A waterproofed gypsum board and associated method are provided, featuring the use of a mixture of magnesium oxide and a gypsum crystal modifier for improving the resistance to sagging of the waterproofed gypsum board, in particular, in moist and warm climatic conditions.

A waterproofed gypsum board and associated method are provided, featuring the use of a mixture of magnesium oxide and a gypsum crystal modifier for improving the resistance to sagging of the waterproofed gypsum board, in particular, in moist and warm climatic conditions.

Process for the production composite articles, comprising the steps of: a) providing a curable mixture comprising: 30-95 wt % of filler material, —5-70 wt % of resin, selected from unsaturated polyester resins, vinyl ester resins, (meth)acrylate resins, and combinations thereof, 0.5-10 phr of at least one peroxyester, 0.1-2.0 phr of at least one organic hydroperoxide, the weight ratio peroxyester/organic hydroperoxide being below 14.0, the curable mixture being essentially free of ketone peroxide, b) shaping the mixture, and c) heating the shaped mixture at a temperature in the range 60-100° C. to affect hardening of the resin and the formation of an article.

Process for the production composite articles, comprising the steps of: a) providing a curable mixture comprising: 30-95 wt % of filler material, —5-70 wt % of resin, selected from unsaturated polyester resins, vinyl ester resins, (meth)acrylate resins, and combinations thereof, 0.5-10 phr of at least one peroxyester, 0.1-2.0 phr of at least one organic hydroperoxide, the weight ratio peroxyester/organic hydroperoxide being below 14.0, the curable mixture being essentially free of ketone peroxide, b) shaping the mixture, and c) heating the shaped mixture at a temperature in the range 60-100° C. to affect hardening of the resin and the formation of an article.

There is provided a functional layer including a layered double hydroxide (LDH). The functional layer includes a first layer with a thickness of 0.10 μm or more, the first layer being composed of fine LDH particles having a diameter of less than 0.05 μm, and a second layer composed of large LDH particles having a mean particle diameter of 0.05 μm or more, the second layer being an outermost layer provided on the first layer.

There is provided a functional layer including a layered double hydroxide (LDH). The functional layer includes a first layer with a thickness of 0.10 μm or more, the first layer being composed of fine LDH particles having a diameter of less than 0.05 μm, and a second layer composed of large LDH particles having a mean particle diameter of 0.05 μm or more, the second layer being an outermost layer provided on the first layer.

A method of cementing a wellbore comprises injecting into the wellbore a cement slurry comprising an aqueous carrier, a swellable nanoclay, and a solid delayed releasing divalent inorganic salt comprising calcined magnesium oxide, calcined calcium oxide, calcium magnesium polyphosphate, a borate, a nitride, a silicate, an agent having a cation of Ba.sup.2+, Sr.sup.2+, Fe.sup.2+, Ni.sup.2+, or a combination comprising at least one of the foregoing; and allowing the cement slurry to set.

A method of cementing a wellbore comprises injecting into the wellbore a cement slurry comprising an aqueous carrier, a swellable nanoclay, and a solid delayed releasing divalent inorganic salt comprising calcined magnesium oxide, calcined calcium oxide, calcium magnesium polyphosphate, a borate, a nitride, a silicate, an agent having a cation of Ba.sup.2+, Sr.sup.2+, Fe.sup.2+, Ni.sup.2+, or a combination comprising at least one of the foregoing; and allowing the cement slurry to set.

There is provided a functional layer including a layered double hydroxide. The functional layer further contains titania.

There is provided a functional layer including a layered double hydroxide. The functional layer further contains titania.