A method of reducing sulfur concentration in fly ash, flue gas desulfurization (FGD) ash, and mixtures thereof by contacting the fly ash, FGD ash, or mixtures thereof with an aqueous acidic solution, for a time, at a temperature, and at a liquid-to-solid ratio wherein the sulfur concentration within the fly ash, FGD ash, or mixture thereof is reduced to no more than 5 wt % SO.sub.3 based on the total weight of dry fly ash, FGD ash, or mixture thereof so treated.

The present invention relates to method for producing construction aggregate, comprising the steps of: (i) preparing materials, which comprises (% by weight): fly ash (80 to 99.75%); alkaline activator (0.25 to 20%); water (6 to 30% of total weight of fly ash and alkaline activator); (ii) mixing the alkaline activator with all the aforementioned water amount to create alkaline activator solution, after which will be mixed with fly ash to create geopolymer mortar; (iii) molding the geopolymer mortar with the compressive force of 2 MPa and more with desired dimension, wherein the molding is carried out with hydraulic pressing, extrusion, rolling or tablet lamination. (iv) solidifying; and (v) optionally, crushing the construction aggregate obtained above to a predefined dimension. Besides, the present invention relates to the construction aggregate from fly ash obtained by the above mentioned method.

This invention relates to using a unique blend of components of a composite cement and subjecting them to a rotary mill process using variably sized and shaped media to reduce the blends' particle size. The invention is novel in that it mills the blended materials together to achieve reduced particle size, increased particle surface area, higher compressive strength and lower permeability. In one embodiment, the invention combines fly ash or other pozzolan material with a cement of any type at varying rations between 1% and 99%.

This invention relates to using a unique blend of components of a composite cement and subjecting them to a rotary mill process using variably sized and shaped media to reduce the blends' particle size. The invention is novel in that it mills the blended materials together to achieve reduced particle size, increased particle surface area, higher compressive strength and lower permeability. In one embodiment, the invention combines fly ash or other pozzolan material with a cement of any type at varying rations between 1% and 99%.

A method of reducing sulfur concentration in fly ash, flue gas desulfurization (FGD) ash, and mixtures thereof by contacting the fly ash, FGD ash, or mixtures thereof with an aqueous acidic solution, for a time, at a temperature, and at a liquid-to-solid ratio wherein the sulfur concentration within the fly ash, FGD ash, or mixture thereof is reduced to no more than 5 wt % SO.sub.3 based on the total weight of dry fly ash, FGD ash, or mixture thereof so treated.

It has been unexpectedly discovered that the addition of a natural or other pozzolan to non-spec coal ash significantly improves the properties of the non-spec coal ash to the extent it can be certified under ASTM C618 and AASHTO 295, as either a Class F or Class C coal ash. The natural pozzolan may be a volcanic ejecta, such as pumice or perlite. Other pozzolans may also be used for this beneficiation process. Many pozzolans are experimentally tested and may be used to beneficiate non-spec coal ash into certifiable Class F coal ash. Additionally, this disclosure provides a method of converting a Class C coal ash to a more valuable Class F coal ash. This discovery will extend diminishing Class F coal ash supplies and turn non-spec coal ash waste streams into valuable, certified coal ash pozzolan which will protect and enhance concrete, mortars and grouts.

It has been unexpectedly discovered that the addition of a natural or other pozzolan to non-spec fly ash significantly improves the properties of the non-spec fly ash to the extent it can be certified under ASTM C618 and AASHTO 295, as either a Class F or Class C fly ash. The natural pozzolan may be a volcanic ejecta, such as pumice or perlite. Other pozzolans may also be used for this beneficiation process. Many pozzolans are experimentally tested and may be used to beneficiate non-spec fly ash into certifiable Class F fly ash. Additionally, this disclosure provides a method of converting a Class C fly ash to a more valuable Class F fly ash. This discovery will extend diminishing Class F fly ash supplies and turn non-spec fly ash waste streams into valuable, certified fly ash pozzolan which will protect and enhance concrete, mortars and grouts.

It has been unexpectedly discovered that the addition of a natural or other pozzolan to non-spec coal ash significantly improves the properties of the non-spec coal ash to the extent it can be certified under ASTM C618 and AASHTO 295, as either a Class F or Class C coal ash. The natural pozzolan may be a volcanic ejecta, such as pumice or perlite. Other pozzolans may also be used for this beneficiation process. Many pozzolans are experimentally tested and may be used to beneficiate non-spec coal ash into certifiable Class F coal ash. Additionally, this disclosure provides a method of converting a Class C coal ash to a more valuable Class F coal ash. This discovery will extend diminishing Class F coal ash supplies and turn non-spec coal ash waste streams into valuable, certified coal ash pozzolan which will protect and enhance concrete, mortars and grouts.

It has been unexpectedly discovered that the addition of a natural or other pozzolan to non-spec coal ash significantly improves the properties of the non-spec coal ash to the extent it can be certified under ASTM C618 and AASHTO 295, as either a Class F or Class C coal ash. The natural pozzolan may be a volcanic ejecta, such as pumice or perlite. Other pozzolans may also be used for this beneficiation process. Many pozzolans are experimentally tested and may be used to beneficiate non-spec coal ash into certifiable Class F coal ash. Additionally, this disclosure provides a method of converting a Class C coal ash to a more valuable Class F coal ash. This discovery will extend diminishing Class F coal ash supplies and turn non-spec coal ash waste streams into valuable, certified coal ash pozzolan which will protect and enhance concrete, mortars and grouts.

It has been unexpectedly discovered that the addition of a natural or other pozzolan to non-spec fly ash significantly improves the properties of the non-spec fly ash to the extent it can be certified under ASTM C618 and AASHTO 295, as either a Class F or Class C fly ash. The natural pozzolan may be a volcanic ejecta, such as pumice or perlite. Other pozzolans may also be used for this beneficiation process. Many pozzolans are experimentally tested and may be used to beneficiate non-spec fly ash into certifiable Class F fly ash. Additionally, this disclosure provides a method of converting a Class C fly ash to a more valuable Class F fly ash. This discovery will extend diminishing Class F fly ash supplies and turn non-spec fly ash waste streams into valuable, certified fly ash pozzolan which will protect and enhance concrete, mortars and grouts.