A method of cementing may include preparing a cement composition comprising: cementitious components comprising: a cement; a supplementary cementitious material; and nanoparticulate boehmite; and water; and introducing the cement composition into a subterranean formation.

A method of cementing may include preparing a cement composition comprising: cementitious components comprising: a cement; a supplementary cementitious material; and nanoparticulate boehmite; and water; and introducing the cement composition into a subterranean formation.

A method of cementing may include preparing a cement composition comprising: cementitious components comprising: a cement; a supplementary cementitious material; and nanoparticulate boehmite; and water; and introducing the cement composition into a subterranean formation.

An activating composition, in particular for concrete or industrial mortars containing hydraulic binder and/or pozzolanic material, comprises at least 40% by weight, preferably at least 50% by weight of calcium carbonate and/or magnesium carbonate particles having a d80 less than or equal to 15 .Math.m, and a d50 less than or equal to 4 .Math.m, and at least 1.5% by weight and up to 60% by weight of at least one alkaline metal salt. A binder composition is also provided, the binder composition comprising the activating composition and a component C comprising at least one hydraulic binder. The binder composition and at least one aggregate are combined to form a dry concrete or industrial mortar composition. Also provided is a process for preparing wet concrete or mortar compositions and hardened concrete or industrial mortar compositions obtained therefrom.

An activating composition, in particular for concrete or industrial mortars containing hydraulic binder and/or pozzolanic material, comprises at least 40% by weight, preferably at least 50% by weight of calcium carbonate and/or magnesium carbonate particles having a d80 less than or equal to 15 .Math.m, and a d50 less than or equal to 4 .Math.m, and at least 1.5% by weight and up to 60% by weight of at least one alkaline metal salt. A binder composition is also provided, the binder composition comprising the activating composition and a component C comprising at least one hydraulic binder. The binder composition and at least one aggregate are combined to form a dry concrete or industrial mortar composition. Also provided is a process for preparing wet concrete or mortar compositions and hardened concrete or industrial mortar compositions obtained therefrom.

The invention concerns a method for fluidifying wet concrete or industrial mortar compositions comprising: (a) at least one hydraulic binder, (b) at least one water reducing polymer, (c) at least one accelerator in the form of a salt containing at least one kosmotropic ion, (d) water, and (e) possibly one or more supplementary cementitious materials, and (f) possibly one or more filler materials, the method comprising a step of adding at least one salt (ch) including at least one chaotropic ion to the concrete or industrial mortar composition.

The invention concerns a method for fluidifying wet concrete or industrial mortar compositions comprising: (a) at least one hydraulic binder, (b) at least one water reducing polymer, (c) at least one accelerator in the form of a salt containing at least one kosmotropic ion, (d) water, and (e) possibly one or more supplementary cementitious materials, and (f) possibly one or more filler materials, the method comprising a step of adding at least one salt (ch) including at least one chaotropic ion to the concrete or industrial mortar composition.

A method of manufacturing inorganic binder by reduction furnace slag includes a raw material preparation step, a stirring step, a maintaining step and a drying step. The raw material preparation step is to provide a powder mixture containing 30 wt % to 55 wt % of reduction furnace slag, and 45 wt % to 70 wt % of glass powder. The stirring step is to place the powder mixture in a mixing tank, and add an alkali activator to the mixing tank to stir and react to form mixed slurry. The alkali equivalent (AE) of the mixed slurry is 2% to 7%, and the water-binder ratio is 0.25 to 0.4. The maintaining step is to place the mixed slurry in a high-temperature and high pressure maintaining environment for a maintaining time to get a binder. The drying step is to dry the binder.

A permeable, pourable concrete that has water permeability of on average about 1 inch per hour and compressive strength of an average of about 3000 psi, the permeable concrete comprising a mixture comprising blast-furnace slag, sand, gravel and Portland-type or equivalent cement, the concrete mixed with a predetermined ratio of water, poured into a predetermined form as desired, and set to harden until sufficiently strong.

The invention relates to a device comprising a cable and/or a cable accessory, said cable and/or cable accessory containing at least one insulating and fire-resistant layer, as well as to a method for manufacturing a cable and/or accessory of said type.