The invention discloses high-strength glass-ceramic-based lightweight aggregates and the preparation method thereof. The mass ratio of raw material components is 50-70 parts of engineering muck, 20-40 parts of glass, 3-7 parts of calcium carbonate, 3-7 parts of magnesium oxide, and 2-10 parts of a nucleating agent; the nucleating agent is at least one of calcium fluoride, titanium dioxide, and chromium oxide. After crushing, mixing, and granulating, spherical particles with a particle size of 10-12 mm are formed; and then the product can be obtained after drying, sintering, and cooling. The obtained lightweight aggregate from the invention has a diopside matrix which provides high strength and a low water absorption rate at low densities. Moreover, waste glass and engineering muck could be utilized with high value.

The invention discloses high-strength glass-ceramic-based lightweight aggregates and the preparation method thereof. The mass ratio of raw material components is 50-70 parts of engineering muck, 20-40 parts of glass, 3-7 parts of calcium carbonate, 3-7 parts of magnesium oxide, and 2-10 parts of a nucleating agent; the nucleating agent is at least one of calcium fluoride, titanium dioxide, and chromium oxide. After crushing, mixing, and granulating, spherical particles with a particle size of 10-12 mm are formed; and then the product can be obtained after drying, sintering, and cooling. The obtained lightweight aggregate from the invention has a diopside matrix which provides high strength and a low water absorption rate at low densities. Moreover, waste glass and engineering muck could be utilized with high value.

The present invention relates generally to silicate-based coatings and to methods to make and apply same. In one embodiment, the silicate-coatings of the present invention are formed from a two part mixture of phosphate-based component and a glass-based component. In another embodiment, the silicate-based coatings of the present invention are free from any organic materials.

The present invention relates generally to silicate-based coatings and to methods to make and apply same. In one embodiment, the silicate-coatings of the present invention are formed from a two part mixture of phosphate-based component and a glass-based component. In another embodiment, the silicate-based coatings of the present invention are free from any organic materials.

A process for the preparation of multi-coloured dental restorations is described, in which glasses and glass ceramics with various compositions are given the shapes of dental restorations and colour changes are effected in the glasses and glass ceramics by irradiating them with artificial electromagnetic radiation and subjecting them to a heat treatment.

A process for the preparation of multi-coloured dental restorations is described, in which glasses and glass ceramics with various compositions are given the shapes of dental restorations and colour changes are effected in the glasses and glass ceramics by irradiating them with artificial electromagnetic radiation and subjecting them to a heat treatment.

Coated glass or glass ceramic substrates having high temperature resistance, high strength, and a low coefficient of thermal expansion. The coating includes pores, is fluid-tight and suitable for coating a temperature-resistant, high-strength glass or glass ceramic substrate with a low coefficient of thermal expansion, and to a method for producing such a coated substrate.

Coated glass or glass ceramic substrates having high temperature resistance, high strength, and a low coefficient of thermal expansion. The coating includes pores, is fluid-tight and suitable for coating a temperature-resistant, high-strength glass or glass ceramic substrate with a low coefficient of thermal expansion, and to a method for producing such a coated substrate.

A thermally tempered aluminosilicate glass-ceramic composition includes a crystalline phase and a residual glass phase, wherein the two phases form a system wherein the thermal expansion curve of the system has two distinct sections diverging from an inflection point temperature in the range of about 450° C. to about 600° C., and wherein the difference between coefficient of thermal expansion of the glass-ceramic below and above the inflection point is greater than about 4 ppm/° C.

A thermally tempered aluminosilicate glass-ceramic composition includes a crystalline phase and a residual glass phase, wherein the two phases form a system wherein the thermal expansion curve of the system has two distinct sections diverging from an inflection point temperature in the range of about 450° C. to about 600° C., and wherein the difference between coefficient of thermal expansion of the glass-ceramic below and above the inflection point is greater than about 4 ppm/° C.