A method of modifying glass frit involves treating the frit with a grain-boundary-healing compound. The method increases transmission and clarity, and reduces haze of a fired enamel coating made from such modified glass frit as compared to a coating not made from such modified glass frit. The grain-boundary-healing compound influences the chemistry at the grain boundaries to prevent haze. The compound burns out to yield a fluxing material that dissolves alkaline carbonates or bicarbonates on the surface of the glass frit. The dissolved species are incorporated into the enamel coating, thereby promoting the fusion of the glass frit and reducing the amount of haze in the enamel coating. The additives also function to prevent the formation of seed crystals on the surface of the glass frit that may inhibit the fusion of the glass frit.

A method of modifying glass frit involves treating the frit with a grain-boundary-healing compound. The method increases transmission and clarity, and reduces haze of a fired enamel coating made from such modified glass frit as compared to a coating not made from such modified glass frit. The grain-boundary-healing compound influences the chemistry at the grain boundaries to prevent haze. The compound burns out to yield a fluxing material that dissolves alkaline carbonates or bicarbonates on the surface of the glass frit. The dissolved species are incorporated into the enamel coating, thereby promoting the fusion of the glass frit and reducing the amount of haze in the enamel coating. The additives also function to prevent the formation of seed crystals on the surface of the glass frit that may inhibit the fusion of the glass frit.

The present invention relates to a particle mixture comprising particles of glass frit and particles of a crystalline oxide material, wherein the glass frit comprises silicon oxide (SiO.sub.2), zinc oxide (ZnO) and sulfur (S) and wherein the D90 particle size of the particle mixture is less than 5 microns. The particle mixture may be used to apply an enamel to a substrate. The present invention further relates to the use of the particle mixture to form an enamel on a substrate, to a glass sheet and to an automotive window pane.

The present invention relates to a particle mixture comprising particles of glass frit and particles of a crystalline oxide material, wherein the glass frit comprises silicon oxide (SiO.sub.2), zinc oxide (ZnO) and sulfur (S) and wherein the D90 particle size of the particle mixture is less than 5 microns. The particle mixture may be used to apply an enamel to a substrate. The present invention further relates to the use of the particle mixture to form an enamel on a substrate, to a glass sheet and to an automotive window pane.

The present disclosure discloses a low LOI tellurium-lithium-silicon-zirconium frit system and a conductive paste and application thereof, and belongs to the field of conductive paste. In the low LOI tellurium-lithium-silicon-zirconium frit system, components of the frit are 24%-40% TeO.sub.2, 18%-24% Li.sub.2O, 4%-13% SiO.sub.2, 0-2% ZrO.sub.2, and a balance MO.sub.x, and M is one or a mixture of Na, K, Mg, Ca, Sr, Ti, V, Cr, Mo, W, Mn, Cu, Ag, Zn, Cd, B, Al, Ga, Tl, Ge, Pb, P, and Bi. There is no need to add additional surfactants, a viscosity change of the conductive paste prepared after standing for 30 days is less than 20%, the conductive paste has good stability, the water related weight loss of inorganic oxide of the conductive paste is less than 1.6%, and the application performance of the conductive paste is not affected after standing for 30 days.

The present disclosure discloses a low LOI tellurium-lithium-silicon-zirconium frit system and a conductive paste and application thereof, and belongs to the field of conductive paste. In the low LOI tellurium-lithium-silicon-zirconium frit system, components of the frit are 24%-40% TeO.sub.2, 18%-24% Li.sub.2O, 4%-13% SiO.sub.2, 0-2% ZrO.sub.2, and a balance MO.sub.x, and M is one or a mixture of Na, K, Mg, Ca, Sr, Ti, V, Cr, Mo, W, Mn, Cu, Ag, Zn, Cd, B, Al, Ga, Tl, Ge, Pb, P, and Bi. There is no need to add additional surfactants, a viscosity change of the conductive paste prepared after standing for 30 days is less than 20%, the conductive paste has good stability, the water related weight loss of inorganic oxide of the conductive paste is less than 1.6%, and the application performance of the conductive paste is not affected after standing for 30 days.

The invention provides a glazing comprising first glass sheet comprising a printed layer on a portion of a surface of the glass sheet and a conductive coating on the surface of the first glass sheet. The conductive coating extends over at least a portion of the printed layer to form a coated print portion and extends over a portion of the surface of the glass sheet to form a coated glass portion. The coated print portion has a Developed Interfacial Area Ratio Sdr less than 27.45%. A method for producing the glazing and use of the glazing in a vehicle is also disclosed.

The invention provides a glazing comprising first glass sheet comprising a printed layer on a portion of a surface of the glass sheet and a conductive coating on the surface of the first glass sheet. The conductive coating extends over at least a portion of the printed layer to form a coated print portion and extends over a portion of the surface of the glass sheet to form a coated glass portion. The coated print portion has a Developed Interfacial Area Ratio Sdr less than 27.45%. A method for producing the glazing and use of the glazing in a vehicle is also disclosed.

An antiskid and wear-resistant glaze, an antiskid, wear-resistant and easy-to-clean ceramic tile and a preparation method thereof, relating to the technical field of building ceramics, are provided. This antiskid and wear-resistant glaze is prepared by antiskid and wear-resistant particles, a printing paste and sodium tripolyphosphate. This antiskid, wear-resistant and easy-to-clean ceramic tile comprises, from the bottom up, a green body layer, an overglaze layer, a decoration layer, an antiskid and wear-resistant layer and an easy-to-clean protection layer provided in turn, wherein the antiskid and wear-resistant layer is mainly prepared by antiskid and wear-resistant particles, and the easy-to-clean protection layer is mainly prepared by easy-to-clean protection particles.

An antiskid and wear-resistant glaze, an antiskid, wear-resistant and easy-to-clean ceramic tile and a preparation method thereof, relating to the technical field of building ceramics, are provided. This antiskid and wear-resistant glaze is prepared by antiskid and wear-resistant particles, a printing paste and sodium tripolyphosphate. This antiskid, wear-resistant and easy-to-clean ceramic tile comprises, from the bottom up, a green body layer, an overglaze layer, a decoration layer, an antiskid and wear-resistant layer and an easy-to-clean protection layer provided in turn, wherein the antiskid and wear-resistant layer is mainly prepared by antiskid and wear-resistant particles, and the easy-to-clean protection layer is mainly prepared by easy-to-clean protection particles.