A panel that is excellent in both appearance and dent resistance after being formed from a starting material is provided. The panel has a steel sheet including martensite, and a surface roughness parameter (Sa) at a flat part of a center-side portion of the panel is Sa≤0.500 μm. In laths of the martensite, the panel has precipitates having a major axis of 0.05 μm to 1.00 μm and an aspect ratio of 3 or more in an amount of 15 precipitates/μm.sup.2 or more. A ratio YS.sub.1/YS.sub.2 between a yield stress YS.sub.1 measured in a tensile test specimen cut out from the flat part of the center-side portion of the panel and a yield stress YS.sub.2 measured in a tensile test specimen cut out from an end part of the panel is 0.90 to 1.10.

This hot-rolled steel sheet has a predetermined chemical composition, in which a metallographic structure contains, by area %, more than 92.0% and 100.0% or less of martensite and tempered martensite in total, less than 3.0% of residual austenite, and less than 5.0% of ferrite, has a ratio S.sub.60/S.sub.7, which is a ratio of a density S.sub.60 of a length of a grain boundary having a crystal misorientation of 60° to a density S.sub.7 of a length of a grain boundary having a crystal misorientation of 7° about a <110> direction, of more than 0.34 and less than 0.60, has a standard deviation of a Mn concentration of 0.60 mass % or less, and has a tensile strength of 980 MPa or more.

This hot-rolled steel sheet has a predetermined chemical composition, in which a metallographic structure contains, by area %, more than 92.0% and 100.0% or less of martensite and tempered martensite in total, less than 3.0% of residual austenite, and less than 5.0% of ferrite, has a ratio S.sub.60/S.sub.7, which is a ratio of a density S.sub.60 of a length of a grain boundary having a crystal misorientation of 60° to a density S.sub.7 of a length of a grain boundary having a crystal misorientation of 7° about a <110> direction, of more than 0.34 and less than 0.60, has a standard deviation of a Mn concentration of 0.60 mass % or less, and has a tensile strength of 980 MPa or more.

What is provided is a steel sheet for a non-oriented electrical steel sheet containing, in mass %, C: 0.0040% or less, Si: 1.9% or more and 3.5% or less, Al: 0.10% or more and 3.0% or less, Mn: 0.10% or more and 2.0% or less, P: 0.09% or less, S: 0.005% or less, N: 0.0040% or less, B: 0.0060% or less, and the remainder consisting of Fe and impurities, in which the recrystallization rate of the structure of a sheet thickness-direction cross section at each position 10 mm apart toward the sheet width center from each of both end portions in the sheet width direction is less than 50%, and, when the sheet width is represented by W, the recrystallization rate of the structure of a sheet thickness-direction cross section at the position of ¼W from each of both end portions in the sheet width direction is 50% or more.

What is provided is a steel sheet for a non-oriented electrical steel sheet containing, in mass %, C: 0.0040% or less, Si: 1.9% or more and 3.5% or less, Al: 0.10% or more and 3.0% or less, Mn: 0.10% or more and 2.0% or less, P: 0.09% or less, S: 0.005% or less, N: 0.0040% or less, B: 0.0060% or less, and the remainder consisting of Fe and impurities, in which the recrystallization rate of the structure of a sheet thickness-direction cross section at each position 10 mm apart toward the sheet width center from each of both end portions in the sheet width direction is less than 50%, and, when the sheet width is represented by W, the recrystallization rate of the structure of a sheet thickness-direction cross section at the position of ¼W from each of both end portions in the sheet width direction is 50% or more.

A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

Provided herein is a stainless steel seamless pipe having a composition that contains, in mass %, C: 0.06% or less, Si: 1.0% or less, Mn: 0.01% or more and 1.0% or less, P: 0.05% or less, S: 0.005% or less, Cr: 15.2% or more and 18.5% or less, Mo: 1.5% or more and 4.3% or less, Cu: 1.1% or more and 3.5% or less, Ni: 3.0% or more and 6.5% or less, Al: 0.10% or less, N: 0.10% or less, O: 0.010% or less, and Sb: 0.001% or more and 1.000% or less, and in which C, Si, Mn, Cr, Ni, Mo, Cu, and N satisfy the predetermined formula, and the balance is Fe and incidental impurities, the stainless steel seamless pipe having a microstructure containing 30% or more martensitic phase, 65% or less ferrite phase, and 40% or less retained austenite phase by volume.

Provided herein is a stainless steel seamless pipe having a composition that contains, in mass %, C: 0.06% or less, Si: 1.0% or less, Mn: 0.01% or more and 1.0% or less, P: 0.05% or less, S: 0.005% or less, Cr: 15.2% or more and 18.5% or less, Mo: 1.5% or more and 4.3% or less, Cu: 1.1% or more and 3.5% or less, Ni: 3.0% or more and 6.5% or less, Al: 0.10% or less, N: 0.10% or less, O: 0.010% or less, and Sb: 0.001% or more and 1.000% or less, and in which C, Si, Mn, Cr, Ni, Mo, Cu, and N satisfy the predetermined formula, and the balance is Fe and incidental impurities, the stainless steel seamless pipe having a microstructure containing 30% or more martensitic phase, 65% or less ferrite phase, and 40% or less retained austenite phase by volume.

Disclosed are an outer ring for an oil pump having an increased number and size of open pores in a surface of a molded article and a method for manufacturing the outer ring.