Sintered product having a relative density of greater than 90%, with, to more than 80% of the volume thereof, a stack of flat ceramic platelets, the assembly of the platelets having a mean thickness of less than 3 μm, having a width of greater than 50 mm, and including more than 20% of alumina, as a percentage on the basis of the weight of the product. The width of the product is the largest dimension measured in the plane in which the length of the product is measured, along a direction perpendicular to the direction of the length. The length of the product is the largest dimension thereof in a plane parallel to the general plane in which the platelets extend.

The present disclosure includes proppants and methods of making the proppants. The proppants herein may contain titanium dioxide, silicon dioxide, and/or aluminum dioxide. Also included in the present disclosure are methods of using the proppants to treat a reservoir.

The present invention provides a polyvinyl acetal resin which leaves less fine undissolved matter when dissolved in an organic solvent and thus can improve productivity particularly when used as a binder for a ceramic green sheet, and which can also provide a ceramic green sheet having excellent toughness and enables production of a highly reliable multilayer ceramic capacitor. Provided is a polyvinyl acetal resin having: a wavenumber A (cm.sup.−1) of a peak within a range of 3,100 to 3,700 cm.sup.−1 in an IR absorption spectrum measured using an infrared spectrophotometer; and a hydroxy group content (mol %), the wavenumber A of the peak and the hydroxy group content satisfying relations of the following formulas (1) and (2):

[(3,470−A)/Hydroxy group content]≤5.5  (1)

(3,470−A)≤185  (2)

wherein A is a wavenumber which is lower than 3,470 cm.sup.−1 and at which a transmittance a (%) satisfying [100−(100−X)/2] is exhibited, where X (%) is a minimum transmittance of the peak within the wavenumber range of 3,100 to 3,700 cm.sup.−1.

To provide a sintered body with improved impact resistance due to impact absorption through plastic deformation before brittle fracture for an impact exceeding the fracture resistance of the sintered body, and/or a method for producing the sintered body.

A sintered body including: zirconia containing a stabilizer; and a region in which an impact mark is formed when an impact force is applied.

Green ceramic batch mixtures include: at least one inorganic batch component, preferably cordierite; at least one binder, preferably polyisoprene, poly(vinyl formal), poly(vinyl methyl ether), polybutadiene carboxy terminated; and an inverse emulsion having a continuous phase, an aqueous dispersed phase, and at least one emulsifier, preferably at least one functionalized silicone compound having at least one functional group chosen from a hydroxyl group, a carboxyl group, hydroxyl-terminated ethylene oxide groups.

Provided are metal oxide ceramic materials and intermediate materials thereof (e.g., nanozirconia gels, nanozirconia green bodies, pre-sintered ceramic bodies, zirconia dental ceramic materials, and dental articles). The nanozirconia gels are formable gels. Also provided are methods of making and using the metal oxide materials and intermediate materials. The nanozirconia gels can be made using, for example, osmotic processing. The nanozirconia gels can be used to make nanozirconia green bodies, pre-sintered ceramic bodies, zirconia dental ceramic materials, and dental article. The nanozirconia green bodies, pre-sintered ceramic bodies, zirconia dental ceramic materials, and dental articles have desirable properties (e.g., optical properties and mechanical properties).

A method for preparing dispersant using lignin degradation products includes preparation of lignin degradation products: degrading lignin which are used as raw materials using alkali through microwave-assisted activation at the presence of a metal oxide catalyst to obtain the lignin degradation products; and preparation of dispersant: preparing dispersant by molecularly reforming and chemically modifying the lignin degradation products obtained in the step of preparation of lignin degradation products.

Provided in one embodiment is a method of making, comprising: applying a hydrodynamic cavitation process to a raw material comprising particles comprising a metal-containing material or a carbon containing material of a first size to produce a slurry having particles comprising the metal-containing material or the carbon-containing material of a second size, smaller than the first size; and tape casting the slurry to form a green tape. Apparatuses employed to apply the method and the exemplary compositions made in accordance with the method are also provided.

The present invention relates to a kit of parts comprising a dental mill blank comprising a porous zirconia material and a colouring solution for colouring the porous zirconia material. The porous zirconia material comprises Zr oxide calculated as ZrO2: from 80 to 97 wt.-%, Al oxide calculated as Al2O3: from 0 to 0.15 wt.-%, Y oxide calculated as Y2O3: from 1 to 10 wt.-%, Bi oxide calculated as Bi2O3: from 0.01 to 0.2 wt.-%, the porous zirconia material not comprising Fe calculated as Fe2O3 in an amount of more than 0.01 wt.-%, wt.-% with respect to the weight of the porous zirconia material. The colouring solution comprises solvent(s), colouring agent(s) comprising metal ions selected from Tb, Er, Pr, Mn or combinations thereof, the solution not comprising Fe ions in an amount of more than 0.01 wt.-%, the solution not comprising Bi ions in an amount of more than 0.01 wt.-%, wt.-% with respect to the weight of the colouring solution. The invention also relates to a process of producing a dental restoration, the process comprising the steps: providing a dental mill blank comprising a porous zirconia material as described in any of the preceding claims, machining an article out of the porous zirconia material, the article having the shape of a dental restoration with an outer and inner surface, providing a colouring solution as described in any of the preceding claims, applying the colouring solution to at least portions of the surface of the article having the shape of a dental restoration.

A method of making a plurality of composite granules can include: forming green body granules comprising an aluminosilicate; heating the green body granules to form sintered granules; cooling the sintered granules according to a cooling regime, wherein the cooling regime comprises a temperature hold between 700° C. and 900° C. for at least one hour. In a particular embodiment, the aluminosilicate for making the composite granules can have a particle size less than 150 μm. The composite granules are particularly suitable as roofing granules and can have a desired combination of high solar reflectance SR and low lightness L*, a low bulk density, good weather resistance and strength.