Provided are a battery-level Ni—Co—Mn mixed solution and a preparation method for a battery-level Mn solution, the steps thereof comprising: acid dissolution (S1), alkalization to remove impurities (S2), synchronous precipitation of calcium, magnesium, and lithium (S3), deep ageing to remove impurities (S4), synergistic extraction (S5), and refining extraction (S6). The steps of deep ageing to remove impurities (S4) and synergistic extraction (S5) comprise: performing deep ageing on a filtrate obtained from the step of synchronous precipitation of calcium, magnesium, and lithium (S3), and after performing filtration to remove impurities, obtaining an aged filtrate; using P204 to extract the aged filtrate and obtain a loaded organic phase, and subjecting the loaded organic phase to staged back-extraction to obtain the battery-level Ni—Co—Mn mixed solution and a Mn-containing solution. By means of the cooperation between the multiple process steps of synchronous precipitation of calcium, magnesium, and lithium (S3), deep ageing to remove impurities (S4), and synergistic extraction (S5), the impurity content of the obtained battery-level Ni—Co—Mn mixed solution is significantly lowered, and the battery-level Ni—Co—Mn mixed solution can be directly used to prepare a lithium battery ternary precursor material. At the same time, the battery-level Mn solution can also be obtained, which is favorable for large-scale applications of the process and increasing economic benefits.

Provided are a battery-level Ni—Co—Mn mixed solution and a preparation method for a battery-level Mn solution, the steps thereof comprising: acid dissolution (S1), alkalization to remove impurities (S2), synchronous precipitation of calcium, magnesium, and lithium (S3), deep ageing to remove impurities (S4), synergistic extraction (S5), and refining extraction (S6).

The steps of deep ageing to remove impurities (S4) and synergistic extraction (S5) comprise: performing deep ageing on a filtrate obtained from the step of synchronous precipitation of calcium, magnesium, and lithium (S3), and after performing filtration to remove impurities, obtaining an aged filtrate; using P204 to extract the aged filtrate and obtain a loaded organic phase, and subjecting the loaded organic phase to staged back-extraction to obtain the battery-level Ni—Co—Mn mixed solution and a Mn-containing solution. By means of the cooperation between the multiple process steps of synchronous precipitation of calcium, magnesium, and lithium (S3), deep ageing to remove impurities (S4), and synergistic extraction (S5), the impurity content of the obtained battery-level Ni—Co—Mn mixed solution is significantly lowered, and the battery-level Ni—Co—Mn mixed solution can be directly used to prepare a lithium battery ternary precursor material. At the same time, the battery-level Mn solution can also be obtained, which is favorable for large-scale applications of the process and increasing economic benefits.

A method for producing a mixed metal solution containing manganese ions and at least one of cobalt ions and nickel ions, the method including: an Al removal step of subjecting an acidic solution containing at least manganese ions and aluminum ions, and at least one of cobalt ions and nickel ions, to removal of the aluminum ions by extracting the aluminum ions into a solvent while leaving at least a part of the manganese ions in the acidic solution in an aqueous phase, the acidic solution being obtained by subjecting battery powder of lithium ion batteries to a leaching step; and a metal extraction step of bringing an extracted residual liquid obtained in the Al removal step to an equilibrium pH of 6.5 to 7.5 using a solvent containing a carboxylic acid-based extracting agent, extracting at least one of the manganese ions and at least one of the cobalt ions and the nickel ions into the solvent, and then back-extracting the manganese ions and at least one of the cobalt ions and nickel ions.

Provided is a method for separating impurities and cobalt without using an electrolysis process from a cobalt chloride solution containing impurities and producing a high purity cobalt sulfate. The production method includes: a first solvent extraction step (S1) of bringing an organic solvent containing an alkyl phosphoric acid-based extractant into contact with a cobalt chloride solution containing impurities, and extracting zinc, manganese, and calcium into the organic solvent to separate to remove zinc, manganese, and calcium; a copper removal step (S2) of adding a sulfurizing agent to a cobalt chloride solution and generating a precipitate of sulfide of copper to separate to remove copper; a second solvent extraction step (S3) of bringing an organic solvent containing a carboxylic acid-based extractant into contact with a cobalt chloride solution and back extracting cobalt with sulfuric acid after extracting cobalt into the organic solvent to obtain cobalt sulfate solution; and a crystallization step (S4) of the cobalt sulfate solution obtained after having undergone through the second solvent extraction step (S3). These steps are sequentially executed. Without using an electrolysis process, a high purity cobalt sulfate is directly produced by separating cobalt and impurities containing manganese.

