An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ultrastable cementitious material and a process for making the tile backer board.

A method to make an ultra-stable structural laminate of a cementitious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from .sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that inter-engages the cementitious material forming a matrix creating the ultra-stable structural laminate with fire resistance; a lateral nail pull strength from 44 pounds to 300 pounds of force; an insulation R value from 1 to 40; a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale; a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

A building with ultra-stable cementitious material with nano-molecular veneer has 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, a phosphorus-containing material, and wherein the mixture forms a liquid suspension that reacts into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer and a wall material that is affixed to a frame of a building.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ultrastable cementitious material and a process for making the tile backer board.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ulstrastable cementitious material and a process for making the tile backer board.

A building with ultra-stable cementitious material with nano-molecular veneer has 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, a phosphorus-containing material, and wherein the mixture forms a liquid suspension that reacts into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer and a wall material that is affixed to a frame of a building.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ulstrastable cementitious material and a process for making the tile backer board.

A method to make an ultra-stable structural laminate of a cementitious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from .sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that inter-engages the cementitious material forming a matrix creating the ultra-stable structural laminate with fire resistance; a lateral nail pull strength from 44 pounds to 300 pounds of force; an insulation R value from 1 to 40; a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale; a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ultrastable cementitious material and a process for making the tile backer board.

A ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer.