The present disclosure is directed at methods of preparing rare earth-based permanent magnets having improved coercivity and remanence, the method comprising one or more steps comprising: (a) homogenizing a first population of particles of a first GBM alloy with a second population of particles of a second core alloy to form a composite alloy preform, the first GBM alloy being substantially represented by the formula: AC.sub.bR.sub.xCo.sub.yCu.sub.dM.sub.z, the second core alloy being substantially represented by the formula G.sub.2Fe.sub.14B, where AC, R, M, G, b, x, y, and z are defined; (b) heating the composite alloy preform particles to form a population of mixed alloy particles; (c) compressing the mixed alloy particles, under a magnetic field of a suitable strength to align the magnetic particles with a common direction of magnetization and inert atmosphere, to form a green body; (d) sintering the green body; and (e) annealing the sintered body. Particular embodiments include magnets comprising neodymium-iron-boron core alloys, including Nd.sub.2Fe.sub.14B.

A polycrystalline super hard construction has a first region having a body of thermally stable polycrystalline super hard material having a plurality of intergrown grains of super hard material; a second region forming a substrate having a hard phase and a binder phase; and a third region interposed between the first and second regions. The third region includes a composite material having a first phase comprising a plurality of non-intergrown grains of super hard material, and a matrix material. A fourth region interposed between the second and third region has a major proportion having one or more components of the binder material of the second region, and one or more reaction products between the binder material of the second region and one or more components of the third region.

A material for producing a three-dimensionally printed part including a metal material and at least one sintering aid in an amount effective to give the three-dimensionally printed part a density of between about 90% and about 100% after sintering is disclosed. A method of printing a three-dimensional part including selecting a metal material, incorporating at least one sintering aid into the metal material to form a print material, and printing the three-dimensional part is also disclosed. A method of producing a sintered metal part including providing a metal material for the sintered metal part incorporating boron as a first sintering aid, incorporating phosphorus as a second sintering aid, forming the metal part in a predetermined form the metal material, and heating the formed metal part to a sintering temperature is also disclosed. Three-dimensionally printed parts are also disclosed.

A material for producing a three-dimensionally printed part including a metal material and at least one sintering aid in an amount effective to give the three-dimensionally printed part a density of between about 90% and about 100% after sintering is disclosed. A method of printing a three-dimensional part including selecting a metal material, incorporating at least one sintering aid into the metal material to form a print material, and printing the three-dimensional part is also disclosed. A method of producing a sintered metal part including providing a metal material for the sintered metal part incorporating boron as a first sintering aid, incorporating phosphorus as a second sintering aid, forming the metal part in a predetermined form the metal material, and heating the formed metal part to a sintering temperature is also disclosed. Three-dimensionally printed parts are also disclosed.

A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1−m) (Pr.sub.25Nd.sub.75)].sub.x(Fe.sub.100-a-b-c-dM.sub.aGa.sub.bIn.sub.cSn.sub.d).sub.100-x-yB.sub.y formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1−m) (Pr.sub.25Nd.sub.75)].sub.x(Fe.sub.100-a-b-c-dM.sub.aGa.sub.bIn.sub.cSn.sub.d).sub.100-x-yB.sub.y formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

A component obtainable by a process which includes providing a composition and sintering the composition at a sintering temperature of from 1250° C. to 1400° C. for a period of from 3 to 15 minutes. The composition includes hard material particles with an inner core of fused tungsten carbide and an outer shell of tungsten carbide, and a binder metal selected from Co, Ni, Fe and alloys with at least one metal selected from Co, Ni and Fe.

A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1-m) (Pr.sub.25Nd.sub.75)].sub.x(Fe.sub.100-a-b-c-dM.sub.aGa.sub.bIn.sub.cSn.sub.d).sub.100-x-yB.sub.y formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1-m) (Pr.sub.25Nd.sub.75)].sub.x(Fe.sub.100-a-b-c-dM.sub.aGa.sub.bIn.sub.cSn.sub.d).sub.100-x-yB.sub.y formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

An improved atomized powder metal material containing an increased amount of free graphite after heat treatment and/or sintering is provided. The powder metal material is typically a ferrous alloy and includes carbon in an amount of 1.0 wt. % to 6.5 wt. % and silicon in an amount of 0.1 wt. % to 6.0 wt. %, based on the total weight of the powder metal material. The powder metal material can also include various other alloying elements, for example at least one of nickel (Ni), cobalt (Co), copper (Cu), tin (Sn), aluminum (Al), sulfur (S), phosphorous (P), boron (B), nitrogen (N), chromium (Cr), manganese (Mn), molybdenum (Mo), vanadium (V), niobium (Nb), tungsten (W), titanium (Ti), tantalum (Ta) zirconium (Zr), zinc (Zn), strontium (Sr), calcium (Ca), barium (Ba) magnesium (Mg), lithium (Li), sodium (Na), and potassium (K).