A method for the application of hydrous mineral binder compositions which contain fibres. An aqueous accelerator is mixed with the aqueous binder composition in a mixer shortly before the application. The method is very robust and makes it possible to quickly produce even large moulded bodies having a uniform surface and very good strength development properties.

A method for the application of hydrous mineral binder compositions which contain fibres. An aqueous accelerator is mixed with the aqueous binder composition in a mixer shortly before the application. The method is very robust and makes it possible to quickly produce even large moulded bodies having a uniform surface and very good strength development properties.

To provide a molded body which has high strength, high ductility, and excellent dimensional stability while maintaining incombustibility and fire resistance. A molded body formed from a curable composition containing (A) at least one aluminosilicate source, (B) an alkali metal hydroxide, (C) a calcium ion source, and (D) an alkali resistant fiber, wherein the aluminosilicate source (A) has an SiO.sub.2 content of 50% by mass or more based on a total mass of the aluminosilicate source (A), an amorphous ratio of 50% by mass or higher, and an average particle diameter of 50 μm or smaller, and comprises an aluminosilicate source having an average particle diameter of 10 μm or smaller in an amount of 30% by mass or more based on the total mass of the aluminosilicate source (A).

To provide a molded body which has high strength, high ductility, and excellent dimensional stability while maintaining incombustibility and fire resistance. A molded body formed from a curable composition containing (A) at least one aluminosilicate source, (B) an alkali metal hydroxide, (C) a calcium ion source, and (D) an alkali resistant fiber, wherein the aluminosilicate source (A) has an SiO.sub.2 content of 50% by mass or more based on a total mass of the aluminosilicate source (A), an amorphous ratio of 50% by mass or higher, and an average particle diameter of 50 μm or smaller, and comprises an aluminosilicate source having an average particle diameter of 10 μm or smaller in an amount of 30% by mass or more based on the total mass of the aluminosilicate source (A).

The present invention relates to curable compositions which comprise (meth)acrylic monomers, ethylenically unsaturated oligomers and a specific multistage polymer additive. The additive is used as a processing aid to reduce cure shrinkage and reduce or prevent the formation of cracks during the polymerization of the composition.

The present invention relates to curable compositions which comprise (meth)acrylic monomers, ethylenically unsaturated oligomers and a specific multistage polymer additive. The additive is used as a processing aid to reduce cure shrinkage and reduce or prevent the formation of cracks during the polymerization of the composition.

The present invention relates to additives and, more specifically, the use of biochar, in concrete and other cementitious materials to provide for building materials that have a lower carbon footprint than their traditional counterparts. Traditional methods for production of cement produce large amount of carbon dioxide (CO2). When coupled with the massive demand for cement building materials around the world, this means that the cement production has a significant impact on the amount of CO2 produced globally. By including biochar and other additives along with, or instead of some traditional components of cement, one may be able to provide for cementitious building materials that sequester carbon, rather than release it.

The present invention relates to additives and, more specifically, the use of biochar, in concrete and other cementitious materials to provide for building materials that have a lower carbon footprint than their traditional counterparts. Traditional methods for production of cement produce large amount of carbon dioxide (CO2). When coupled with the massive demand for cement building materials around the world, this means that the cement production has a significant impact on the amount of CO2 produced globally. By including biochar and other additives along with, or instead of some traditional components of cement, one may be able to provide for cementitious building materials that sequester carbon, rather than release it.

Provided are a textile reinforced cement composite for suppressing occurrence of slipping and a crack and a manufacturing method thereof. The textile reinforced cement composite for suppressing occurrence of slipping and a crack can suppress slipping between a textile grid reinforcement and a cement composite by using an angulated filling material mixed therewith when a textile reinforced cement composite having a textile grid reinforcement embedded in a cement composite is manufactured, suppress occurrence of a crack of the cement composite, suppress occurrence of a crack of the cement composite due to a fiber bridging reaction by using organic fiber mixed therewith, induce distribution of fine cracks, suppress degradation of fluidity of the cement composite caused by mixing of the angulated filling material by using a spherical binder and a chemical admixture added thereto, and suppress slipping between the textile grid reinforcement and the cement composite by using a fine powder binder having a predetermined particle size and mixed therewith.

Provided are a textile reinforced cement composite for suppressing occurrence of slipping and a crack and a manufacturing method thereof. The textile reinforced cement composite for suppressing occurrence of slipping and a crack can suppress slipping between a textile grid reinforcement and a cement composite by using an angulated filling material mixed therewith when a textile reinforced cement composite having a textile grid reinforcement embedded in a cement composite is manufactured, suppress occurrence of a crack of the cement composite, suppress occurrence of a crack of the cement composite due to a fiber bridging reaction by using organic fiber mixed therewith, induce distribution of fine cracks, suppress degradation of fluidity of the cement composite caused by mixing of the angulated filling material by using a spherical binder and a chemical admixture added thereto, and suppress slipping between the textile grid reinforcement and the cement composite by using a fine powder binder having a predetermined particle size and mixed therewith.