperature of the cold-rolled sheet at the soaking temperature T2° C., and the heating rate HR1 from the time point when the temperature of the cold-rolled sheet is an inlet side temperature T0° C. to the time point when the temperature of the cold-rolled sheet reaches a attained temperature T1° C. is 40° C./sec or more and the heating rate HR2 from the time point when the temperature of the cold-rolled sheet is the desired temperature T1° C. to the time point when the temperature of the cold-rolled sheet reaches the soaking temperature T2° C. is more than 15° C./sec to 30° C./sec in the heating in the decarburization annealing step.

A ferritic stainless steel sheet is provided that has a predetermined chemical composition, wherein: a grain size number is 6.0 or more; the ferritic stainless steel sheet satisfies the formulas [A+B≥9.0] and [X+Y≥9.0] with respect to crystal orientation intensities of a ferrite phase obtained by X-ray diffraction; and the sheet thickness is 1.0 mm or more. A represents a {111}<112> crystal orientation intensity at a center portion of sheet thickness, B represents a {111}<112> crystal orientation intensity at a ⅛ portion of the sheet thickness, X represents a {322}<236> crystal orientation intensity at a center portion of sheet thickness, and Y represents a {322}<236> crystal orientation intensity at a ⅛ portion of the sheet thickness.

A grain-oriented electrical steel sheet of an embodiment of the present invention comprises Si: 1.0% to 7.0% and Y: 0.005% to 0.5% by wt %, and the remainder comprising Fe and other inevitable impurities, and 10 pieces or less of inclusions comprising Y and having a diameter of 30 nm to 5 μm per area of 1 mm.sup.2.

Disclosed is a manufacturing method for a high silicon grain oriented electrical steel sheet, the silicon content of the high silicon grain oriented electrical steel is greater than 4 wt %, comprising the steps of: (1) performing decarburization annealing of a cold-rolled steel plate; (2) allowing high silicon alloy particles in a completely solid state to collide at a high speed with the surface of the decarburization annealed steel plate to be sprayed, thus forming a high silicon alloy coating on the surface of the steel plate to be sprayed; (3) coating a release agent and drying; and (4) annealing. The manufacturing method for the high silicon grain oriented electrical steel sheet of the present invention is inexpensive, and, the high silicon grain oriented electrical steel sheet produced is of stable quality and is provided with great magnetic performance.