The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

Disclosed is a method for preparing an uncalcined geopolymer-based refractory material. The method includes the steps of mixing a mineral powder, a fly ash, a metakaolin, and silicon carbide whiskers by ball milling to form a milled material; mixing the milled material with a sodium water glass solution and water to form a slurry; and curing the slurry to obtain the uncalcined geopolymer-based refractory material. The uncalcined geopolymer-based refractory material thus prepared contains a geopolymer matrix formed of the mineral powder, the fly ash, and the metakaolin and the silicon carbide whiskers embedded in the geopolymer matrix.

An uncalcined geopolymer-based refractory material is provided, comprising a matrix of a geopolymer obtainable by polymerization of a mixture consisting of mineral powder, fly ash, and metakaolin; and SiC whiskers embedded in the geopolymer matrix. The material has excellent mechanical properties and high resistance to high temperatures and exhibits a ductile fracture mechanism instead of a brittle fracture mechanism.

An uncalcined geopolymer-based refractory material is provided, comprising a matrix of a geopolymer obtainable by polymerization of a mixture consisting of mineral powder, fly ash, and metakaolin; and SiC whiskers embedded in the geopolymer matrix. The material has excellent mechanical properties and high resistance to high temperatures and exhibits a ductile fracture mechanism instead of a brittle fracture mechanism.

In one aspect, the disclosed examples relate to a curable casting compound for producing plastics moulded parts. For example, the curable casting compound may include a binder component on the basis of a polymerisable monomer and a proportion of approximately 40% to approximately 85% by weight of one or more inorganic fillers. In one example, the casting compound includes an aluminosilicate as one of the inorganic fillers. Other examples are provided.

Disclosed is a method for preparing an uncalcined geopolymer-based refractory material. The method includes the steps of mixing a mineral powder, a fly ash, a metakaolin, and silicon carbide whiskers by ball milling to form a milled material; mixing the milled material with a sodium water glass solution and water to form a slurry; and curing the slurry to obtain the uncalcined geopolymer-based refractory material. The uncalcined geopolymer-based refractory material thus prepared contains a geopolymer matrix formed of the mineral powder, the fly ash, and the metakaolin and the silicon carbide whiskers embedded in the geopolymer matrix.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350 C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350 C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The present invention discloses a micro-nano composite plugging agent for drilling fluid, a preparation method of the micro-nano composite plugging agent for drilling fluid, a drilling fluid, and an application thereof. The composite plugging agent contains nanometer calcium carbonate, nanometer zinc oxide whiskers, nanometer emulsified paraffin, a flocculating agent, and a lubricant, wherein in the composite plugging agent, the nanometer calcium carbonate is in 10-36 parts by weight, the nanometer zinc oxide whiskers are in 20-40 parts by weight, the nanometer emulsified paraffin is in 30-70 parts by weight, the flocculating agent is in 1-10 parts by weight, and the lubricant is 5-20 parts by weight.