A glass/quartz composite structure comprises quartz grit, quartz powder and glass grit wherein the glass grit is in an amount greater than any other single material by weight of the composite structure (e.g. a combined weight of the quartz grit, quartz powder, glass grit, resin, and coupling agent). Natural stone components, which may include the quartz grit and quartz powder, may be in an amount greater than 30% by weight of the composite structure. The structure may be formed into a 1.2-1.5 cm thick slab for countertops using standard cabinet perimeter support. The slab may be made by mixing the quartz grit, quartz powder, glass grit, and binding resin, pouring the mixture in a mold, and compacting the mixture in the mold. Specific natural mineral components, decorative chips, and/or wet mixture pieces may be added to the composite structure to provide aesthetics of specific natural stones.

A glass/quartz composite structure comprises quartz grit, quartz powder and glass grit wherein the glass grit is in an amount greater than any other single material by weight of the composite structure (e.g. a combined weight of the quartz grit, quartz powder, glass grit, resin, and coupling agent). Natural stone components, which may include the quartz grit and quartz powder, may be in an amount greater than 30% by weight of the composite structure. The structure may be formed into a 1.2-1.5 cm thick slab for countertops using standard cabinet perimeter support. The slab may be made by mixing the quartz grit, quartz powder, glass grit, and binding resin, pouring the mixture in a mold, and compacting the mixture in the mold. Specific natural mineral components, decorative chips, and/or wet mixture pieces may be added to the composite structure to provide aesthetics of specific natural stones.

A quartz container manufacturing method and a forming apparatus, relating to the solar photovoltaic technical field, and providing a mold comprising a top cylinder and a mold bottom; during formation of a container blank, when the mold forms a first included angle with a horizontal plane and the mold is rotated at a first rotation speed, the source material forms a first blank on the inner wall of the top cylinder; when the mold forms a second included angle with the horizontal plane and the mold is rotated at a second rotation speed, the source material forms a second blank on the inner wall of the mold bottom; a quartz container is manufactured from a container blank composed of the first blank and the second blank.

The present disclosure provides a cellular foam composition, a method for producing and using the same. One particular aspect of the disclosure provides a cellular foam composition comprising a plurality of foam layers, where each foam layer is made from a hollow microstructure material. In particular, the density of the hollow microstructure material in each foam layer is different from the density of the hollow microstructure material that forms the adjacent foam layer. In some embodiments, cellular foam compositions of the disclosure further include an interfacial layer comprising interfacial voids in between adjacent layers.

The present disclosure provides a cellular foam composition, a method for producing and using the same. One particular aspect of the disclosure provides a cellular foam composition comprising a plurality of foam layers, where each foam layer is made from a hollow microstructure material. In particular, the density of the hollow microstructure material in each foam layer is different from the density of the hollow microstructure material that forms the adjacent foam layer. In some embodiments, cellular foam compositions of the disclosure further include an interfacial layer comprising interfacial voids in between adjacent layers.

In an exemplary embodiment, a quartz glass crucible 1 includes: a cylindrical crucible body 10 which has a bottom and is made of quartz glass; and crystallization-accelerator-containing coating films 13A and 13B which are formed on surfaces of the crucible body 10 so as to cause crystallization-accelerator-enriched layers to be formed in the vicinity of the surfaces of the crucible body 10 by heating during a step of pulling up a silicon single crystal by a Czochralski method. The quartz glass crucible is capable of withstanding a single crystal pull-up step undertaken for a very long period of time, such as multi-pulling, and a manufacturing method thereof.

A quartz glass crucible including bottom, curved, and straight body portions, where the quartz glass crucible includes an outer layer including opaque quartz glass containing bubbles, and an inner layer including transparent quartz glass, the outer layer fabricated from different types of raw material powder, the outer layer having regions sectioned by bubble content densities, and bubble content densities of two outer layer adjacent regions, when d.sub.a (pcs/mm.sup.3) is defined as content density of a region “a” having a greater content density, and d.sub.b (pcs/mm.sup.3) is defined as content density of a region “b” having a smaller content density, a difference D=(d.sub.a−d.sub.b)/d.sub.b between content densities of the two regions is 10% or more.

A wavelength conversion element converts excitation light to light with a different wavelength. The wavelength conversion element includes a substrate including an upper surface, and a wavelength converter on the upper surface of the substrate. The wavelength converter includes a phosphor including a plurality of phosphor particles, molten glass in contact with the plurality of phosphor particles and binding the plurality of phosphor particles to one another, and voids at least between the plurality of phosphor particles, in the molten glass, or between the plurality of phosphor particles and the molten glass. A maximum area of areas of the voids is less than a maximum area of areas of the plurality of phosphor particles in a cross-sectional view of the wavelength converter.

A wavelength conversion element converts excitation light to light with a different wavelength. The wavelength conversion element includes a substrate including an upper surface, and a wavelength converter on the upper surface of the substrate. The wavelength converter includes a phosphor including a plurality of phosphor particles, molten glass in contact with the plurality of phosphor particles and binding the plurality of phosphor particles to one another, and voids at least between the plurality of phosphor particles, in the molten glass, or between the plurality of phosphor particles and the molten glass. A maximum area of areas of the voids is less than a maximum area of areas of the plurality of phosphor particles in a cross-sectional view of the wavelength converter.

A method for producing a solar crucible includes providing a crucible base body of transparent or opaque fused silica having an inner wall, providing a dispersion containing amorphous SiO.sub.2 particles, applying a SiO.sub.2-containing slip layer to at least a part of the inner wall by using the dispersion, drying the slip layer to form a SiO.sub.2-containing grain layer and thermally densifying the SiO.sub.2-containing grain layer to form a diffusion barrier layer. The dispersion contains a dispersion liquid and amorphous SiO.sub.2 particles that form a coarse fraction and a fine fraction with SiO.sub.2 nanoparticles. The weight percentage of the SiO.sub.2 nanoparticles based on the solids content of the dispersion is in the range between 2 and 15% by weight. The SiO.sub.2-containing grain layer is thermally densified into the diffusion barrier layer through the heating up of the silicon in the crystal growing process.