Process for preparing alumina gel in a single precipitation step consisting of dissolving an aluminium precursor, aluminium chloride, in water, at a temperature of 10° C. to 90° C. such that the pH of the solution is from 0.5 to 5, for a period of 2 to 60 minutes, then adjusting the pH to 7.5 to 9.5 by adding a basic precursor, sodium hydroxide, to the solution obtained to obtain a suspension, at a temperature of 5° C. to 35° C., and for 5 minutes to 5 hours, followed by a filtration step, said process not comprising any washing steps. Also, novel alumina gel having a high dispersibility index, in particular a dispersibility index of more than 80%, a crystallite dimension of 0.5 to 10 nm, a chlorine content of 0.001% to 2% by weight and a sodium content of 0.001% to 2% by weight, the percentages by weight being expressed with respect to the total weight of the alumina gel.

The present invention relates to a method of forming a cured conductive binder material, to a method of forming a curable binder formulation, to a curable binder formulation, to a cured conductive binder material and to an electrochemical cell. In one embodiment, the method of forming a cured conductive binder material includes the steps of: (i) providing a liquid formulation comprising a liquid carrier, at least one active material, at least one polymeric binder and at least one modified metal coordination complex; and (ii) curing the liquid formulation of step (i), to thereby form a cured conductive binder material.

Provided herein is a method of preparing a ceramic material, the method including: providing a ceramic gel including a plurality of metal salts and compressing the ceramic gel thereby inducing stress-induced mineralization of the ceramic gel and formation of the ceramic material, wherein the ceramic gel exists in isolated form.

Methods of making robust bijels include dispersing metal oxide precursors and/or metal salts into at least one phase of a bijel and hydrolyzing and condensing the metal oxide precursors and/or metal salts in a sol-gel reaction to form sintered bridges between interfacially jammed surface-active nanoparticles. The methods can be used with any bijels, including those produced during solvent transfer-induced phase separation (STRIPS) methods and other methods. A robust bijel includes chemically sintered bridges between the interfacially jammed surface-active nanoparticles. Methods of making nanocatalyst-functionalized sintered bijels include adsorbing metal salts to a surface of sintered interfacially jammed nanoparticles of bijels, and reducing the metal precursors on the surface of the sintered nanoparticles. Nanocatalyst-functionalized sintered bijels include catalytically active metal or metal oxide nanocatalysts on a surface of the sintered interfacially jammed surface-active nanoparticles.

Methods and systems for manufacturing a mixed-metal part by preparing a mixed-metal sol-gel as a feed material and using an additive manufacturing technique to form the mixed-metal part from the mixed-metal sol-gel feed material.

Methods of making robust bijels include dispersing metal oxide precursors and/or metal salts into at least one phase of a bijel and hydrolyzing and condensing the metal oxide precursors and/or metal salts in a sol-gel reaction to form sintered bridges between interfacially jammed surface-active nanoparticles. The methods can be used with any bijels, including those produced during solvent transfer-induced phase separation (STRIPS) methods and other methods. A robust bijel includes chemically sintered bridges between the interfacially jammed surface-active nanoparticles. Methods of making nanocatalyst-functionalized sintered bijels include adsorbing metal salts to a surface of sintered interfacially jammed nanoparticles of bijels, and reducing the metal precursors on the surface of the sintered nanoparticles. Nanocatalyst-functionalized sintered bijels include catalytically active metal or metal oxide nanocatalysts on a surface of the sintered interfacially jammed surface-active nanoparticles.

Process for preparing alumina gel in a single precipitation step consisting of dissolving an aluminium precursor, aluminium chloride, in water, at a temperature of 10 C. to 90 C. such that the pH of the solution is from 0.5 to 5, for a period of 2 to 60 minutes, then adjusting the pH to 7.5 to 9.5 by adding a basic precursor, sodium hydroxide, to the solution obtained to obtain a suspension, at a temperature of 5 C. to 35 C., and for 5 minutes to 5 hours, followed by a filtration step, said process not comprising any washing steps. Also, novel alumina gel having a high dispersibility index, in particular a dispersibility index of more than 80%, a crystallite dimension of 0.5 to 10 nm, a chlorine content of 0.001% to 2% by weight and a sodium content of 0.001% to 2% by weight, the percentages by weight being expressed with respect to the total weight of the alumina gel.

The invention provides a new method for preparing ultra-small polymeric-lipidic delivery nanoparticles (USDNs) that were synthesized by a nanoprecipitation method followed by a layer-by-layer nanodeposition. The USDNs particle size can be controlled between 5-25 nm and provides loading capacities of 22.12% to 72.08%. Moreover, the USDNs platform provides pH controlled drug release, within a terminal release ratio of 68% at pH 5.0 and almost no release to pH of 7.5. Furthermore, based on their small sizes (5-25 nm) and unique composition, the USDNs penetrates the skin strata efficiently, release the payload at the target site as topical or transdermal treatment of a variety of skin disorders. Additionally the USDNs system can be used to treat and diagnoses other crucial diseases (Cancer, Alzheimer, etc) can be combined with various micro-needles or needles free array technologies for special application.

Methods of making robust bijels include dispersing metal oxide precursors and/or metal salts into at least one phase of a bijel and hydrolyzing and condensing the metal oxide precursors and/or metal salts in a sol-gel reaction to form sintered bridges between interfacially jammed surface-active nanoparticles. The methods can be used with any bijels, including those produced during solvent transfer-induced phase separation (STRIPS) methods and other methods. A robust bijel includes chemically sintered bridges between the interfacially jammed surface-active nanoparticles. Methods of making nanocatalyst-functionalized sintered bijels include adsorbing metal salts to a surface of sintered interfacially jammed nanoparticles of bijels, and reducing the metal precursors on the surface of the sintered nanoparticles. Nanocatalyst-functionalized sintered bijels include catalytically active metal or metal oxide nanocatalysts on a surface of the sintered interfacially jammed surface-active nanoparticles.

Provided herein is a method of preparing a ceramic material, the method including: providing a ceramic gel including a plurality of metal salts and compressing the ceramic gel thereby inducing stress-induced mineralization of the ceramic gel and formation of the ceramic material, wherein the ceramic gel exists in isolated form.