An inverted roof and a method of installing the inverted roof, and in particular to an inverted roof including cellular glass insulation material having a protective alkali silicate coating on the upper surface of the cellular glass insulation material.

A high-strength geopolymer hollow microsphere, a preparation method thereof and a phase change energy storage microsphere are provided, including: dissolving sodium hydroxide, sodium silicate and spheroidizing aid in water to form a solution A, and adding active powder to the solution A, stirring and uniformly mixing to form a slurry B, adding the slurry B to an oil phase, stirring and dispersing into balls, filtering to obtain geopolymer microspheres I, washing the geopolymer microspheres I, and then carrying out a high-temperature calcination to obtain the high-strength geopolymer hollow microspheres II; using the high-strength geopolymer hollow microsphere as a carrier, absorbing a phase change material into the carrier, and mixing a microsphere carrying the phase change material with an epoxy resin, adding a powder dispersant and stirring to disperse the microsphere, after the epoxy resin is solidified, screening the superfluous powder dispersant to obtain the phase energy storage microsphere.

A high-strength geopolymer hollow microsphere, a preparation method thereof and a phase change energy storage microsphere are provided, including: dissolving sodium hydroxide, sodium silicate and spheroidizing aid in water to form a solution A, and adding active powder to the solution A, stirring and uniformly mixing to form a slurry B, adding the slurry B to an oil phase, stirring and dispersing into balls, filtering to obtain geopolymer microspheres I, washing the geopolymer microspheres I, and then carrying out a high-temperature calcination to obtain the high-strength geopolymer hollow microspheres II; using the high-strength geopolymer hollow microsphere as a carrier, absorbing a phase change material into the carrier, and mixing a microsphere carrying the phase change material with an epoxy resin, adding a powder dispersant and stirring to disperse the microsphere, after the epoxy resin is solidified, screening the superfluous powder dispersant to obtain the phase energy storage microsphere.

The present invention relates to a hydraulic binder composition comprising: at least one Portland cement; at least one amorphous calcium aluminate; calcium sulfate; at least one alkaline salt S chosen from K.sub.2CO.sub.3, Rb.sub.2CO.sub.3, Cs.sub.2CO.sub.3 and mixtures thereof; the composition being characterized in that the mass ratio of alkaline salt(s) S to amorphous calcium aluminate(s) ranges from 0.01 to 0.2.

Provided is a concrete hardener composition. The concrete hardener composition includes a sodium silicate compound, an acid compound and a balance amount of solvent. The sodium silicate compound includes sodium silicate or a mixture of sodium silicate and sodium methylsilicate. The acid compound includes acetic acid, glycolic acid, ethylenediaminetetraacetic acid, tartaric acid, nitric acid, boric acid or a combination thereof. The solvent includes water or a mixed solution of water and polyol. Based on the total weight of the concrete hardener composition, the content of silicon is between 5 wt % and 15 wt %, and the content of the acid compound is between 2 wt % and 30 wt %.

Provided is a concrete hardener composition. The concrete hardener composition includes a sodium silicate compound, an acid compound and a balance amount of solvent. The sodium silicate compound includes sodium silicate or a mixture of sodium silicate and sodium methylsilicate. The acid compound includes acetic acid, glycolic acid, ethylenediaminetetraacetic acid, tartaric acid, nitric acid, boric acid or a combination thereof. The solvent includes water or a mixed solution of water and polyol. Based on the total weight of the concrete hardener composition, the content of silicon is between 5 wt % and 15 wt %, and the content of the acid compound is between 2 wt % and 30 wt %.

To repair reinforced concrete easily and at low cost. An anticorrosion method includes infiltrating an anticorrosion solution held inside concrete of reinforced concrete into a vicinity of a reinforcing bar through the concrete to passivate the reinforcing bar, detecting that the anticorrosion solution is infiltrated to a surface of the concrete, and discharging, after detecting the anticorrosion solution, the anticorrosion solution to outside of the concrete to form an anticorrosive coating on a surface of the reinforcing bar.

To repair reinforced concrete easily and at low cost. An anticorrosion method includes infiltrating an anticorrosion solution held inside concrete of reinforced concrete into a vicinity of a reinforcing bar through the concrete to passivate the reinforcing bar, detecting that the anticorrosion solution is infiltrated to a surface of the concrete, and discharging, after detecting the anticorrosion solution, the anticorrosion solution to outside of the concrete to form an anticorrosive coating on a surface of the reinforcing bar.

The present disclosure relates to the field of dental material treatment, and particularly to a dental zirconia treatment technology. The specific technical solution is as follows: a zirconia treatment method, mainly involving color masking the zirconia, surface roughening the zirconia, coloring the zirconia, surface protection treatment and additional protective film treatment. Based on this treatment method, a brand-new color masking liquid, coloring liquid and adhesive solution are proposed. The present zirconia treatment technology not only meets the individualized requirements of patients for teeth, but also meets the requirements of dentists for convenient operation, so that it is of great value in application and popularization on the market.

The present disclosure relates to the field of dental material treatment, and particularly to a dental zirconia treatment technology. The specific technical solution is as follows: a zirconia treatment method, mainly involving color masking the zirconia, surface roughening the zirconia, coloring the zirconia, surface protection treatment and additional protective film treatment. Based on this treatment method, a brand-new color masking liquid, coloring liquid and adhesive solution are proposed. The present zirconia treatment technology not only meets the individualized requirements of patients for teeth, but also meets the requirements of dentists for convenient operation, so that it is of great value in application and popularization on the market.