A magnesium alloy containing: Al: 0.2-1.6 wt. % Zn: 0.2-0.8 wt. % 5 Mn: 0.1-0.5 wt. % Zr 0-0.5 wt. % La: 1-3.5 wt. % Y: 0.05-3.5 wt. % Ce: 0-2 wt. % 10 Nd: 0-2 wt. % Gd: 0-3 wt. % Pr: 0-0.5 wt. % Be: 0-20 ppm the balance being Mg and incidental elements.

Provided are: a flame-retardant magnesium alloy which is prevented from the occurrence of the molten metal combustion during the melting of the alloy in casting; and a method for producing the flame-retardant magnesium alloy. A magnesium alloy containing a specific element in a specified amount and also containing a specific rare earth element (RE) in a specified amount. The magnesium alloy makes it possible to form an oxide film of the rare earth element (RE) which is dense and thin and is rarely cracked on the outermost surface of a molten metal. More specifically a flame-retardant magnesium alloy which contains, in % by mass, less than 9.0% of Ca, 0.5% or more and less than 5.7% of Al, 1.3% or less of Si, 0.4% or more and less than 1.3% of a rare earth element and a remainder made up by Mg and unavoidable impurities, wherein the requirement represented by the formula: Al+8Ca≥20.5% is satisfied.

Provided are: a flame-retardant magnesium alloy which is prevented from the occurrence of the molten metal combustion during the melting of the alloy in casting; and a method for producing the flame-retardant magnesium alloy. A magnesium alloy containing a specific element in a specified amount and also containing a specific rare earth element (RE) in a specified amount. The magnesium alloy makes it possible to form an oxide film of the rare earth element (RE) which is dense and thin and is rarely cracked on the outermost surface of a molten metal. More specifically a flame-retardant magnesium alloy which contains, in % by mass, less than 9.0% of Ca, 0.5% or more and less than 5.7% of Al, 1.3% or less of Si, 0.4% or more and less than 1.3% of a rare earth element and a remainder made up by Mg and unavoidable impurities, wherein the requirement represented by the formula: Al+8Ca≥20.5% is satisfied.

Examples of an alloy injection molded liquid metal substrate are described. In an example, an alloy injection molded liquid metal substrate includes a liquid metal substrate and an alloy injection molded on a first surface of the liquid metal substrate.

A high-strength and high-toughness magnesium alloy includes a Mg—Al—Bi—Sb—Zn—Sr—Y—Mn alloy, prepared from the following components in percentage by mass: 7.0 to 10.0% of Al, 0.2 to 2.0% of Bi, 0.2 to 0.8% of Sb, 0.2 to 0.5% of Zn, 0.1 to 0.5% of Sr, 0.03 to 0.3% of Y, 0.05 to 0.1% of Mn and a balance of Mg.

A high-strength and high-toughness magnesium alloy includes a Mg—Al—Bi—Sb—Zn—Sr—Y—Mn alloy, prepared from the following components in percentage by mass: 7.0 to 10.0% of Al, 0.2 to 2.0% of Bi, 0.2 to 0.8% of Sb, 0.2 to 0.5% of Zn, 0.1 to 0.5% of Sr, 0.03 to 0.3% of Y, 0.05 to 0.1% of Mn and a balance of Mg.

A plastic wrought magnesium alloy includes a Mg—Al—Bi—Sn—Ca—Y alloy, prepared from the following chemical components in percentage by mass: 3 to 6.0% of Al, 1 to 3.0% of Bi, 0.5 to 2.0% of Sn, 0.02 to 0.05% of Ca, 0.02 to 0.05% of Y and the balance of Mg, in which the percentage sum of Ca and Y elements is more than 0.05% and less than 0.1%.

A plastic wrought magnesium alloy includes a Mg—Al—Bi—Sn—Ca—Y alloy, prepared from the following chemical components in percentage by mass: 3 to 6.0% of Al, 1 to 3.0% of Bi, 0.5 to 2.0% of Sn, 0.02 to 0.05% of Ca, 0.02 to 0.05% of Y and the balance of Mg, in which the percentage sum of Ca and Y elements is more than 0.05% and less than 0.1%.

A Mg—Li—Al—Zn alloy is disclosed. The Mg—Li—Al—Zn alloy comprises, in weight percent: 5-15% Li, 1.5-9.0% Al, 0.5-1.5% Zn, 0.4-1.3% Y, 0.18-1.01% Nd, 0.09-0.65% Ce, and the balance Mg and incidental impurities. Experimental data have proved that, this novel Mg—Li—Al—Zn alloy has a flashover temperature in a range between 620° C. and 700° C., such that the flashover temperature of the specifically-designed Mg—Li—Al—Zn alloy is greater than that of commercial LAZ521, LAZ721, LAZ771, LAZ921, and LAZ1491 alloys. Therefore, the Mg—Li—Al—Zn alloy of the present invention can be processed to be a structural article through air melt and casting process.

The present invention provides a novel heat exchange medium to replace lead. A carbon-steel wire 1A heated in a heating furnace 11 is passed through a bath 12A filled with a liquid-phase Mg—Al—Ca alloy 20 obtained by melting a Mg—Al—Ca alloy in which the main constituent elements are Mg (magnesium), Al (aluminum) and Ca (calcium). When it passes through the bath 12A, the carbon-steel wire 1A, which has been heated for example to about 950° C. in the heating furnace 11, is cooled to about 550° C. The Mg—Al—Ca alloy is non-toxic and has no environmental impact as well.