There is provided a method of patterning platinum on a substrate. A platinum layer is deposited on the substrate, and a patterned photoresist layer is formed over the platinum layer leaving partly exposed regions of the platinum layer. An aluminum layer is deposited over the partly exposed regions of the platinum layer. An alloy is formed of aluminum with platinum from the partly exposed regions. The platinum aluminum alloy is etched away leaving a remaining portion of the platinum layer to form a patterned platinum layer on the substrate. In an embodiment, a thin hard mask layer is deposited on the platinum layer on the semiconductor substrate before the patterned photoresist layer is formed.

There is provided a method of patterning platinum on a substrate. A platinum layer is deposited on the substrate, and a patterned photoresist layer is formed over the platinum layer leaving partly exposed regions of the platinum layer. An aluminum layer is deposited over the partly exposed regions of the platinum layer. An alloy is formed of aluminum with platinum from the partly exposed regions. The platinum aluminum alloy is etched away leaving a remaining portion of the platinum layer to form a patterned platinum layer on the substrate. In an embodiment, a thin hard mask layer is deposited on the platinum layer on the semiconductor substrate before the patterned photoresist layer is formed.

Provided are: an etchant composition for titanium or titanium alloy, the etchant composition being used for selectively etching a titanium layer or titanium-containing layer formed on an oxide semiconductor layer; and an etching method using said etchant composition. The etchant composition according to the present invention, which is used for etching a titanium layer or titanium-containing layer on an oxide semiconductor, comprises: a compound containing ammonium ions; hydrogen peroxide; and a basic compound, wherein the etchant composition has a pH of 7-11.

Provided are: an etchant composition for titanium or titanium alloy, the etchant composition being used for selectively etching a titanium layer or titanium-containing layer formed on an oxide semiconductor layer; and an etching method using said etchant composition. The etchant composition according to the present invention, which is used for etching a titanium layer or titanium-containing layer on an oxide semiconductor, comprises: a compound containing ammonium ions; hydrogen peroxide; and a basic compound, wherein the etchant composition has a pH of 7-11.

The present invention provides a composition for cleaning a mask comprising a) 0.2 to 10% by weight of two or more alkali compounds selected from alkali hydroxides and alkali carbonates, b) 0.1 to 8% by weight of nitrate, c) 1 to 8% by weight of an oxidizer, and d) residual water, wherein the pH is 11.5 to 14.

According to the present invention, a composition for cleaning a mask and a method for cleaning a mask using the same, which can remove only the film deposited on the mask in a short time without damaging the mask, was provided.

A neutral to alkaline chemical mechanical composition for polishing tungsten includes, as initial components: water; an oxidizing agent selected from an iodate compound, a periodate compound and mixtures thereof; colloidal silica abrasive particles including a nitrogen-containing compound; optionally, a pH adjusting agent; and, optionally, a biocide. The chemical mechanical polishing method includes providing a chemical mechanical polishing pad, having a polishing surface; creating dynamic contact at an interface between the polishing pad and the substrate; and dispensing the neutral to alkaline chemical mechanical polishing composition onto the polishing surface at or near the interface between the polishing pad and the substrate; wherein some of the tungsten is polished away from the substrate and, further, to at least inhibit static etch of the tungsten.

An etching method that includes using the etching liquid composition containing (A) 0.1 to 15 mass % of hydrogen peroxide, (B) 0.01 to 1 mass % of a fluoride ion source, (C) 2-hydroxyethane sulfonic acid or a salt thereof in an amount of 0.1 to 20 mass % in terms of organic sulfonic acid, (D) 0.01 to 5 mass % of at least one compound selected from the group consisting of azole-based compounds and compounds having a structure that has a 6-membered heterocycle including at least one nitrogen atom and three double bonds, and (E) water, is provided.

A method of selectively removing NiPt material from a microelectronic substrate, the method comprising contacting the NiPt material with an aqueous etching composition comprising: an oxidising agent; a strong acid; and a source of chloride.

An etch chemistry solution for treating metallic surfaces in which the etch chemistry solution includes an oxidizing agent and gluconic acid. The etch chemistry solution may also include an oxidizing agent and a short-chained polyethylene polymer glycol or a short-chained polyethylene copolymer glycol. The metallic surfaces are usually used in circuits such as flexible circuits.

Provided are a silicon nitride film etching composition, a method of etching a silicon nitride film using the same, and a manufacturing method of a semiconductor device. Specifically, a silicon nitride film may be stably etched with a high selection ratio relative to a silicon oxide film, and when the composition is applied to an etching process at a high temperature and a semiconductor manufacturing process, not only no precipitate occurs but also anomalous growth in which the thickness of the silicon oxide film is rather increased does not occur, thereby minimizing defects and reliability reduction.