A modified metal oxide particle material includes: a metal oxide particle material having, on a surface thereof, a functional group other than a phenyl group; and a modifying material formed of a silicon-containing compound having a phenyl group. The modifying material is adhered to the surface of the metal oxide particle material. When the modified metal oxide particle material is washed with methyl ethyl ketone, a ratio (C/H) of a carbon content C (% by mass) to a surface area H (m.sup.2) per 1 g is 0.05 or less, after the washing. The ratio (C/H) is reduced by 0.1 or more, and the modifying material is removed by 50% or more by mass, after the washing compared with before the washing.

An annealing separator composition for a grain-oriented electrical steel sheet according to an exemplary embodiment of the present invention contains a composite metal oxide containing Mg and a metal M, wherein the metal M is one or more of Be, Ca, Ba, Sr, Sn, Mn, Fe, Co, Ni, Cu, and Zn.

Electromagnetic Electromagnetic wave absorbing particles including cesium tungsten oxide represented by a general formula Cs.sub.xW.sub.1-yO.sub.3-z (0.2≤x≤0.4, 0<y≤0.4, and 0<z≤0.46) and having an orthorhombic crystal structure or a hexagonal crystal structure are provided.

The disclosed method and related systems and devices relate to producing a pigment from microbial biomass. The pigment may be an engineered black pigment. The method may include a thermal processing step where the microbial biomass is charred. The biomass in the charred and pre-charred state can be washed chemically and/or mechanically. In another step the biomass is ground via a grinding of milling process. The grinding/milling may occur at any various points in the process. In some embodiments the biomass has a particle size between 0.01 and 100 microns.

The present invention relates to cerium-based particles and their use as a component of a composition for polishing. The present invention also relates to the method of preparation of the cerium-based particles.

Disclosed is a method for manufacturing a photocatalytic filter for air purification. The present manufacturing method comprises the steps of: oxidizing a titanium metal to obtain a nanostructured titanium dioxide (TiO2); adding the nanostructured titanium dioxide to an acidic fluorine-containing solution to allow a reaction to occur therebetween for a predetermined period of time; and, after treatment in the acidic fluorine-containing solution, performing heat treatment on the nanostructured titanium dioxide.

According to the invention there is provided an electrothermic composition comprising: a carbon component; a graphite component having a crystallinity of 99.9% and wherein the graphite is heat treated at a temperature of 2500° C. to 3000° C., and a binder, whereby the composition has a thermal coefficient of electrical resistance (TCR) of ±0.0001 to 0.0010 per ° C. over a temperature range of from about 20° C. to 60° C. in an airborne environment, wherein the ratio of the first conductive component and the second resistor component is selected between 10:1 to 1:10.

A reactor for nanoparticle production comprising a main chamber including a first nozzle to which raw material gas is supplied, a lens housing connected to the main chamber in a fluidly movable manner and including a second nozzle for supplying flushing gas to the lens housing, a lens mounted on the lens housing, a light source for irradiating a laser, which passes through the lens to reach the raw material gas in the main chamber, and a hood for discharging nanoparticles generated in the main chamber. A cross-sectional area of at least a part of the lens housing decreases along a direction facing the main chamber.

A submicron sized Si based powder having an average primary particle size between 20 nm and 200 nm, wherein the powder has a surface layer comprising SiO.sub.x, with 0<x<2, the surface layer having an average thickness between 0.5 nm and 10 nm, and wherein the powder has a total oxygen content equal or less than 3% by weight at room temperature. The method for making the powder comprises a step where a Si precursor is vaporized in a gas stream at high temperature, after which the gas stream is quenched to obtain Si particles, and the Si particles are quenched at low temperature in an oxygen containing gas.

Provided are semiconductor particles including a Group 12-16 semiconductor including a Group 12 element and a Group 16 element, a Group 13-15 semiconductor including a Group 13 element and a Group 15 element, or a Group 14 semiconductor including a Group 14 element, the semiconductor particles having a plasma frequency of 1.7×10.sup.14 rad/s to 4.7×10.sup.14 rad/s and a maximum length of 1 nm to 2,000 nm; and a dispersion, a film, an optical filter, a building member, or a radiant cooling device, in all of which the semiconductor particles are used.