A wall compound for use in all applications and particularly well-suited for joining adjacent wallboards. The compound includes a latex resin, a thickener, fibers, and a filler material. In some embodiments, the repair compound is configured to exhibit at least one of yield stress and pseudoplastic-type behavior. In some embodiments, the compound includes hydrophobic and hydrophilic fibers of different morphologies. In some embodiments, the wall compound includes one or more associative thickeners.

A hydraulic binder including (in % by dry weight); A. at least 50 of at least one ground and granulated blast-furnace slag; B. more than 5 of at least one calcium aluminate cement and/or of at least one calcium sulfoaluminate cement; C. more than 5 of at least one source of sulfate ions; D. between 1 and 5 of Ca(OH).sub.2 and/or Portland cement; E. between 0.01 and 1 of at least one alkali metal carbonate; F. and at least one alkalifying reagent consisting of at least one alkali metal carbonate and/or bicarbonate, different from E; under the following conditions: (i) amount of C allows sulfate ions of C to react with B and A; (ii) the amount of F sufficiently causes a reaction with D in water resulting in a wet formulation with a pH not less than 12, for a water-to-mortar mixing rate between 10 and 35% by weight.

A composition including cement, filler, polymer and a compound having epoxide groups and also an amine, wherein the composition contains more than 10% by weight of cement and at room temperature is present as storage-stable free-flowing powder and/or granular material. When mixed with water, the composition makes polymer-modified mortars having good processability, excellent adhesion, strength, water impermeability, chemical resistance and quick coatability possible.

Polyvinyl alcohol-stabilized (meth)acrylic ester polymers, processes for preparing and uses for the same. Where the polyvinyl alcohol-stabilized (meth)acrylic ester polymers have particle sizes Dw of from 100 to 900 nm in the form of aqueous dispersions or water-redispersible powders. Where the (meth)acrylic ester polymers are based on (a) 1% to 30% by weight of one or more vinyl esters of carboxylic acids having 5 to 15 carbon atoms, (b) 20% to 80% by weight of one or more (meth)acrylic esters, wherein the homopolymer of which has a glass transition temperature Tg of ≤20° C., (c) 10% to 70% by weight of one or more (meth)acrylic esters, wherein the homopolymer of which has a glass transition temperature Tg of ≥50° C., and (d) optionally one or more further ethylenically unsaturated monomers. The percentages by weight are based on the total weight of the (meth)acrylic ester polymers.

The present invention relates to a process for producing a redispersible dispersion powder, to the redispersible dispersion powder obtainable by this process, to an aqueous dispersion obtainable by step (1) of this process, and to a building material composition comprising the redispersible dispersion powder and/or the aqueous dispersion, to the use of the redispersible dispersion powder in a building material composition and to the use of the aqueous dispersion for production of a redispersible dispersion powder.

A construction adhesive composition comprises between about 10 weight percent (wt. %) and about 30 wt. % of a vinyl acrylic latex, between about 30 wt. % and about 65 wt. % of calcium carbonate, and a surfactant.

An activating composition, in particular for concrete or industrial mortars containing hydraulic binder and/or pozzolanic material, comprises at least 40% by weight, preferably at least 50% by weight of calcium carbonate and/or magnesium carbonate particles having a d80 less than or equal to 15 .Math.m, and a d50 less than or equal to 4 .Math.m, and at least 1.5% by weight and up to 60% by weight of at least one alkaline metal salt. A binder composition is also provided, the binder composition comprising the activating composition and a component C comprising at least one hydraulic binder. The binder composition and at least one aggregate are combined to form a dry concrete or industrial mortar composition. Also provided is a process for preparing wet concrete or mortar compositions and hardened concrete or industrial mortar compositions obtained therefrom.

The invention relates to compositions of cement and concrete having properties of resistance, modulus and expansion which are significantly improved, using an additive for cement based on thermoplastic styrene-butadiene-styrene (SBS) copolymer in cationic latex, when compared with non-modified cement and concrete references.

Vinyl acetate-ethylene and/or styrene-(meth)acrylic ester copolymers along with processes for preparing the same and uses for the same. Wherein the vinyl acetate-ethylene and/or styrene-(meth)acrylic ester copolymers are in the form of water-redispersible powders for producing hydraulically-setting building material dry formulations. Where the storage stability of the protective-colloid-stabilized vinyl acetate-ethylene or styrene-(meth)acrylic ester copolymers in the form of water-redispersible powders is improved by drying aqueous dispersions comprising protective-colloid-stabilized vinyl acetate-ethylene and/or styrene-(meth)acrylic ester copolymers, one or more water-soluble inorganic salts, and one or more desiccants. Where the water-soluble inorganic salts are selected from the group consisting of alkali metal sulfates and where the desiccants are selected from the group comprising polyvinyl alcohols, polyvinyl acetals, nonionic polyvinylpyrrolidones, nonionic poly(meth)acrylamides, polysaccharides and proteins.

A free-flowing powder composition includes at least one substrate having pores and an external surface between said pores, said surface functionalized with at least one accelerator for a hydraulic setting composition, said accelerator being liquid, hygroscopic, or deliquescent, and wherein after 15 minutes of immersion of free-flowing powder composition in water at 20° C. at least 80% in weight of said accelerator is solubilized, said free-flowing powder composition being immersed in an amount of water sufficient so that the saturation concentration of said accelerator cannot be reached. There is also a method for preparing said free-flowing powder composition. The use of said free-flowing powder composition as an additive for mortar or concrete composition provides an accelerating effect, an anti-ageing effect and an anti-dusting effect. A dry mortar or concrete composition includes a hydraulic binder, said free-flowing powder composition and a granulate, wet mortar or concrete composition and hardened body obtained therefrom.