Provided is a method for inhibiting extractant degradation in the DSX process through the metal extraction control, the method comprising steps of: (a) adding limestone to a copper solvent extraction-raffinate to precipitate iron (Fe) and aluminum (Al) as a slurry, recovering a clarifying liquid; and (b) adding sulfuric acid to the recovered clarifying liquid to adjust the pH thereof.

The invention relates to sulfonated aminomethylated chelate resins, to a method for producing same, to the use thereof for obtaining and purifying metals, in particular rare earth metals, from aqueous solutions and organic liquids, and for producing highly pure silicon.

A method for processing positive electrode active material waste of lithium ion secondary batteries, the waste containing cobalt, nickel, manganese and lithium, the method including: a carbon mixing step of mixing the positive electrode active material waste in the form of powder with carbon to obtain a mixture having a ratio of a mass of carbon to a total mass of the positive electrode active material waste and the carbon of from 10% to 30%; a roasting step of roasting the mixture at a temperature of from 600° C. to 800° C. to obtain roasted powder; a dissolution step including a first dissolution process of dissolving lithium in the roasted powder in water or a lithium-containing solution, and a second dissolution process of dissolving the lithium in a residue obtained in the first dissolution process in water; and an acid leaching step of leaching a residue obtained in the lithium dissolution step with an acid.

Provided is a method for inhibiting extractant degradation in the DSX process through the manganese extraction control, the method comprising: (a) stirring DSX solvent and DSX feed solution, which is a solution containing a valuable metal from which iron has been removed in an agitator, in which soda ash (Na.sub.2CO.sub.3) is further added to maintain a constant pH; and (b) scrubbing the manganese from the DSX solvent, extracted in step (a).

A method of manufacturing a cobalt-nickel-containing solution including: preparing a crude nickel hydroxide and/or a crude cobalt hydroxide as a starting material, the crude nickel or cobalt hydroxide containing cobalt and nickel and elements except the cobalt and nickel as impurities, the crude nickel hydroxide containing the nickel more than the cobalt, and the crude cobalt hydroxide containing the cobalt more than the nickel; a water-washing process for obtaining a post-water-washing crude hydroxide from the starting material; a leaching process for obtaining a post-leaching solution from the post-water-washing crude hydroxide; a neutralization process of subjecting the post-leaching solution to neutralization and solid-liquid-separation to remove the impurities as a post-neutralization residue containing one or more of iron, silicon, aluminum, and chromium, thereby obtaining a post-neutralization solution; and an extraction process of subjecting the post-neutralization solution to solvent extraction to obtain a post-extraction solution containing cobalt and nickel with the impurities reduced.

Producing Co.sub.xFe.sub.100-x, where x is an integer from 20 to 95, nanoparticles by: (a) providing a first aqueous hydroxide solution; (b) preparing a second aqueous solution containing iron ions and cobalt ions; and (c) depositing measured volumes of the second aqueous solution into the first aqueous solution whereby coprecipitation yields CoFe alloy nanoparticles, wherein step (c) occurs in an essentially oxygen-free environment. The nanoparticles are annealed at ambient temperatures to yield soft nanoparticles with targeted particle size, saturation magnetization and coercivity. The chemical composition, crystal structure and homogeneity are controlled at the atomic level. The CoFe magnetic nanoparticles have M.sub.s of 200-235 emu/g, (H.sub.c) coercivity of 18 to 36 O.sub.e and size range of 5-40 nm. The high magnetic moment CoFe nanoparticles can be employed in drug delivery, superior contrast agents for highly sensitive magnetic resonance imaging, magnetic immunoassay, magnetic labeling, waste water treatment, and magnetic separation.