The present disclosure discloses a preparation method of a powder metallurgy (PM) superalloy with high strength and plasticity. Under the multi-field coupling action of a thermal field and a force field, the PM superalloy is obtained in a high-temperature graphite mold by using the method of conducting heat preservation and oscillating-pressure sintering in two steps. Under the action of a circulating pressure, rearrangement of powders and discharge of pores are promoted, and therefore, the PM superalloy is sintered and formed. The present disclosure further discloses a PM superalloy prepared by using the method above. The PM superalloy has the characteristics of low grade of prior particle boundary defects, uniform grain refinement and high density. The sintered PM superalloy obtained in the present disclosure has a yield strength of 955 MPa, a tensile strength of 1,437 MPa and an elongation of 31.9%, and has high strength and plasticity.

The present disclosure discloses a preparation method of a powder metallurgy (PM) superalloy with high strength and plasticity. Under the multi-field coupling action of a thermal field and a force field, the PM superalloy is obtained in a high-temperature graphite mold by using the method of conducting heat preservation and oscillating-pressure sintering in two steps. Under the action of a circulating pressure, rearrangement of powders and discharge of pores are promoted, and therefore, the PM superalloy is sintered and formed. The present disclosure further discloses a PM superalloy prepared by using the method above. The PM superalloy has the characteristics of low grade of prior particle boundary defects, uniform grain refinement and high density. The sintered PM superalloy obtained in the present disclosure has a yield strength of 955 MPa, a tensile strength of 1,437 MPa and an elongation of 31.9%, and has high strength and plasticity.

A tool and die set and related method of use of the tool and die set in a press for the compaction of a powder metal into a preform involves an uneven amount of positional deflection of at least two lower or upper tool members. This asymmetrical elastic response under load may help to eliminate cracking of the part after the compressive load is removed.

A tool and die set and related method of use of the tool and die set in a press for the compaction of a powder metal into a preform involves an uneven amount of positional deflection of at least two lower or upper tool members. This asymmetrical elastic response under load may help to eliminate cracking of the part after the compressive load is removed.

Disclosed are systems, devices, and methods for additive manufacturing that allow for control of composition and/or porosity of components being manufactured. More particularly, in exemplary embodiments, a secondary material can be used in conjunction with a primary feedstock material in a spatially controlled manner during an additive manufacturing process to control a composition of materials and/or porosity of a manufactured component. Systems, devices, and methods for additive manufacturing are also disclosed that allow for control of a pressure of an atmosphere surrounding a build surface during an additive manufacturing process. More particularly, a pressure of an atmosphere surrounding a build surface can be raised to a pressure greater than standard atmospheric pressure. Various features of the exemplary embodiments of the systems, devices, and methods disclosed can be used together to further control for composition and/or porosity and quality of a manufactured part.

Disclosed are systems, devices, and methods for additive manufacturing that allow for control of composition and/or porosity of components being manufactured. More particularly, in exemplary embodiments, a secondary material can be used in conjunction with a primary feedstock material in a spatially controlled manner during an additive manufacturing process to control a composition of materials and/or porosity of a manufactured component. Systems, devices, and methods for additive manufacturing are also disclosed that allow for control of a pressure of an atmosphere surrounding a build surface during an additive manufacturing process. More particularly, a pressure of an atmosphere surrounding a build surface can be raised to a pressure greater than standard atmospheric pressure. Various features of the exemplary embodiments of the systems, devices, and methods disclosed can be used together to further control for composition and/or porosity and quality of a manufactured part.

While a molten metal of copper heated to a temperature, which is higher than the melting point of copper by 250 to 700° C. (preferably 350 to 650° C. and more preferably 450 to 600° C.), is allowed to drop, a high-pressure water is sprayed onto the heated molten metal of copper in a non-oxidizing atmosphere (such as an atmosphere of nitrogen, argon, hydrogen or carbon monoxide) to rapidly cool and solidify the heated molten metal of copper to produce a copper powder which has an average particle diameter of 1 to 10 μm and a crystallite diameter Dx.sub.(200) of not less than 40 nm on (200) plane thereof, the content of oxygen in the copper powder being 0.7% by weight or less.

While a molten metal of copper heated to a temperature, which is higher than the melting point of copper by 250 to 700° C. (preferably 350 to 650° C. and more preferably 450 to 600° C.), is allowed to drop, a high-pressure water is sprayed onto the heated molten metal of copper in a non-oxidizing atmosphere (such as an atmosphere of nitrogen, argon, hydrogen or carbon monoxide) to rapidly cool and solidify the heated molten metal of copper to produce a copper powder which has an average particle diameter of 1 to 10 μm and a crystallite diameter Dx.sub.(200) of not less than 40 nm on (200) plane thereof, the content of oxygen in the copper powder being 0.7% by weight or less.

The present disclosure provides three-dimensional (3D) printing processes, apparatuses, software, and systems for the production of at least one desired 3D object. The 3D printer system (e.g., comprising a processing chamber, build module, or an unpacking station) described herein may retain a desired (e.g., inert) atmosphere around the material bed and/or 3D object at multiple 3D printing stages. The 3D printer described herein comprises one or more build modules that may have a controller separate from the controller of the processing chamber. The 3D printer described herein comprises a platform that may be automatically constructed. The invention(s) described herein may allow the 3D printing process to occur for a long time without operator intervention and/or down time.

The present disclosure provides three-dimensional (3D) printing processes, apparatuses, software, and systems for the production of at least one desired 3D object. The 3D printer system (e.g., comprising a processing chamber, build module, or an unpacking station) described herein may retain a desired (e.g., inert) atmosphere around the material bed and/or 3D object at multiple 3D printing stages. The 3D printer described herein comprises one or more build modules that may have a controller separate from the controller of the processing chamber. The 3D printer described herein comprises a platform that may be automatically constructed. The invention(s) described herein may allow the 3D printing process to occur for a long time without operator intervention and/or down time.