A multilayered flexible package comprises a polymeric coating (2) that contains a dispersion of antioxidant capsules (3) having a particle size distribution comprised between 0.1 and 10 μm and a core-shell structure comprising a core (4), of an antioxidant with a reduction potential comprised between 0.1 and 0.5 V, and a polymeric shell (5) covering the core (4) at least by 70%.

A method for producing elastic laminates includes gripping first and second continuous elastic films in respective gripping zones by respective first and second stretching members, transversely stretching the first and second continuous elastic films by rotating said first and second stretching members about respective first and second axes of rotation inclined with respect to each other, and releasing the transversely stretched first and second continuous elastic films from the respective first and second stretching members in respective release zones aligned along a common transverse release line.

The present disclosure provides a resin composition containing a bio-polyethylene resin (A), an ethylene-vinyl alcohol copolymer (B), and an alkali metal salt (C), wherein the content of the alkali metal salt (C) is 10 ppm to 1500 ppm, in terms of metal, with respect to the weight of the ethylene-vinyl alcohol copolymer (B). With this resin composition, gel formation and a reduction in transparency during molding are suppressed, and a molded product having an excellent appearance can thus be obtained.

The invention provides a sealant film that is less likely to adsorb components formed of various types of organic compounds, has excellent heat sealing characteristics at 140° C., while having low heat sealing strength at 100° C. and being less likely for heat sealing layers to adhere to each other even when the film is used as a packaging bag and the content thereof is warmed in boiling water. The sealant film has at least one heat sealing layer consisting of a polyester component, wherein a heat sealing strength of the heat sealing layer being heat sealed to another heat sealing layer at 100° C. and 0.2 MPa for 2 seconds is 0-5 N/15 mm and at 140° C. and 0.2 MPa for 2 seconds is 8-30 N/15 mm, and a film density including all layers is 1.20 or more and less than 1.39.

Oriented, multilayer shrink films, either clear or opaque, comprise a core layer and at least one skin layer. The core layer has a thickness greater than the thickness of the at least one skin layer. The at least one skin layer comprises at least one cyclic-olefin copolymer as the predominant component thereof. The core layer comprises a blend of a polyolefin polymer and a polybutene-1 copolymer with ethylene, the butene-1 constituting over 75% by weight of the polybutene-1 copolymer. The film has a shrinkage of at least 20% in at least one of the machine and transverse directions of formation when said film is heated to a temperature of between 80 and 100° C. Optionally the films can include a propylene-based elastomer, a styrenic based block copolymer elastomer, reclaim including the components of the film, or combinations thereof.

A process for producing a resinous panel which is for use as at least some of the front panel of an article, the process including (A) a step in which a resin sheet having a thickness of 0.5-10 mm is fixed to a working table and (B) a step in which the resin sheet is punched out by forcing a Thomson blade into the resin sheet approximately perpendicularly thereto from the side where the surface of the resin sheet is to be the outer surface of the article, thereby obtaining the front panel, wherein (C) the Thomson blade is a double-edged blade having an edge angle of 30-60 degrees. The resin sheet has a tensile modulus of preferably 1,500 MPa or greater. Preferably, the resin sheet includes a transparent resin sheet layer and a colored resin sheet layer in this order from the surface that is to be the outer surface of the article. The colored resin sheet is one which does not break when a DuPont impact test was conducted in accordance with ASTM-D2794 in a 0° C. environment under the conditions of a height of 50 cm, an impactor diameter of 1 inch, an impactor weight of 1 Kg, and a pedestal diameter of ½ inch.

In an embodiment, a heat-seal film includes 10-90 wt % of a first polymer component and 10-90 wt % of a second polymer component, based on a total weight of the first polymer component and the second polymer component, wherein: the first polymer component includes propylene, and optionally, up to 18 wt % of a C.sub.2 and/or a C.sub.4-C.sub.20 α-olefin based on a total weight of the first polymer component; and the second polymer component includes 91-99.9 wt % of propylene and 0.1-9 wt % of ethylene based on a total weight of the second polymer component, the second copolymer component having a melt flow rate of 2-60 g/10 min. In another embodiment, a multi-layer film structure includes a heat-seal layer including a heat-seal film described herein; and an unoriented, an uniaxially oriented, or a biaxially oriented base layer including polypropylene homopolymer, a polypropylene random copolymer, or a combination thereof.

Regioselectively substituted cellulose esters having a plurality of pivaloyl substituents and a plurality of aryl-acyl substituents are disclosed along with methods for making the same. Such cellulose esters may be suitable for use in films, such as +A optical films, and/or +C optical films. Optical films prepared employing such cellulose esters have a variety of commercial applications, such as, for example, as compensation films in liquid crystal displays and/or waveplates in creating circular polarized light used in 3-D technology.

The present invention relates generally to the field of laminated packaging. In particular, the present invention relates to laminated flexible packaging comprising aluminium and a plastic sealant layer only on one side of the aluminium. One embodiment of the present invention relates to a laminated flexible packaging made at least in part from a laminated flexible packaging material comprising an aluminium foil layer, a plastic sealant layer and a coating, wherein the aluminium foil layer is laminated to the plastic sealant layer on the side facing the packaged product, the other side of the aluminium foil layer is coated with the coating but not laminated to a layer of plastic or paper, and wherein the laminated flexible packaging is manufactured from the laminated flexible packaging material on a horizontal form fill and seal (HFFS) machine.

A recyclable flexible laminate for use in a packaging structure, and method of manufacture, comprising a first structure having an inner surface and an outer surface. The first structure comprises machine-direction oriented polyethylene or biaxially oriented polyethylene. The laminate also comprises a second structure having an inner surface and an outer surface, wherein the second structure is machine-direction oriented polyethylene or biaxially oriented polyethylene. The first structure and the second structure are adhesively laminated together using an adhesive.