The present invention provides a high-strength and high-plasticity titanium matrix composite and a preparation method thereof. The preparation method includes: preparing high-oxygen hydride-dehydride titanium powder using a high-temperature rotary ball grinding treatment process, in which the prepared hydride-dehydride titanium powder has a particle size of 10-40 μm, and has an oxygen content of 0.8-1.5 wt. %; preparing high-purity ultra-fine oxygen adsorbent powder using a wet grinding method of high-energy vibration ball grinding treatment process; in which a purity of the oxygen adsorbent powder is ≥99.9%, and a particle size of the oxygen adsorbent powder is ≤8 μm; mixing the high-oxygen hydride-dehydride titanium powder with the oxygen adsorbent powder in a protective atmosphere, and then press-forming the powder obtained after mixing to obtain a raw material blank; and performing atmosphere protective sintering treatment on the raw material blank to obtain a titanium matrix composite. The method prepares a titanium matrix composite reinforced by in-situ self-generating multi-scale Ca—Ti—O, TiC, TiB particles. The microstructure and grains are effectively refined, and the strength and plasticity of the material are significantly improved.

The present invention discloses a short process preparation technology of sintered NdFeB magnets from the NdFeB sludge, which relates to a field of recycle technology of NdFeB sludge. The present invention comprises the following steps: water bath distillation of organics in sludge, ultrasonic cleaning, calcium reduction and diffusion, ultrasonic rinsing in a magnetic field and drying, powders mixing and sintering. NdFeB sludge as raw materials was directly prepared from recycled sintered magnets with high magnetic properties. Most of the organics in the sludge could be removed by a vacuum distillation process with stepwise heating. The ultrasonic rinsing process in a magnetic field could effectively remove the remaining organics. The recycled sintered magnets exhibited good maximum energy product [(BH).sub.max] of 35.26 MGOe. The present invention has important features, such as the short processing time, efficient environmental protection, high recycling rate and effective utilization rate of rare earth metals.

The present invention relates to a method for the economic production of metallic parts, with high flexibility in the geometry attainable. It also relates to the material required for the manufacturing of those parts. The method of the present invention allows for a very fast manufacturing of the parts. Also some forming technologies applicable to polymers can be used. The method allows for the fast and economic production of complex geometry metallic parts.

A method for producing a powder-metallurgical product may include providing a powder mixture, forming the powder mixture into a green body, and sintering the green body to form a resulting powder-metallurgical product. The powder mixture may include a first hard phase, a second hard phase, 0 to 1.8% by weight of graphite, 0 to 5% by weight each of cobalt, tri-iron phosphide, copper, bronze, phosphorous, sulphur, calcium fluoride and molybdenum, 0.1 to 1.8% by weight of a pressing aid and a flow improver, and a remaining proportion that is an iron-base powder. The first hard phase may include 52 to 78% by weight of molybdenum, 0 to 2% by weight of silicon, 0 to 1.5% by weight of copper, and a remaining weight proportion of iron and production-related contaminations. The second hard phase may include 0 to 0.8% by weight of manganese and less than 0.1% by weight of carbon.

A method for producing a powder-metallurgical product may include providing a powder mixture, forming the powder mixture into a green body, and sintering the green body to form a resulting powder-metallurgical product. The powder mixture may include a first hard phase, a second hard phase, 0 to 1.8% by weight of graphite, 0 to 5% by weight each of cobalt, tri-iron phosphide, copper, bronze, phosphorous, sulphur, calcium fluoride and molybdenum, 0.1 to 1.8% by weight of a pressing aid and a flow improver, and a remaining proportion that is an iron-base powder. The first hard phase may include 52 to 78% by weight of molybdenum, 0 to 2% by weight of silicon, 0 to 1.5% by weight of copper, and a remaining weight proportion of iron and production-related contaminations. The second hard phase may include 0 to 0.8% by weight of manganese and less than 0.1% by weight of carbon.

A method is for the economic production of metallic parts, with high flexibility in the geometry. Certain materials are required for the manufacturing of those parts. The method allows for a very fast manufacturing of the parts. The method may use some forming technologies applicable to polymers. The method allows for the fast and economic production of complex geometry metallic parts.

The present invention provides a high-strength and high-plasticity titanium matrix composite and a preparation method thereof. The preparation method includes: preparing high-oxygen hydride-dehydride titanium powder using a high-temperature rotary ball grinding treatment process, in which the prepared hydride-dehydride titanium powder has a particle size of 10-40 m, and has an oxygen content of 0.8-1.5 wt. %; preparing high-purity ultra-fine oxygen adsorbent powder using a wet grinding method of high-energy vibration ball grinding treatment process; in which a purity of the oxygen adsorbent powder is 99.9%, and a particle size of the oxygen adsorbent powder is 8 m; mixing the high-oxygen hydride-dehydride titanium powder with the oxygen adsorbent powder in a protective atmosphere, and then press-forming the powder obtained after mixing to obtain a raw material blank; and performing atmosphere protective sintering treatment on the raw material blank to obtain a titanium matrix composite. The method prepares a titanium matrix composite reinforced by in-situ self-generating multi-scale CaTiO, TiC, TiB particles. The microstructure and grains are effectively refined, and the strength and plasticity of the material are significantly improved.

The present invention relates to a method for the economic production of metallic parts, with high flexibility in the geometry attainable. It also relates to the material required for the manufacturing of those parts. The method of the present invention allows for a very fast manufacturing of the parts. Also some forming technologies applicable to polymers can be used. The method allows for the fast and economic production of complex geometry metallic parts.