A doping method using an electric field includes stacking a sacrificial layer on a doped layer, disposing a doping material on the sacrificial layer, disposing electrodes on the doping material and the doped layer, respectively, and doping the doping material into the doped layer through oxidation, diffusion, and reduction of the doping material by the electric field.

A method for improving the surface of an aluminum alloy article includes manufacturing the aluminum alloy article using an additive manufacturing technique, wherein the article as-manufactured includes one or more of cracks, roughness, or porosity at a surface of the article; coating the surface of the aluminum alloy article with a diffusion element, the diffusion element being capable of diffusing at least 0.2 mils into the article; heating the aluminum alloy article coated with the diffusion element to cause the diffusion element to diffuse the at least 0.2 mils into the article, thereby forming a diffusion layer of at least 0.2 mils in thickness comprising both aluminum alloy and diffusion element; and removing the diffusion layer from the aluminum alloy article, whereby upon the removing, a resulting improved surface of the article comprises fewer or smaller cracks, reduced roughness, or reduced porosity.

A method for improving the surface of an aluminum alloy article includes manufacturing the aluminum alloy article using an additive manufacturing technique, wherein the article as-manufactured includes one or more of cracks, roughness, or porosity at a surface of the article; coating the surface of the aluminum alloy article with a diffusion element, the diffusion element being capable of diffusing at least 0.2 mils into the article; heating the aluminum alloy article coated with the diffusion element to cause the diffusion element to diffuse the at least 0.2 mils into the article, thereby forming a diffusion layer of at least 0.2 mils in thickness comprising both aluminum alloy and diffusion element; and removing the diffusion layer from the aluminum alloy article, whereby upon the removing, a resulting improved surface of the article comprises fewer or smaller cracks, reduced roughness, or reduced porosity.

A method for improving the surface of an aluminum alloy article includes manufacturing the aluminum alloy article using an additive manufacturing technique, wherein the article as-manufactured includes one or more of cracks, roughness, or porosity at a surface of the article; coating the surface of the aluminum alloy article with a diffusion element, the diffusion element being capable of diffusing at least 0.2 mils into the article; heating the aluminum alloy article coated with the diffusion element to cause the diffusion element to diffuse the at least 0.2 mils into the article, thereby forming a diffusion layer of at least 0.2 mils in thickness comprising both aluminum alloy and diffusion element; and removing the diffusion layer from the aluminum alloy article, whereby upon the removing, a resulting improved surface of the article comprises fewer or smaller cracks, reduced roughness, or reduced porosity.

A method for improving the surface of an aluminum alloy article includes manufacturing the aluminum alloy article using an additive manufacturing technique, wherein the article as-manufactured includes one or more of cracks, roughness, or porosity at a surface of the article; coating the surface of the aluminum alloy article with a diffusion element, the diffusion element being capable of diffusing at least 0.2 mils into the article; heating the aluminum alloy article coated with the diffusion element to cause the diffusion element to diffuse the at least 0.2 mils into the article, thereby forming a diffusion layer of at least 0.2 mils in thickness comprising both aluminum alloy and diffusion element; and removing the diffusion layer from the aluminum alloy article, whereby upon the removing, a resulting improved surface of the article comprises fewer or smaller cracks, reduced roughness, or reduced porosity.

A surface-treated steel sheet for a battery container, including a steel sheet, an iron-nickel diffusion layer formed on the steel sheet, and a nickel layer formed on the iron-nickel diffusion layer and constituting the outermost layer, wherein when the Fe intensity and the Ni intensity are continuously measured from the surface of the surface-treated steel sheet for a battery container along the depth direction with a high frequency glow discharge optical emission spectrometric analyzer, the thickness of the iron-nickel diffusion layer being the difference between the depth at which the Fe intensity exhibits a first predetermined value and the depth at which the Ni intensity exhibits a second predetermined value is 0.04 to 0.31 m; and the total amount of the nickel contained in the iron-nickel diffusion layer and the nickel contained in the nickel layer is 10.8 to 26.7 g/m.sup.2.

A surface-treated steel sheet for a battery container, including a steel sheet, an iron-nickel diffusion layer formed on the steel sheet, and a nickel layer formed on the iron-nickel diffusion layer and constituting the outermost layer, wherein when the Fe intensity and the Ni intensity are continuously measured from the surface of the surface-treated steel sheet for a battery container along the depth direction with a high frequency glow discharge optical emission spectrometric analyzer, the thickness of the iron-nickel diffusion layer being the difference between the depth at which the Fe intensity exhibits a first predetermined value and the depth at which the Ni intensity exhibits a second predetermined value is 0.04 to 0.31 m; and the total amount of the nickel contained in the iron-nickel diffusion layer and the nickel contained in the nickel layer is 10.8 to 26.7 g/m.sup.2.

Various embodiments herein relate to electrochromic devices, methods of fabricating electrochromic devices, and apparatus for fabricating electrochromic devices. In a number of cases, the electrochromic device may be fabricated to include a particular counter electrode material. The counter electrode material may include a base anodically coloring material. The counter electrode material may further include one or more halogens. The counter electrode material may also include one or more additives.

Various embodiments herein relate to electrochromic devices, methods of fabricating electrochromic devices, and apparatus for fabricating electrochromic devices. In a number of cases, the electrochromic device may be fabricated to include a particular counter electrode material. The counter electrode material may include a base anodically coloring material. The counter electrode material may further include one or more halogens. The counter electrode material may also include one or more additives.

This method for producing a transparent optical film includes a film formation step of forming a silver layer and a high standard electrode potential metal layer so as to be laminated on a substrate, the film formation step including a silver deposition step of forming the silver layer, at a thickness of 6 nm or less by vacuum deposition, and a high standard electrode potential metal deposition step of forming the high standard electrode potential metal layer formed of a high standard electrode potential metal having a higher standard electrode potential than that of silver by vacuum deposition, and an alloying step of forming a silver alloy layer by diffusing the high standard electrode potential metal within the silver layer by performing a heating treatment at a temperature of 50 C. or higher and 400 C. or lower.