Photoluminescent sand preferably includes play sand, photoluminescent pigment, a powdered binder and a curing agent. The play sand is preferably mixed with the photoluminescent pigment to form a photo sand mix. The photo sand mix is then mixed with the powered binder and curing agent to form the photoluminescent sand mix. The photoluminescent sand mix is allowed to cure for between 3-7 days to form the photoluminescent sand.

A method for producing a ceramic composite includes: preparing a sintered body in a plate form containing a fluorescent material having a composition of a rare earth aluminate, and aluminum oxide; and eluting the aluminum oxide from the sintered body by contacting the sintered body with a basic substance, for example, contained in an alkali aqueous solution, and the dissolution amount of the fluorescent material eluted from the sintered body in the step of eluting the aluminum oxide is 0.5% by mass or less based on an amount of the fluorescent material contained in the sintered body as 100% by mass.

Disclosed is a colored luminescent composite pigment including an association of at least one luminescent pigment having an average particle size of between 50 and 2000 μm and at least one coloring agent. Also disclosed are compositions and materials including the pigment, to the method for the production thereof and to the use of same for coloring materials, particularly of a hydraulic binder composition.

Luminescent concrete compositions containing cement, fine aggregates such as sand, and a phosphor such as strontium aluminate. Glow-in-the-dark concrete products made therefrom and methods of producing such concrete products are also specified. The glow-in-the-dark concrete products demonstrate good mechanical strength (e.g. compressive strength) and skid resistance. The addition of phosphorescent strontium aluminate provides luminance that persists for up to 10 hours to the concrete products.

Luminescent concrete compositions containing cement, fine aggregates such as sand, and a phosphor such as strontium aluminate. Glow-in-the-dark concrete products made therefrom and methods of producing such concrete products are also specified. The glow-in-the-dark concrete products demonstrate good mechanical strength (e.g. compressive strength) and skid resistance. The addition of phosphorescent strontium aluminate provides luminance that persists for up to 10 hours to the concrete products.

Luminescent concrete compositions containing cement, fine aggregates such as sand, and a phosphor such as strontium aluminate. Glow-in-the-dark concrete products made therefrom and methods of producing such concrete products are also specified. The glow-in-the-dark concrete products demonstrate good mechanical strength (e.g. compressive strength) and skid resistance. The addition of phosphorescent strontium aluminate provides luminance that persists for up to 10 hours to the concrete products.

The present invention relates to a photoluminescent cementitious composition suitable for use in safety signs in accordance with DIN 67510-1 standard, characterized by including a hydraulic binder, an aggregate and/or a filler and at least a photoluminescent pigment selected from strontium aluminates or silicates doped with rare earths selected from europium and dysprosium. The invention also relates to the use of a photoluminescent pigment in the manufacturing of concrete articles with aesthetic quality given by persistent photoluminescent properties.

Luminescent concrete compositions containing cement, fine aggregates such as sand, and a phosphor such as strontium aluminate. Glow-in-the-dark concrete products made therefrom and methods of producing such concrete products are also specified. The glow-in-the-dark concrete products demonstrate good mechanical strength (e.g. compressive strength) and skid resistance. The addition of phosphorescent strontium aluminate provides luminance that persists for up to 10 hours to the concrete products.

Some phosphor powders can be difficult to form into ceramic compacts because they are difficult to sinter. As described herein, phosphor powders that can degrade under conventional sintering temperatures can be sintered by heating the powder at a lower temperature, such as less than 800° C., while the powder is under greater than atmospheric pressure, such as at least 0.05 GPa. Phosphor ceramic compacts prepared by this method, and light-emitting devices incorporating these phosphor ceramic compacts, are also described.

The invention relates to a solution for coloring and imparting fluorescence to a zirconia dental article, the solution comprising: •a solvent, •a coloring agent comprising ions selected from Tb, Er, Pr, Mn and combinations thereof, •a fluorescing agent comprising ions of Bi, the solution not comprising Fe ions in an amount above about 0.05 wt.-% with respect to the weight of the whole solution.