A refractory composition including refractory aggregate, one or more matrix components, and silicate-coated set accelerator particles. The silicate-coated set accelerator particles can include one more of silicate-coated calcium hydroxide, magnesium hydroxide, calcium chloride, calcium carbonate, magnesium carbonate and calcium sulfate. Suitable silicate coatings include sodium silicate, potassium silicate, lithium silicate and mixtures thereof. A method of recovering an aged refractory composition, a settable composition and a method of manufacturing silicate-coated calcium hydroxide particles are also provided.

The present invention belongs to the technical field of metallurgical solid waste resource utilization, and particularly relates to acidification and carbonization coupling modified steel slag as well as a preparation process and an application thereof. The process specifically includes the following steps of adopting acetic acid, tributyl phosphate, ethanolamine and a NaOH and Ca(OH).sub.2 emulsion as reaction reinforcing agents, and modifying the steel slag together with CO.sub.2-rich lime kiln flue gas. The process for modifying the steel slag through acidification and carbonization coupling provided in the present invention has the advantages of simple reaction conditions and no need of high-pressure CO.sub.2, additionally, the carbonation reaction rate can be greatly increased, and f-CaO and f-MgO in the steel slag can be effectively eliminated.

Methods of preparing engineered cementitious composite precursors include carbonating a fly ash comprising >about 25% by weight of calcium oxide (CaO) and having a water content of >about 12% to <about 18% by weight of water by exposing the fly ash to a first gas stream comprising carbon dioxide to form a carbonated fly ash. A steel slag is also carbonated that comprises >about 40% by weight of calcium oxide (CaO) and having a water content of >about 12% to <about 18% by weight of water by exposing the steel slag to a second gas stream comprising carbon dioxide to form a carbonated steel slag. The carbonated fly ash and the carbonated steel slag are suitable for use as engineered cementitious composite precursors in a bendable engineered cementitious composite composition that further comprises Portland cement, a polymeric fiber, and a superplasticizer.

A dry mortar, in particular a cementitious tile adhesive using fibers. A method improves the slip resistance, the flexibility, and/or the consistency of a dry mortar mixed up with water. Moreover, a structure, in particular a floor, a wall or a ceiling, includes a cover element, in particular a tile, whereby the cover element is fixed to the structure with a dry mortar mixed up with water.

A synchronous single-liquid grouting slurry, its technology and application for large diameter shield engineering under water-rich, high-pressure and weak soil strata conditions, comprising raw materials: 1050-1200 parts of gold tailing, 420-480 parts of silicate cement clinker, 220-240 parts of fly ash, 45-120 parts of waste clay brick, 65-95 parts of slag, 25-45 parts of limestone tailing, 70-80 parts of steel slag, 30-45 parts of silica fume, 15-22 parts of desulfurized gypsum, and 9-15 parts of quick-setting and early-strength composite additive. The invention controls the d.sub.50, d.sub.85 and d.sub.95 of the material particles as 35-40, 42-48 and 50-55 μm, respectively. Gold tailing with the particle size of 120-600 μm being used as the fine aggregate, their volume fractions are 40-60%. The slurry production technique, comprising crushing-sieving-superfine ball milling-homogenization-particle size classification-variable speed mixing being developed. The shield tail eight-point grouting technique is being developed for filling.

Provided are a textile reinforced cement composite for suppressing occurrence of slipping and a crack and a manufacturing method thereof. The textile reinforced cement composite for suppressing occurrence of slipping and a crack can suppress slipping between a textile grid reinforcement and a cement composite by using an angulated filling material mixed therewith when a textile reinforced cement composite having a textile grid reinforcement embedded in a cement composite is manufactured, suppress occurrence of a crack of the cement composite, suppress occurrence of a crack of the cement composite due to a fiber bridging reaction by using organic fiber mixed therewith, induce distribution of fine cracks, suppress degradation of fluidity of the cement composite caused by mixing of the angulated filling material by using a spherical binder and a chemical admixture added thereto, and suppress slipping between the textile grid reinforcement and the cement composite by using a fine powder binder having a predetermined particle size and mixed therewith.

The present invention relates to a compact and highly dense engineered concrete binder composition and a method of producing the same. In particular, the engineered concrete binder composition comprises at least one mechano-chemically modified component.

The present invention relates to a compact and highly dense engineered concrete binder composition and a method of producing the same. In particular, the engineered concrete binder composition comprises at least one mechano-chemically modified component.

Fresh concrete which contains in 1 m3 50 to 300 kg of water, 135 to 400 kg of cement or 135 to 600 kg of a mixture of cement and at least one substituent thereof, 10 to 150 kg of finely ground brick, ceramic, mixed or concrete recyclate having a particle size of 5 to 250 microns and a specific surface of 300 to 1500 m2/kg or 10 to 150 kg of a mixture of finely ground brick, ceramic, mixed or concrete recyclate having a particle size of 5 to 250 microns and a specific surface of 300 to 1500 m2/kg and microsilica and/or at least one substituent thereof, with a content of finely ground recyclate in this combination of at least 10% by weight, and 1000 to 2300 kg of aggregate.

A vegetal concrete masonry unit is provided which comprises cooked crop residues, binder and pulverized fuel ash in a mass ratio of 1:1:1.5 to 1:1.5:3.