An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

A low-density, high-strength concrete composition that is lightweight and self-compacting or non-self-compacting, with a low weight-fraction of aggregate to total dry raw materials, and a highly-homogenous distribution of a non-absorptive and closed-cell lightweight aggregate such as glass microspheres or copolymer polymer beads or a combination thereof, and the steps of providing the composition or components. Lightweight concretes formed therefrom have low density, high strength-to-weight ratios, and high R-value. The concrete has strength similar to that ordinarily found in structural lightweight concrete but at a lower density, such as an oven-dried density as low as 40 lbs./cu.ft. Such strength-to-density ratios range approximately from above 30 cu.ft/sq.in. to above 110 cu.ft/sq.in., with a 28-day compressive strength ranging from about 3400 to 8000 psi.

A low-density, high-strength concrete composition that is lightweight and self-compacting or non-self-compacting, with a low weight-fraction of aggregate to total dry raw materials, and a highly-homogenous distribution of a non-absorptive and closed-cell lightweight aggregate such as glass microspheres or copolymer polymer beads or a combination thereof, and the steps of providing the composition or components. Lightweight concretes formed therefrom have low density, high strength-to-weight ratios, and high R-value. The concrete has strength similar to that ordinarily found in structural lightweight concrete but at a lower density, such as an oven-dried density as low as 40 lbs./cu.ft. Such strength-to-density ratios range approximately from above 30 cu.ft/sq.in. to above 110 cu.ft/sq.in., with a 28-day compressive strength ranging from about 3400 to 8000 psi.

A fire-resistant gypsum panel comprises: a gypsum core layer comprising set gypsum and a high temperature sag-resistant material including mineral wool in an amount between 0.2% and 3.0% by weight of gypsum.

A fire-resistant gypsum panel comprises: a gypsum core layer comprising set gypsum and a high temperature sag-resistant material including mineral wool in an amount between 0.2% and 3.0% by weight of gypsum.

The present invention discloses inorganic pelletized perlitic lightweight granules and a preparation process and use thereof. The present invention develops through encapsulation technology a novel type of lightweight particles, namely, inorganic pelletized perlitic lightweight granules comprising expanded perlite as a core material and a cementitious material as a shell material, forming a core-shell structure in which a perlite core is encapsulated in a cementitious shell. The cementitious material including cement and fly ash is coated onto the surface of expanded perlite particles through an encapsulation process by a pelletizer under controlled water spraying. The resulting inorganic pelletized perlitic lightweight granules are lower in cost and easier to produce, and have better fire resistance, higher crushing strength, and better compatibility with concrete. The inorganic pelletized perlitic lightweight granules can overcome the problems of conventional lightweight concrete, such as high water absorption and inconsistent performance.

Disclosed are an organic binder-based coating; a composite gypsum board containing face and back cover sheets, an outside surface of the back cover sheet bearing the coating; and a method of preparing composite board where the back cover sheet contains the coating on its outer surface. The coating is formed from a composition comprising an alkaline silicate, a solid filler, and optionally, a borate. An enhancing layer can also be applied to the back cover sheet.

Disclosed are an organic binder-based coating; a composite gypsum board containing face and back cover sheets, an outside surface of the back cover sheet bearing the coating; and a method of preparing composite board where the back cover sheet contains the coating on its outer surface. The coating is formed from a composition comprising an alkaline silicate, a solid filler, and optionally, a borate. An enhancing layer can also be applied to the back cover sheet.