Cement-SCM blends employ particle packing principles to increase particle packing density and reduce interstitial spacing between the cement and SCM particles. Particle packing reduces the amount of water required to obtain a cement paste having a desired flow, lowers the water-cementitious material ratio (w/cm), and increases early and long-term strengths. This may be accomplished by providing a hydraulic cement fraction having a narrow PSD and at least one SCM fraction having a mean particle size that differs from the mean particle size of the narrow PSD cement by a multiple of 3.0 or more to yield a cement-SCM blend having a particle packing density of at least 57.0%.

Cement-SCM blends employ particle packing principles to increase particle packing density and reduce interstitial spacing between the cement and SCM particles. Particle packing reduces the amount of water required to obtain a cement paste having a desired flow, lowers the water-cementitious material ratio (w/cm), and increases early and long-term strengths. This may be accomplished by providing a hydraulic cement fraction having a narrow PSD and at least one SCM fraction having a mean particle size that differs from the mean particle size of the narrow PSD cement by a multiple of 3.0 or more to yield a cement-SCM blend having a particle packing density of at least 57.0%.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from ⅛.sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

The present invention relates to the field of foam formation and stabilization, particularly foamed construction materials, such as cement. Disclosed are additives suitable to obtain mineral foams when added to the corresponding starting materials. The invention provides a ready-to-use product in the form of a solid particulate composition comprising hydrophobized particles (1) and catalytically active particles (2) as defined in claim 1. The invention further provides for manufacturing methods of such ready-to-use product.

The present invention relates to the field of foam formation and stabilization, particularly foamed construction materials, such as cement. Disclosed are additives suitable to obtain mineral foams when added to the corresponding starting materials. The invention provides a ready-to-use product in the form of a solid particulate composition comprising hydrophobized particles (1) and catalytically active particles (2) as defined in claim 1. The invention further provides for manufacturing methods of such ready-to-use product.

A low-density, high-strength concrete composition that is lightweight and self-compacting or non-self-compacting, with a low weight-fraction of aggregate to total dry raw materials, and a highly-homogenous distribution of a non-absorptive and closed-cell lightweight aggregate such as glass microspheres or copolymer polymer beads or a combination thereof, and the steps of providing the composition or components. Lightweight concretes formed therefrom have low density, high strength-to-weight ratios, and high R-value. The concrete has strength similar to that ordinarily found in structural lightweight concrete but at a lower density, such as an oven-dried density as low as 40 lbs./cu.ft. Such strength-to-density ratios range approximately from above 30 cu.ft/sq.in. to above 110 cu.ft/sq.in., with a 28-day compressive strength ranging from about 3400 to 8000 psi.

A low-density, high-strength concrete composition that is lightweight and self-compacting or non-self-compacting, with a low weight-fraction of aggregate to total dry raw materials, and a highly-homogenous distribution of a non-absorptive and closed-cell lightweight aggregate such as glass microspheres or copolymer polymer beads or a combination thereof, and the steps of providing the composition or components. Lightweight concretes formed therefrom have low density, high strength-to-weight ratios, and high R-value. The concrete has strength similar to that ordinarily found in structural lightweight concrete but at a lower density, such as an oven-dried density as low as 40 lbs./cu.ft. Such strength-to-density ratios range approximately from above 30 cu.ft/sq.in. to above 110 cu.ft/sq.in., with a 28-day compressive strength ranging from about 3400 to 8000 psi.

The present invention refers to a mineral matter powder preparation by wet process without acrylic additive or other grinding aid additives and to the use of said mineral matter after an optional hydrophobic treatment. Said mineral material having superior dispersing properties.