The present invention relates to the field of foam formation and stabilization, particularly foamed construction materials, such as cement. Disclosed are additives suitable to obtain mineral foams when added to the corresponding starting materials. The invention provides a ready-to-use product in the form of a solid particulate composition comprising hydrophobized particles (1) and catalytically active particles (2) as defined in claim 1. The invention further provides for manufacturing methods of such ready-to-use product.

A manganese-zinc ferrite with a high magnetic permeability at negative temperature and low loss at high temperature consists of Fe.sub.2O.sub.3, MnO and ZnO, and additives consisting of CaCO.sub.3, ZrO.sub.2, Co.sub.2O.sub.3 and SnO.sub.2 are also added. A method for preparing the manganese-zinc ferrite is further provided. According to the method, by reasonably adjusting a ratio of Mn to Zn to Fe and appropriately increasing the content of Co in the additives, a manganese-zinc ferrite material with both a high magnetic permeability and low loss at about −20° C. and low loss at 120-140° C. is obtained. The manganese-zinc ferrite material has two loss valleys at about −20° C. and about 100° C. in a temperature range of −30° C. to 140° C., which expands the application range of the manganese-zinc ferrite material.

A capacitor component includes: a body including a dielectric layer and an internal electrode layer; and an external electrode disposed on the body, and connected to the internal electrode layer. A surface color of the body is R≤30, G≤30, B≤40 based on R/G/B, and a dielectric constant of the dielectric layer is 2000 or more and 4000 or less.

In an embodiment a ceramic material includes ZnO as main constituent, Y as a first additive, second additives including at least one compound containing a metal element, wherein the metal element is selected from the group consisting of Bi, Cr, Co, Mn, Ni and Sb, Si.sup.4+ as a first dopant and second dopants having at least one compound containing a metal cation from Al.sup.3+, B.sup.3+, or Ba.sup.2+, wherein a corresponds to a molar proportion of Bi calculated as Bi.sub.2O.sub.3, b corresponds to a molar proportion of Y calculated as Y.sub.2O.sub.3, c corresponds to a molar proportion of Al calculated as Al.sub.2O.sub.3, d corresponds to a molar proportion of Ba calculated as BaO, e corresponds to a molar proportion of B calculated as B.sub.2O.sub.3, f corresponds to a molar proportion of Si calculated as SiO.sub.2, g corresponds to a molar proportion of Ni calculated as NiO, h corresponds to a molar proportion of Co calculated as Co.sub.3O.sub.4, i corresponds to a molar proportion of Cr calculated as Cr.sub.2O.sub.3, j corresponds to a molar proportion of Sb calculated as Sb.sub.2O.sub.3, and k corresponds to a molar proportion of Mn calculated as Mn.sub.3O.sub.4.

The invention relates to a ceramic material, comprising lead zirconate titanate, which additionally contains K and optionally Cu. The ceramic material can be used in an electroceramic component, for example a piezoelectric actuator. The invention also relates to methods for producing the ceramic material and the electronic component.

The invention relates to a method for preparing a material based on an aluminosilicate selected from barium aluminosilicate BAS, barium-strontium aluminosilicate BSAS, and strontium aluminosilicate SAS, said aluminosilicate consisting of aluminosilicate with a hexagonal structure, characterised in that it includes a single sintering step in which a mixture of powders of precursors of said aluminosilicate, including an aluminium hydroxide Al(OH).sub.3 powder, are sintered by a hot-sintering technique with a pulsed electric field SPS; whereby a material based on an aluminosilicate, said aluminosilicate consisting of an aluminosilicate with a hexagonal structure is obtained. The material based on an aluminosilicate prepared by said method can be used in a method for preparing a composite material consisting of an aluminosilicate matrix reinforced by reinforcements made of metalloid or metal oxide.

Ceramic-bonded diamond composite particle includes a plurality of diamond grains and silicon carbide reaction bonded to the diamond grains having a composition of 60-90 wt. % diamond, 10-40 wt. % silicon carbide, ≦2 wt. % silicon. Particles are formed by processes that forms granules in a pre-consolidation process, forms a densified compact including ceramic-bonded diamond composite material in a consolidation process or forms ceramic-bonded diamond composite material directly, and a post-consolidation process in which the densified compact or ceramic-bonded diamond composite material is mechanically broken to form a plurality of the particles. Inert or active material can be incorporated into the densified compact or coated on granules to reduce the number and extent of diamond to silicon carbide bonding occurring in the consolidation process and make the ceramic-bonded diamond composite material more friable and easily breakable into composite particles.

A dielectric ceramic composition including a first component and a second component. The first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % an oxide of Sr of 0.00 mol % to 47.12 mol %, an oxide of Ba of 0.00 mol % to 51.22 mol %, an oxide of Ti of 0.00 mol % to 17.36 mol %, an oxide of Zr of 0.00 mol % to 17.36 mol %, an oxide of Sn of 0.00 mol % to 2.60 mol %, an oxide of Nb of 0.00 mol % to 35.32 mol %, an oxide of Ta of 0.00 mol % to 35.32 mol %, and an oxide of V of 0.00 mol % to 2.65 mol %. The second component includes (by mass) at least (a) an oxide of Mn of 0.005% to 3.500% and (b) one or both of an oxide of Cu of 0.080% to 20.000% and an oxide of Ru of 0.300% to 45.000%.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A dielectric composition and a multilayer capacitor including the same are disclosed. The dielectric composition including: a BaTiO.sub.3-based main ingredient; a first auxiliary ingredient including rare earth elements; and a second auxiliary ingredient including at least one of Ba and Ca but essentially including Ba, wherein the rare earth elements include Tb and Dy, and the first auxiliary ingredient and the second auxiliary ingredient satisfy a molar content condition of 0.40<(Tb/T_RE)*(Ba+Ca)<0.93, where T_RE is a total molar content of the rare earth elements in the first auxiliary ingredient.