Disclosed herein are a heat-shrinkable polyester label film and a preparation method thereof. The label film has a shrinkage force not lower than 5.5 N in at least one shrinkage direction after immersing the heat-shrinkable polyester label film in water at 55° C. for 30 seconds, and a heat shrinkage rate of not lower than 50% in the shrinkage direction after immersing the heat-shrinkable polyester label film in water at 55° C. for 240 seconds.

Embodiments of methods for producing a trimodal polymer in a solution polymerization process comprise three solution polymerization reactors organized in parallel or in series.

A composition including a melt blend of at least one thermoplastic elastomer (TPE) and at least one non-crosslinked elastomer and optionally at least one catalyst for catalyzing chain extension and/or crosslinking and/or coupling reactions of the at least one non-crosslinked elastomer. Further, a method for producing a polymer composition, to a shaped article including a substrate layer composed of the composition, to a method producing a shaped article, and to a method for covering a roof using the shaped articles.

A polymer composition is disclosed that comprises a polymer matrix containing at least one thermotropic liquid crystalline polymer and at least one hollow inorganic filler having a dielectric constant of about 3.0 or less at a frequency of 100 MHz wherein the weight ratio of the at least one thermotropic liquid crystalline polymer to the at least one hollow inorganic filler is from about 0.1 to about 10 and wherein the polymer composition exhibits a dielectric constant of about 4 or less and a dissipation factor of about 0.02 or less, as determined at a frequency of 10 GHz.

The present disclosure relates to a composition for a rack housing member of a vehicle having excellent dimensional stability, and a rack housing member of a vehicle formed therefrom. In an embodiment, the composition for a rack housing member of a vehicle comprises 100 parts by weight of a base resin containing polybutylene terephthalate, an acrylonitrile-styrene-acrylate copolymer, and polyethylene terephthalate, and 40 to 75 parts by weight of an inorganic filler, wherein the inorganic filler includes a glass fiber and a plate-shaped mineral filler.

Adhesive hot-melt formulations with a main polymeric component, of at least one isotactic metallocene butene-1 polymer composition, that has a low viscosity, and that has a bimodal composition, directly obtained during polymerization, in two consecutive and separate reaction steps. Moreover, said hot-melts include less than 5% by weight of at least one viscosity modifier that is not solid at room temperature. Such unusually low level of said additives, surprisingly allows to attain substantially improved levels both of high adhesiveness and cohesion. The adhesive hot-melt formulations include less than 5% by weight of a polyethylene wax or of a blend of polyethylene waxes, that characterized by a highly linear/non-branched structure and by an exceptionally low Polydispersity Index. The presence of such peculiar polyethylene waxes, that are partially incompatible with the butene-1 polymer composition, allows to use the disclosed hot-melt formulations even in the presence of fibrous or perforated substrates.

The invention is directed to a polypropylene composition, to a three-dimensional article comprising said polypropylene composition, and to the use of said composition for automotive articles. The polypropylene composition of the invention comprises: 40-90% by total weight of the composition of a polymer blend comprising polypropylene having a melt flow index as measured according to ISO 1133 at 230° C. and 2.16 kg of 2.0-100 g/10 min; 5-25% by total weight of the composition of one or more plastomers; 0.5-25% by total weight of the composition of mineral filler selected from the group consisting of phyllosilicates, mica or wollastonite; and 0.2-4% by total weight of the composition of glass fibres having an average fibre diameter in the range of 5-30 μm.

A preparation method of a conductive elastomer includes the following steps: (1) according to the mass percent of 20˜75%, dissolving the metallic salts into deionized water to form an electrolyte solution, wherein said metallic salts is either of magnesium nitrate, sodium nitrate, zinc nitrate, cesium nitrate, calcium nitrate, neodymium nitrate, aluminum nitrate, potassium nitrate, potassium chloride, magnesium chloride, calcium chloride, sodium chloride, zinc chloride, cesium chloride, aluminum chloride or their combinations; (2) according to the mass percent of 10˜40%, mixing starches into the electrolyte solution prepared in step (1), then at the temperature of 33˜120 ° C., stirring to gelatinize the starches, forming a viscous liquid; (3) standing the viscous liquid obtained in step (2) at 25˜90° C. for 10 min to 48 h to obtain the conductive elastomer.

The disclosed technology relates to a plastic compound suitable for preparing articles, such as pipe, with good physical properties, such as impact strength, and resistance to environmental stress cracking (ESC). In particular, the technology relates to a vinyl chloride resin, which includes chlorinated polyvinyl chloride (“CPVC”) homopolymer. Further-more, the invention relates to vinyl chloride homopolymer compounds containing the vinyl chloride homopolymer resin, and articles made from such compounds, which compounds meet 23447 cell classifications under ASTM D1784.

Provided herein are metallocene-catalyzed polymer compositions that exhibit advantageous rheological properties, at least some of which are consistent with long-chain branching, as well as polymerization processes suitable for forming such polymer compositions. The polymer compositions may have both LCB index measured at 125° C. of less than 5; and phase angle δ at complex shear modulus G*=100,000 Pa of less than about 54.5°, as determined at 125° C. The polymer compositions of particular embodiments are reactor blends, preferably of ethylene copolymers (e.g., ethylene-propylene (EP) copolymers and/or ethylene-propylene-diene (EPDM) terpolymers). The reactor blend may include first and second copolymer components, which may differ in monomer content and weight-average molecular weight (Mw).