Concrete may be melted to form a glass product. Methods and batch compositions including concrete may be used to produce amorphous silica materials including, but not limited to, glass, container glass, fiber glass, glass bead, glass spheres, sheet or plate glass, glass aggregate, glass sand, abrasives, proppants, foamed glass, and manufactured glass articles. The initial processing steps include preparing a melt batch comprising concrete and, optionally, other components, melting the melt batch, and cooling the melted melt batch. Further processing steps may be utilized to produce the glass article.

Concrete may be melted to form a glass product. Methods and batch compositions including concrete may be used to produce amorphous silica materials including, but not limited to, glass, container glass, fiber glass, glass bead, glass spheres, sheet or plate glass, glass aggregate, glass sand, abrasives, proppants, foamed glass, and manufactured glass articles. The initial processing steps include preparing a melt batch comprising concrete and, optionally, other components, melting the melt batch, and cooling the melted melt batch. Further processing steps may be utilized to produce the glass article.

The present disclosure provides a solidifying method of a radionuclide. The solidifying method of the radionuclide includes operations of: providing a low melting point glass including Bi.sub.2O.sub.3, B.sub.2O.sub.3, ZnO and SiO.sub.2; providing a glass mixture mixing a mixture to be treated containing a hydroxide of radionuclide and BaSO.sub.4 and the low melting point glass; and heating the glass mixture.

The invention relates to a glass melting process comprising melting glass cullet in a submerged combustion melter comprising at least one submerged burner, under oxidizing conditions, wherein the glass cullet comprises increased levels of contaminants.

The invention relates to a glass melting process comprising melting glass cullet in a submerged combustion melter comprising at least one submerged burner, under oxidizing conditions, wherein the glass cullet comprises increased levels of contaminants.

The present invention relates to a method and a plant for treating carbon-containing waste that may comprise mineral fillers and/or potential contaminants. This method comprises: preparing a molten glass bath at a temperature between 1100° C. and 1600° C.; loading the waste to be treated into said molten glass bath; injecting an oxidizer and optionally a fuel under pressure into said molten glass bath by means of at least one hose, one end of which is immersed in said bath, said oxidizer being introduced in a molar amount less than the molar amount of the carbon-containing compounds, thus causing combustion of said waste and generation of hot synthesis gases; implementing heat exchange between a heat-transfer fluid and the hot synthesis gases in conditions allowing simultaneous recovery of at least part of their heat energy and at least part of the heat energy released by their combustion, air being injected sequentially into said gases during said heat exchange to cause self-ignition of the mixture of said gases and air, each injection increasing the degree of combustion.

The present invention relates to a method and a plant for treating carbon-containing waste that may comprise mineral fillers and/or potential contaminants. This method comprises: preparing a molten glass bath at a temperature between 1100° C. and 1600° C.; loading the waste to be treated into said molten glass bath; injecting an oxidizer and optionally a fuel under pressure into said molten glass bath by means of at least one hose, one end of which is immersed in said bath, said oxidizer being introduced in a molar amount less than the molar amount of the carbon-containing compounds, thus causing combustion of said waste and generation of hot synthesis gases; implementing heat exchange between a heat-transfer fluid and the hot synthesis gases in conditions allowing simultaneous recovery of at least part of their heat energy and at least part of the heat energy released by their combustion, air being injected sequentially into said gases during said heat exchange to cause self-ignition of the mixture of said gases and air, each injection increasing the degree of combustion.

Concrete may be melted to form a glass product. Methods and batch compositions including concrete may be used to produce amorphous silica materials including, but not limited to, glass, container glass, fiber glass, glass bead, glass spheres, sheet or plate glass, glass aggregate, glass sand, abrasives, proppants, foamed glass, and manufactured glass articles. The initial processing steps include preparing a melt batch comprising concrete and, optionally, other components, melting the melt batch, and cooling the melted melt batch. Further processing steps may be utilized to produce the glass article.

Concrete may be melted to form a glass product. Methods and batch compositions including concrete may be used to produce amorphous silica materials including, but not limited to, glass, container glass, fiber glass, glass bead, glass spheres, sheet or plate glass, glass aggregate, glass sand, abrasives, proppants, foamed glass, and manufactured glass articles. The initial processing steps include preparing a melt batch comprising concrete and, optionally, other components, melting the melt batch, and cooling the melted melt batch. Further processing steps may be utilized to produce the glass article.

The invention relates to a glass melting process comprising melting glass cullet in a submerged combustion melter comprising at least one submerged burner, under oxidizing conditions, wherein the glass cullet comprises increased levels of contaminants.