The disclosure relates to tiles or slabs comprising a fired ceramic material which has a chemical composition with a particular combination of oxides; to a method for the manufacture of said tiles or slabs; and to the use thereof for construction or decoration applications.

A multilayer ceramic capacitor includes a multilayer body including dielectric layers, inner-electrode layers, and outer electrodes coupled to the inner-electrode layers. The multilayer body includes Ba, Ti, Ca, Mg, Zr, and R, and when the Ti content is defined as 100 parts by mole, the relative amounts are as follows: Ca, 0.03 parts by mole or more and 0.15 parts by mole or less, Mg, 0.01 parts by mole or more and 0.09 parts by mole or less, R, 2.5 parts by mole or more and 8.4 parts by mole or less; Zr, 0.05 parts by mole or more and 3.00 parts by mole or less: Si, 0.5 parts by mole or more and 4.0 parts by mole or less; and P, 0.005 parts by mole or more and 0.500 parts by mole or less. Ca is in a vicinity of the center of crystal grains contained in the dielectric layers.

The present disclosure includes proppants and methods of making the proppants. The proppants herein may contain titanium dioxide, silicon dioxide, and/or aluminum dioxide. Also included in the present disclosure are methods of using the proppants to treat a reservoir.

A ferrite sintered magnet comprising an M type Sr ferrite having a hexagonal structure as a main phase, wherein the ferrite sintered magnet comprises La and Co, a content of B is 0.005 to 0.9% by mass in terms of B.sub.2O.sub.3, a content of Zn is 0.01 to 1.2% by mass in terms of ZnO, and the ferrite sintered magnet satisfies [La]/[Zn]≤0.79 and [Co]/[Zn]≤0.67 when an atomic concentration of La is represented by [La], an atomic concentration of Co is represented by [Co], and an atomic concentration of Zn is represented by [Zn].

A composite polycrystal contains polycrystalline diamond formed of diamond grains that are directly bonded mutually, and compressed graphite dispersed in the polycrystalline diamond.

The invention relates to a method for preparing a material based on an aluminosilicate selected from barium aluminosilicate BAS, barium-strontium aluminosilicate BSAS, and strontium aluminosilicate SAS, said aluminosilicate consisting of aluminosilicate with a hexagonal structure, characterised in that it includes a single sintering step in which a mixture of powders of precursors of said aluminosilicate, including an aluminium hydroxide Al(OH).sub.3 powder, are sintered by a hot-sintering technique with a pulsed electric field SPS; whereby a material based on an aluminosilicate, said aluminosilicate consisting of an aluminosilicate with a hexagonal structure is obtained. The material based on an aluminosilicate prepared by said method can be used in a method for preparing a composite material consisting of an aluminosilicate matrix reinforced by reinforcements made of metalloid or metal oxide.

A novel metal oxide or a novel sputtering target is provided. A sputtering target includes a conductive material and an insulating material. The insulating material includes an oxide, a nitride, or an oxynitride including an element M1. The element M1 is one or more kinds of elements selected from Al, Ga, Si, Mg, Zr, Be, and B. The conductive material includes an oxide, a nitride, or an oxynitride including indium and zinc. A metal oxide film is deposited using the sputtering target in which the conductive material and the insulating material are separated from each other.

Provided is an inorganic structure including a plurality of zirconium silicate particles; and a binding part that covers a surface of each of the zirconium silicate particles and binds the zirconium silicate particles together. The binding part contains an amorphous compound containing silicon, a metallic element other than silicon, and oxygen, and contains substantially no alkali metal, B, V, Te, P, Bi, Pb and Zn. Also provided is a method for producing an inorganic structure including: a step for obtaining a mixture by mixing a plurality of zirconium silicate particles, a plurality of amorphous silicon dioxide particles, and an aqueous solution containing a metallic element other than silicon; and a step for pressurizing and heating the mixture under conditions of a pressure of 10 to 600 MPa and a temperature of 50 to 300° C.

A tableted catalyst support, characterized by an alpha-alumina content of at least 85 wt.-%, a pore volume of at least 0.40 mL/g, as determined by mercury porosimetry, and a BET surface area of 0.5 to 5.0 m.sup.2/g. The tableted catalyst support is an alpha-alumina catalyst support obtained with high geometrical precision and displaying a high overall pore volume, thus allowing for impregnation with a high amount of silver, while exhibiting a surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further provides a process for producing a tableted alpha-alumina catalyst support, which comprises i) forming a free-flowing feed mixture comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina; ii) tableting the free-flowing feed mixture to obtain a compacted body; and iii) heat treating the compacted body at a temperature of at least 1100° C., preferably at least 1300° C., more preferably at least 1400° C., in particular at least 1450° C., to obtain the tableted alpha-alumina catalyst support. The invention moreover relates to a compacted body obtained by tableting a free-flowing feed mixture which comprises, based on inorganic solids content, at least 50 wt.-% of a transition alumina having a loose bulk density of at most 600 g/L, a pore volume of at least 0.6 mL/g, as determined, and a median pore diameter of at least 15 nm. The invention moreover relates to a shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, comprising at least 15 wt.-% of silver, relative to the total weight of the catalyst, deposited on the tableted alpha-alumina catalyst support. The invention moreover relates to a process for producing ethylene oxide by gas-phase oxidation of ethylene, comprising reacting ethylene and oxygen in the presence of the shaped catalyst body.

Provided is a dielectric ceramic composition comprising a main component of forsterite and calcium strontium titanate. A content ratio of forsterite in the main component is from 84.0 to 92.5 parts by mole, and a content ratio of calcium strontium titanate is from 7.5 to 16.0 parts by mole. (Sr+Ca)/Ti in the calcium strontium titanate is from 1.03 to 1.20 in terms of a molar ratio. With respect to a total of 100 parts by mass of the main component and a subcomponent except for Li-containing glass, from 2 to 10 parts by mass of Li-containing glass is added. The Li-containing glass includes Al.sub.2O.sub.3 in an amount of from 1% by mass to 10% by mass.