A highly thixotropic 3D printing concrete and a manufacturing method therefor are provided. The weight percentage of each component calculated per cube of concrete is: 35-40% of cement, 0.1-0.4% of polycarboxylate superplasticizer, 0.1-0.4% of polypropylene fiber, 1.0-3.0% of special thixotropic agent for 3D printing concrete, and 12.5-14.5% of water, and the remainder is sand.

A highly thixotropic 3D printing concrete and a manufacturing method therefor are provided. The weight percentage of each component calculated per cube of concrete is: 35-40% of cement, 0.1-0.4% of polycarboxylate superplasticizer, 0.1-0.4% of polypropylene fiber, 1.0-3.0% of special thixotropic agent for 3D printing concrete, and 12.5-14.5% of water, and the remainder is sand.

Rheology modifiers comprising cross-linked poly(amino acid) and methods of their use in aqueous compositions. The modifiers comprise cross-linked poly(amino acid) microparticles having a mean equivalent diameter when fully swollen in deionized water of up to 1000 μm, as measured by laser diffraction. In particular, the poly(amino acid) is D-, L- or D,L-Y-poly(glutamic acid). A method of preparing the modifier comprises cross-linking a poly(amino acid), drying the cross-linked poly(amino acid) and grinding the cross-linked poly(amino acid) to have the required diameter.

A cementitious composition includes a Portland cement and at least one non-Portland hydratable cement selected from the group consisting of calcium sulfoaluminate cement, a calcium aluminosilicate cement, and calcium aluminate cement, wherein the Portland cement has a content of at least 10 percent based on the total weight of the non-Portland hydratable cement powder, wherein the cementitious composition is free of latex bonding agents, and wherein the cementitious composition is bondable to asphalt. The cementitious composition may also include an aggregate in the form of asphalt millings.

A cementitious composition includes a Portland cement and at least one non-Portland hydratable cement selected from the group consisting of calcium sulfoaluminate cement, a calcium aluminosilicate cement, and calcium aluminate cement, wherein the Portland cement has a content of at least 10 percent based on the total weight of the non-Portland hydratable cement powder, wherein the cementitious composition is free of latex bonding agents, and wherein the cementitious composition is bondable to asphalt. The cementitious composition may also include an aggregate in the form of asphalt millings.

To provide a blast furnace slag-type paint using a liquid inorganic material composed of a fluid suspension.

A blast furnace slag-type two-part paint in which a stabilized aqueous suspension containing the following blast furnace slags is contained as the main agent, an alkaline liquid having dissolved therein sodium silicate, sodium carbonate, or potassium carbonate that induces a hydraulic reaction of the suspension serves as the hydraulic reaction inducer, and the main agent and the hydraulic reaction inducer are separately packaged.

<Components of the main agent> (A) 0.5 to 42% by weight of a high-blast-furnace-slag-content blast furnace slag having a blast furnace slag content of 60% or more with respect to the total weight of the blast furnace slag; (B) 0.1 to 20% by weight of a blocking agent containing a phosphorus-containing compound; (C) 0.3 to 5%, preferably 0.3 to 2.5% of a blocking agent differing from a phosphorus-containing compound; (D) water retention agent; others.

To provide a blast furnace slag-type paint using a liquid inorganic material composed of a fluid suspension.

A blast furnace slag-type two-part paint in which a stabilized aqueous suspension containing the following blast furnace slags is contained as the main agent, an alkaline liquid having dissolved therein sodium silicate, sodium carbonate, or potassium carbonate that induces a hydraulic reaction of the suspension serves as the hydraulic reaction inducer, and the main agent and the hydraulic reaction inducer are separately packaged.

<Components of the main agent> (A) 0.5 to 42% by weight of a high-blast-furnace-slag-content blast furnace slag having a blast furnace slag content of 60% or more with respect to the total weight of the blast furnace slag; (B) 0.1 to 20% by weight of a blocking agent containing a phosphorus-containing compound; (C) 0.3 to 5%, preferably 0.3 to 2.5% of a blocking agent differing from a phosphorus-containing compound; (D) water retention agent; others.

A continuous flexible cement sheet roll for coating construction slabs, is disclosed. The sheet comprising a flexible cement layer, which has a thickness of between 0.3 to 6 mm, such as between 0.5 and 5 mm, and which comprises a) essentially inorganic mortar and b) up to 15% polymeric binder. When the amount of a component in a mixture is expressed in % units, the weight % of the component relative to the weight of the whole mixture is intended. The flexible cement sheet roll of the invention comprises, a reinforcing layer of a thickness lower than the thickness of said cement layer, selected from films of a nonwoven fabrics, layers of organic or inorganic fibers, polymer webs, chop strand mat, and fiberglass mats, among others.

A continuous flexible cement sheet roll for coating construction slabs, is disclosed. The sheet comprising a flexible cement layer, which has a thickness of between 0.3 to 6 mm, such as between 0.5 and 5 mm, and which comprises a) essentially inorganic mortar and b) up to 15% polymeric binder. When the amount of a component in a mixture is expressed in % units, the weight % of the component relative to the weight of the whole mixture is intended. The flexible cement sheet roll of the invention comprises, a reinforcing layer of a thickness lower than the thickness of said cement layer, selected from films of a nonwoven fabrics, layers of organic or inorganic fibers, polymer webs, chop strand mat, and fiberglass mats, among others.

The present invention is a ready-mixed, drying-type joint compound including an alkali sensitive component and a pH buffer system of a weak acid and its conjugate base to maintain pH of 8-12, typically for 120 days or more at 75° F. in a sealed container.