Disclosed is a polycrystalline ceramic dielectric comprising: crystal grain bulks made of a barium titanate-based ceramic; and grain boundaries comprising interfaces between the crystal grain bulks, wherein the composition of the grain boundaries is controlled using dopants. By controlling the grain boundary composition using dopants so that the dopants are distributed across a width of 5 nm or less and using a nano-sized, fine-grained barium titanate-based ceramic precursor, the grain boundary structure within the polycrystals may maintain electroneutrality, and their ferroelectricity may be controlled, thereby allowing for smoother polarization reaction. Accordingly, the present disclosure provides polycrystalline ceramic dielectrics that have dielectric properties such as high permittivity and low dielectric losses in a wide frequency range, a small amount of reduction in electric field-dependent relative permittivity, high temperature stability, non-reducibility under a reduction sintering condition, and resulting high insulation resistance, and a preparation method therefor.

This disclosure relates to a polycrystalline diamond (PCD) body comprising a PCD material formed of intergrown diamond grains forming a diamond network, and an iron-containing binder.

A method of preparing an ITO ceramic target includes that: In.sub.2O.sub.3 powder with mass fraction of 90˜97 and SnO.sub.2 powder with mass fraction of 10˜3 are ball-milled and mixed with deionized water, diluent, binder and polymer material by a sand mill to obtain an ITO ceramic slurry with a solid content between 70˜80% and a viscosity between 120˜300 mpa.Math.s, with an average particle size D50 of the mixed powder controlled at 100˜300 nm; the ITO ceramic slurry is shaped by a pressure grouting to obtain an ITO ceramic green body with a relative density of 58˜62%; the ITO ceramic green body is put into a degreasing and sintering integrated furnace, and under a degreasing temperature of 700˜800° C., the ITO ceramic target is degreased in an atmospheric oxygen atmosphere for the time set to 12˜36 hours; the temperature increases from the degreasing temperature to the first sintering temperature of 1,600˜1,650° C.

Provided is a method for producing a wavelength conversion sintered body that emits light under irradiation of excitation light. The method for producing a wavelength conversion sintered body includes: preparing a molded body obtained by molding a mixture containing an α-SiAlON fluorescent material and aluminum oxide particles and having a content of Ga of 15 ppm by mass or less; and primary calcining the molded body at a temperature in a range of 1,370° C. or more and 1,600° C. or less to obtain a first sintered body.

A ceramic composition contains Fe, Cu, Ni, Zn, Co, and Cr. When Fe, Cu, Ni, and Zn are converted to Fe.sub.2O.sub.3, CuO, NiO, and ZnO, respectively, and when a total amount of Fe.sub.2O.sub.3, CuO, NiO, and ZnO is 100 parts by mole, the ceramic composition contains 45.00 to 49.70 parts by mole Fe in terms of Fe.sub.2O.sub.3, 2.00 to 8.00 parts by mole Cu in terms of CuO, 19.40 to 45.40 parts by mole Ni in terms of NiO, and 1.00 to 27.00 parts by mole Zn in terms of ZnO. When Fe, Cu, Ni, and Zn are converted to Fe.sub.2O.sub.3, CuO, NiO, and ZnO, respectively, and when a total amount of Fe.sub.2O.sub.3, CuO, NiO, and ZnO is 100 parts by weight, the ceramic composition contains 5 to 100 ppm Co in terms of CoO and 10 to 400 ppm Cr in terms of Cr.sub.2O.sub.3.

A ceramic composition contains Fe, Cu, Ni, Zn, Co, and Cr. When Fe, Cu, Ni, and Zn are converted to Fe.sub.2O.sub.3, CuO, NiO, and ZnO, respectively, and a total amount of Fe.sub.2O.sub.3, CuO, NiO, and ZnO is 100 parts by mole, the ceramic composition contains from 48.20 to 49.85 parts by mole Fe in terms of Fe.sub.2O.sub.3, from 2.00 parts to 8.00 parts by mole Cu in terms of CuO, from 11.90 to 18.70 parts by mole Ni in terms of NiO, and from 27.00 to 33.50 parts by mole Zn in terms of ZnO. When Fe, Cu, Ni, and Zn are converted to Fe.sub.2O.sub.3, CuO, NiO, and ZnO, respectively, and a total amount of Fe.sub.2O.sub.3, CuO, NiO, and ZnO is 100 parts by weight, the ceramic composition contains from 5 to 100 ppm Co in terms of CoO and from 10 to 400 ppm in terms of Cr.sub.2O.sub.3.

This disclosure relates to a polycrystalline cubic boron nitride, PCBN, composite material comprising cubic boron nitride, cBN, particles and a binder matrix material in which the cBN particles are dispersed. The binder matrix material comprises one or more superalloys.

Provided is a dielectric composition containing: a main component expressed by {Ba.sub.xSr.sub.(1-x)}.sub.mTa.sub.4O.sub.12; and a first subcomponent, m satisfying a relationship of 1.95≤m≤2.40. The first subcomponent includes silicon and manganese. When the amount of the main component contained in the dielectric composition is set to 100 parts by mole, the amount of silicon contained in the dielectric composition is 5.0 to 20.0 parts by mole in terms of SiO.sub.2, and the amount of manganese contained in the dielectric composition is 1.0 to 4.5 parts by mole in terms of MnO.

A plant structure includes a ceramic member including at least one of an oxide or an oxide hydroxide as a main component and substantially including no hydrate, and a plant-derived substance directly fixed to the ceramic member without interposing an adhesive substance different from a ceramic material making up the ceramic member. A building member and an interior member each include the plant structure.

The present invention provides a method for producing a zirconia particle-containing powder that enables easy production of a zirconia sintered body having both high translucency and high strength. The present invention relates to a method for producing a zirconia particle-containing powder, comprising a drying step of spray drying a slurry containing zirconia particles, wherein the zirconia particles have an average primary particle diameter of 30 nm or less, and the slurry comprises a dispersion medium containing a liquid having a surface tension at 25° C. of 50 mN/m or less. Preferably, the zirconia particles comprise 2.0 to 9.0 mol % yttria. Preferably, wherein the content of the liquid in the dispersion medium is 50 mass % or more.