A free-flowing powder composition includes at least one substrate having pores and an external surface between said pores, said surface functionalized with at least one accelerator for a hydraulic setting composition, said accelerator being liquid, hygroscopic, or deliquescent, and wherein after 15 minutes of immersion of free-flowing powder composition in water at 20° C. at least 80% in weight of said accelerator is solubilized, said free-flowing powder composition being immersed in an amount of water sufficient so that the saturation concentration of said accelerator cannot be reached. There is also a method for preparing said free-flowing powder composition. The use of said free-flowing powder composition as an additive for mortar or concrete composition provides an accelerating effect, an anti-ageing effect and an anti-dusting effect. A dry mortar or concrete composition includes a hydraulic binder, said free-flowing powder composition and a granulate, wet mortar or concrete composition and hardened body obtained therefrom.

A free-flowing powder composition includes at least one substrate having pores and an external surface between said pores, said surface functionalized with at least one accelerator for a hydraulic setting composition, said accelerator being liquid, hygroscopic, or deliquescent, and wherein after 15 minutes of immersion of free-flowing powder composition in water at 20° C. at least 80% in weight of said accelerator is solubilized, said free-flowing powder composition being immersed in an amount of water sufficient so that the saturation concentration of said accelerator cannot be reached. There is also a method for preparing said free-flowing powder composition. The use of said free-flowing powder composition as an additive for mortar or concrete composition provides an accelerating effect, an anti-ageing effect and an anti-dusting effect. A dry mortar or concrete composition includes a hydraulic binder, said free-flowing powder composition and a granulate, wet mortar or concrete composition and hardened body obtained therefrom.

The present invention refers to a process for making a calcium carbonate containing material, wherein the process includes a specific drying procedure and allows for the provision of calcium carbonate materials with reduced moisture pick-up and low porosity.

The present invention refers to a process for making a calcium carbonate containing material, wherein the process includes a specific drying procedure and allows for the provision of calcium carbonate materials with reduced moisture pick-up and low porosity.

Magnesium phosphate cement binder systems and method for providing magnesium phosphate cements are described. In an embodiment, a magnesium phosphate cement binder system may include magnesium oxide that has been calcined at a temperature of between about 900° F. to about 1800° F. The magnesium phosphate cement binder system may also include a phosphate material. Other formulations, compositions, and methods are also described.

Magnesium phosphate cement binder systems and method for providing magnesium phosphate cements are described. In an embodiment, a magnesium phosphate cement binder system may include magnesium oxide that has been calcined at a temperature of between about 900° F. to about 1800° F. The magnesium phosphate cement binder system may also include a phosphate material. Other formulations, compositions, and methods are also described.

Magnesium phosphate cement binder systems and method for providing magnesium phosphate cements are described. In an embodiment, a magnesium phosphate cement binder system may include magnesium oxide that has been calcined at a temperature of between about 900° F. to about 1800° F. The magnesium phosphate cement binder system may also include a phosphate material. Other formulations, compositions, and methods are also described.

Magnesium phosphate cement binder systems and method for providing magnesium phosphate cements are described. In an embodiment, a magnesium phosphate cement binder system may include magnesium oxide that has been calcined at a temperature of between about 900° F. to about 1800° F. The magnesium phosphate cement binder system may also include a phosphate material. Other formulations, compositions, and methods are also described.

Various embodiments disclosed relate to a weighted composition for treatment of a subterranean formation. In various embodiments, the present invention provides a method of treating a subterranean formation. The method can include placing in a subterranean formation a weighted composition. The weighted composition can include a weighting agent and an inorganic coating material on the weighting agent. The inorganic coating material can be a crystalline inorganic coating material. The inorganic coating material can be an amorphous inorganic coating material.

Various embodiments disclosed relate to a weighted composition for treatment of a subterranean formation. In various embodiments, the present invention provides a method of treating a subterranean formation. The method can include placing in a subterranean formation a weighted composition. The weighted composition can include a weighting agent and an inorganic coating material on the weighting agent. The inorganic coating material can be a crystalline inorganic coating material. The inorganic coating material can be an amorphous inorganic coating material.