BMG parts having an uniform and consistently thick metal oxide layer. The metal oxide layer, also known as an interference layer, exhibits a consistent color and durability over the entire surface of the part. Methods and devices involved in forming the BMG parts with uniformly thick interference layers are also provided.

One embodiment of the present invention provides an Fe-based amorphous alloy ribbon for an Fe-based nanocrystalline alloy, the Fe-based amorphous alloy ribbon being a cooled body of a molten metal that has been applied to a surface of a chill roll, wherein the Fe-based amorphous alloy ribbon includes a recess having a depth of 1 m or more in a 0.647 mm0.647 mm region located in a central part, in the ribbon width direction, of a ribbon surface, which is a cooled surface, in which a maximum area of the recess having a depth of 1 m or more is 3000 m.sup.2 or less; and a method of manufacturing the same.

An embodiment relates to a cladded composite comprising a cladding layer of a bulk metallic glass and a substrate; wherein the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

PdCuP metallic glass-forming alloy compositions and metallic glasses comprising at least one of Ag, Au, and Fe are provided, wherein the alloys demonstrate improved glass forming ability, as compared to PdCuP alloys free of Ag, Au, and Fe, and are capable of forming metallic glass rods with diameters in excess of 3 mm, and in some embodiments 26 mm or larger.

A process for producing an amorphous ductile brazing foil is provided. According to one example embodiment, the method includes providing a molten mass, and rapidly solidifying the molten mass on a moving cooling surface with a cooling speed of more than approximately 10.sup.5 C./sec to produce an amorphous ductile brazing foil. A process for joining two or more parts is also provided. The process includes inserting a brazing foil between two or more parts to be joined, wherein the parts to be joined have a higher melting temperature than that the brazing foil to form a solder joint and the brazing foil comprises an amorphous, ductile Ni-based brazing foil; heating the solder joint to a temperature above the liquidus temperature of the brazing foil to form a heated solder joint; and cooling the heated solder joint, thereby forming a brazed joint between the parts to be joined.

The present invention provides amorphous bi-functional catalytic aluminum metallic glass particles having an aluminum metallic glass core and 2 or more transition metals disposed on the surface of the aluminum metallic glass core to form amorphous bi-functional aluminum metallic glass particles with catalytic activity.

A method for manufacturing an alloy ribbon piece capable of manufacturing a nanocrystalline alloy ribbon piece is provided. The method for manufacturing an alloy ribbon piece according to the present disclosure is a method for manufacturing an alloy ribbon piece obtained by crystallizing an amorphous alloy ribbon piece, and includes: preparing the amorphous alloy ribbon piece; sequentially heating the amorphous alloy ribbon piece from one end to an intermediate position toward another end to a temperature range equal to or more than a crystallization starting temperature, and stopping the heating when heating the amorphous alloy ribbon piece up to the intermediate position to the temperature range; and heating a region on the other end side with respect to the intermediate position of the amorphous alloy ribbon piece to the temperature range equal after the stopping of the heating in the sequentially heating.

A continuous precision forming device and process for an amorphous alloy is provided. By means of the device, when a melting platform with an alloy melt is rotated from the melting position to a position just below the forming mould (9), temperature of the alloy melt can be in the range of the overcooled liquid zone temperature of the alloy melt, and then a loading rod (7) drives the forming mould (9) to proceed with pressing forming. According to the process, press-forming is carried out in a certain temperature interval in the amorphous alloy melt solidification process, and the heating, cooling, solidification and forming in the forming process are coordinated, such that continuous forming of the amorphous alloy is achieved.

A method is provided for producing a 0.8-4.5 mm thick steel strip with an amorphous, partially amorphous or fine-crystalline microstructure with grain sizes in the range of 10-10000 nm and also a flat steel product made therefrom. A molten steel is cast into a cast strip in a casting device and cooled down at an accelerated rate. Along with Fe and impurities that are unavoidable for production-related reasons, the molten material contains at least two elements belonging to the group Si, B, C and P. In this case, the following applies for the contents of these elements (in % by weight) Si: 1.2-7.0%, B: 0.4-4.0%, C: 0.5-4.0%, P: 1.5-8.0%. With a corresponding composition and a microstructure with corresponding characteristics, a flat steel product according to the invention has a HV0.5 hardness of 760-900.