A method for depositing a metal-based coating on a particulate substrate, including: i) preparing a mixture comprising the particulate substrate, a powder comprising a coating metal oxide of one or more of Ti, Al, Zn, Sn, In, Sb, Ag, Co, V, Ni, Cr, Mn, Fe, Cu, Pt, Pd, Ta, Zr, Nb, Rh, Ru, Mo, Os, Re and W, a reducing agent powder of Al metal or Al alloy, and a powder of aluminium chloride; and ii) mixing and heating the mixture to form a coating on the particulate substrate, to produce a coated substrate product.

A method for depositing a metal-based coating on a particulate substrate, including: i) preparing a mixture comprising the particulate substrate, a powder comprising a coating metal oxide of one or more of Ti, Al, Zn, Sn, In, Sb, Ag, Co, V, Ni, Cr, Mn, Fe, Cu, Pt, Pd, Ta, Zr, Nb, Rh, Ru, Mo, Os, Re and W, a reducing agent powder of Al metal or Al alloy, and a powder of aluminium chloride; and ii) mixing and heating the mixture to form a coating on the particulate substrate, to produce a coated substrate product.

Methodologies, systems, and devices are provided for producing metal spheroidal powder products. By utilizing a microwave plasma, control over spheriodization and resulting microstructure can be tailored to meet desired demands.

Methodologies, systems, and devices are provided for producing metal spheroidal powder products. By utilizing a microwave plasma, control over spheriodization and resulting microstructure can be tailored to meet desired demands.

Methodologies, systems, and devices are provided for producing metal spheroidal powder products. By utilizing a microwave plasma, control over spheriodization and resulting microstructure can be tailored to meet desired demands.

The present disclosure is directed at methods of preparing rare earth-based permanent magnets having improved coercivity and remanence, the method comprising one or more steps comprising: (a) homogenizing a first population of particles of a first GBM alloy with a second population of particles of a second core alloy to form a composite alloy preform, the first GBM alloy being substantially represented by the formula: AC.sub.bR.sub.xCo.sub.yCu.sub.dM.sub.z, the second core alloy being substantially represented by the formula G.sub.2Fe.sub.14B, where AC, R, M, G, b, x, y, and z are defined; (b) heating the composite alloy preform particles to form a population of mixed alloy particles; (c) compressing the mixed alloy particles, under a magnetic field of a suitable strength to align the magnetic particles with a common direction of magnetization and inert atmosphere, to form a green body; (d) sintering the green body; and (e) annealing the sintered body. Particular embodiments include magnets comprising neodymium-iron-boron core alloys, including Nd.sub.2Fe.sub.14B.

The present disclosure is directed at methods of preparing rare earth-based permanent magnets having improved coercivity and remanence, the method comprising one or more steps comprising: (a) homogenizing a first population of particles of a first GBM alloy with a second population of particles of a second core alloy to form a composite alloy preform, the first GBM alloy being substantially represented by the formula: AC.sub.bR.sub.xCo.sub.yCu.sub.dM.sub.z, the second core alloy being substantially represented by the formula G.sub.2Fe.sub.14B, where AC, R, M, G, b, x, y, and z are defined; (b) heating the composite alloy preform particles to form a population of mixed alloy particles; (c) compressing the mixed alloy particles, under a magnetic field of a suitable strength to align the magnetic particles with a common direction of magnetization and inert atmosphere, to form a green body; (d) sintering the green body; and (e) annealing the sintered body. Particular embodiments include magnets comprising neodymium-iron-boron core alloys, including Nd.sub.2Fe.sub.14B.

This invention aims at providing a carbon-coated metal powder having few impurities, a narrower particle size distribution, and sintering properties particularly suitable as a conductive powder of a conductive paste for forming internal conductors in a ceramic multilayer electronic component obtained by co-firing multilayered ceramic sheets and internal conductor layers; a conductive paste containing the carbon-coated metal powder; a multilayer electronic component using the conductive paste; and a method for manufacturing the carbon-coated metal powder. The carbon-coated metal powder has specific properties in TMA or ESCA measurements. The carbon-coated metal powder can be obtained by melting and vaporizing a metallic raw material in a reaction vessel, conveying the generated metal vapor into a cooling tube and rapidly cooling the metal vapor by endothermically decomposing a carbon source supplied into the cooling tube, and forming a carbon coating film on metal nuclei surfaces in parallel with generation of the metal nuclei.

This invention aims at providing a carbon-coated metal powder having few impurities, a narrower particle size distribution, and sintering properties particularly suitable as a conductive powder of a conductive paste for forming internal conductors in a ceramic multilayer electronic component obtained by co-firing multilayered ceramic sheets and internal conductor layers; a conductive paste containing the carbon-coated metal powder; a multilayer electronic component using the conductive paste; and a method for manufacturing the carbon-coated metal powder. The carbon-coated metal powder has specific properties in TMA or ESCA measurements. The carbon-coated metal powder can be obtained by melting and vaporizing a metallic raw material in a reaction vessel, conveying the generated metal vapor into a cooling tube and rapidly cooling the metal vapor by endothermically decomposing a carbon source supplied into the cooling tube, and forming a carbon coating film on metal nuclei surfaces in parallel with generation of the metal nuclei.

Zinc is added to a metal magnetic alloy powder including iron and silicon. An element is formed using this magnetic material, and a coil is formed inside or on the surface of the element.