The present invention relates to the field of foam formation and stabilization, particularly foamed construction materials, such as cement. Disclosed are additives suitable to obtain mineral foams when added to the corresponding starting materials. The invention provides a ready-to-use product in the form of a solid particulate composition comprising hydrophobized particles (1) and catalytically active particles (2) as defined in claim 1. The invention further provides for manufacturing methods of such ready-to-use product.

The invention relates to a method for producing supersulfated cement, wherein pozzolanic and hydraulic aluminosilicate components and a calcium-sulfate-alkaline activation complex are mixed together. The calcium-sulfate-alkaline activation complex is produced by carrying out the following successive steps: a first step of mixing 70% by weight of calcium sulfate and 30% by weight of alkaline components; and subsequently; a second step of thermodynamically activating, by hot quenching, the calcium-sulfate-alkaline activation complex; and subsequently; a third step of cold quenching, by rapid mixing, the activated calcium-sulfate-alkaline activation complex with the pozzolanic aluminosilicate components.

The present invention provides a system, method, and apparatus for producing a dimensionally stable extruded board product for use in surface coverings. The board product may be a basalt casting powder-based product for use as a substrate for wall or other surface coverings or may be used as a core layer in a modular floor covering unit. The modular floor covering unit comprises multiple layers. The layers are a thin cut stone veneer layer, a core layer with a density similar to that of the thin cut stone veneer layer, and an optional magnetically receptive underlayment layer. Other layers or combinations of layers may also be used.

A soundproofing material including a porous body having a cell structure and including inorganic fibers other than asbestos, wherein an average cell diameter is more than 300 μm and 1000 μm or less, a bulk density is 0.007 to 0.024 g/cm.sup.3, and a flow resistivity is 170,000 to 2,000,000 Ns/m.sup.4.

A product includes an aerogel having a single bulk structure, the single bulk structure having at least one dimension greater than 10 millimeters. The single bulk structure includes a plurality of pores, where each pore has a largest diameter defined as a greatest distance between pore walls of the respective pore. In addition, an average of the largest diameters of a majority of the pores is within a specified range, and the plurality of pores are distributed substantially homogenously throughout the single bulk structure.

Fresh concrete which contains in 1 m3 50 to 300 kg of water, 135 to 400 kg of cement or 135 to 600 kg of a mixture of cement and at least one substituent thereof, 10 to 150 kg of finely ground brick, ceramic, mixed or concrete recyclate having a particle size of 5 to 250 microns and a specific surface of 300 to 1500 m2/kg or 10 to 150 kg of a mixture of finely ground brick, ceramic, mixed or concrete recyclate having a particle size of 5 to 250 microns and a specific surface of 300 to 1500 m2/kg and microsilica and/or at least one substituent thereof, with a content of finely ground recyclate in this combination of at least 10% by weight, and 1000 to 2300 kg of aggregate.

A composition for addition to a ceiling tile, flooring product, or other construction product may include microfibrillated cellulose and optionally an inorganic particulate material. The ceiling tile, flooring product, or other construction product may further include perlite, mineral wool, wood pulp, starch and other additives, where the wood pulp and other inorganic particulate materials are bonded to the microfibrillated cellulose. Methods of manufacturing the compound are also disclosed.

The invention belongs to the field of eliminating pollutant gases. In particular, the invention belongs to the field of pollutant gas-absorbing material such as CO2, SO2, NOx and VOCs.

The present invention relates to a fresh composite or composite paste and a composite material comprising aggregates of recycled concrete, porous carbon, a binder and optionally water, as well as to the method for manufacturing the composite and the use thereof for sanitizing air (indoor or outdoor). The invention also relates to an article (for example, an anti-noise wall, a tunnel lining, an indoor decoration, an item of street furniture, etc.) comprising the composite according to the invention.

A process for the production of a mineral foam includes separately preparing a slurry of cement and an aqueous foam, wherein the cement slurry includes water and Portland cement as well as calcium silicate hydrate crystallization seeds; contacting the slurry of cement with the aqueous foam to obtain a slurry of foamed cement; and casting the slurry of foamed cement and leave it to set.

A glassy carbon compact according to the present invention has a maximum inscribed sphere diameter of 5 mm or greater, comprises pores having diameters of 500 nm or less dispersed throughout the glassy carbon compact, and has a density of 1.1 g/cm.sup.3 or greater.