In an embodiment a ceramic material includes ZnO as main constituent, Y as a first additive, second additives including at least one compound containing a metal element, wherein the metal element is selected from the group consisting of Bi, Cr, Co, Mn, Ni and Sb, Si.sup.4+ as a first dopant and second dopants having at least one compound containing a metal cation from Al.sup.3+, B.sup.3+, or Ba.sup.2+, wherein a corresponds to a molar proportion of Bi calculated as Bi.sub.2O.sub.3, b corresponds to a molar proportion of Y calculated as Y.sub.2O.sub.3, c corresponds to a molar proportion of Al calculated as Al.sub.2O.sub.3, d corresponds to a molar proportion of Ba calculated as BaO, e corresponds to a molar proportion of B calculated as B.sub.2O.sub.3, f corresponds to a molar proportion of Si calculated as SiO.sub.2, g corresponds to a molar proportion of Ni calculated as NiO, h corresponds to a molar proportion of Co calculated as Co.sub.3O.sub.4, i corresponds to a molar proportion of Cr calculated as Cr.sub.2O.sub.3, j corresponds to a molar proportion of Sb calculated as Sb.sub.2O.sub.3, and k corresponds to a molar proportion of Mn calculated as Mn.sub.3O.sub.4.

To provide a sintered body with improved impact resistance due to impact absorption through plastic deformation before brittle fracture for an impact exceeding the fracture resistance of the sintered body, and/or a method for producing the sintered body.

A sintered body including: zirconia containing a stabilizer; and a region in which an impact mark is formed when an impact force is applied.

A lead-free piezoelectric material includes perovskite-type metal oxide containing Na, Nb, Ba, Ti, and Mg and indicates excellent piezoelectric properties. The piezoelectric material satisfies the following relational expression (1): 0.430≤a≤0.460, 0.433≤b≤0.479, 0.040≤c≤0.070, 0.0125≤d≤0.0650, 0.0015≤e≤0.0092, 0.9×3e≤c−d≤1.1×3e, a+b+c+d+e=1, where a, b, c, d, and e denote the relative numbers of Na, Nb, Ba, Ti, and Mg atoms, respectively.

When manufacturing a magnetic body which is made of a ferrite material containing Fe, Ni, and Zn, and whose Mn content is 0.1288 percent by mass or higher, or a magnetic body which is made of a ferrite material containing Fe, Ni, Zn, and Cu, and whose Mn content is 0.1178 percent by mass or higher, an iron oxide powder whose Mn content is 0.20 percent by mass or higher is used as a raw material powder.

Provided is a lead-free piezoelectric material reduced in dielectric loss tangent, and achieving both a large piezoelectric constant and a large mechanical quality factor. A piezoelectric material according to at least one embodiment of the present disclosure is a piezoelectric material including a main component formed of a perovskite-type metal oxide represented by the general formula (1): Na.sub.x+s(1−y)(Bi.sub.wBa.sub.1−s−w).sub.1−yNb.sub.yTi.sub.1−yO.sub.3 (where 0.84≤x≤0.92, 0.84≤y≤0.92, 0.002≤(w+s)(1−y)≤0.035, and 0.9≤w/s≤1.1), and a Mn component, wherein the content of the Mn is 0.01 mol % or more and 1.00 mol % or less with respect to the perovskite-type metal oxide.

When manufacturing a magnetic body whose primary component is Ni—Zn ferrite, an iron oxide powder whose Mn content is 0.20 to 0.85 percent by mass is used as a raw material powder, or, in addition to using an iron oxide powder whose Mn content is 0.20 percent by mass or higher as a raw material powder, a mol ratio of Ni to Zn (Ni/Zn) in the ferrite material is determined based on the Mn content in the iron oxide powder and the raw material powders are compounded in such a way that the mol ratio is achieved. The magnetic body does not contain any additives as essential components other than the primary components of the Ni—Zn ferrite material. A coil component using the magnetic body has excellent direct-current superimposition property and magnetic permeability.

A hard lead zirconate titanate (PZT) ceramic has an ABO.sub.3 structure with A sites and B sites. The PZT ceramic is doped with Mn and with Nb on the B sites and the ratio Nb/Mn is <2. A piezoelectric multilayer component having such a PZT ceramic and also a method for producing a piezoelectric multilayer component are also disclosed.

A dielectric material which satisfies X9M characteristics and ensures operations over an extended period of time at 200° C. is provided.

A method for producing MnZn-ferrite comprising Fe, Mn and Zn as main components, and at least Co, Si and Ca as sub-components, the main components in the MnZn-ferrite comprising 53-56% by mol (as Fe.sub.2O.sub.3) of Fe, and 3-9% by mol (as ZnO) of Zn, the balance being Mn as MnO, comprising the step of sintering a green body to obtain MnZn-ferrite; the sintering comprising a temperature-elevating step, a high-temperature-keeping step, and a cooling step; the high-temperature-keeping step being conducted at a keeping temperature of higher than 1050° C. and lower than 1150° C. in an atmosphere having an oxygen concentration of 0.4-2% by volume; the oxygen concentration being in a range of 0.001-0.2% by volume during cooling from 900° C. to 400° C. in the cooling step; and the cooling speed between (Tc+70)° C. and 100° C. being 50° C./hour or more, wherein Tc represents a Curie temperature (° C.) calculated from % by mass of Fe.sub.2O.sub.3 and ZnO.

A dielectric material which satisfies X9M characteristics and ensures operations over an extended period of time at 200° C. is provided.