A method of connecting two CMC substrates that includes providing two substrates; placing one substrate approximate to the other substrate, such that at least a portion of the two substrates overlap and define a brazing area; placing a brazing material approximate the brazing area; defining a primary raster pattern that encompasses the brazing area and a portion of the two substrates outside the brazing area; defining a secondary raster pattern that encompasses the brazing area; allowing a laser to scan the primary raster pattern to preheat the brazing area to a temperature below the brazing material's melting point; allowing the laser to scan the secondary raster pattern to heat the brazing area to a temperature that is above the brazing material's melting point; melting and allowing the brazing material to flow within the brazing area; and cooling the brazing area to form a brazed joint connecting the two substrates.

A method of joining a metal-ceramic substrate having metalization on at least one side to a metal body by using a metal alloy is disclosed. The metal body has a thickness of less than 1.0 mm, and the metal alloy contains aluminum and has a liquidus temperature of greater than 450° C. The resulting metal-ceramic module provides a strong bond between the metal body and the ceramic substrate. The resulting module is useful as a circuit carrier in electronic appliances, with the metal body preferably functioning as a cooling body.

To improve a TCT characteristic of a circuit substrate. The circuit substrate comprises a ceramic substrate including a first and second surfaces, and first and second metal plates respectively bonded to the first and second surfaces via first and second bonding layers. A three-point bending strength of the ceramic substrate is 500 MPa or more. At least one of L1/H1 of a first protruding portion of the first bonding layer and L2/H2 of a second protruding portion of the second bonding layer is 0.5 or more and 3.0 or less. At least one of an average value of first Vickers hardnesses of 10 places of the first protruding portion and an average value of second Vickers hardnesses of 10 places of the second protruding portion is 250 or less.

A milling device is rotatable in one direction around a longitudinal center axis defining a forward direction and an opposite rearward direction, and includes a front part and a rear part. The front part has cutting edges, each having a longitudinal extension, and chip flutes, each having a longitudinal extension. The front part is made of a monolithic piece of ceramic. The rear part is configured to be fixed in a rotatable tool body or a rotatable chuck. The rear part is also made of a monolithic piece of cemented carbide. A front end surface of the rear part has a smaller area than a rear end surface of the front part. The front end surface of the rear part and a rear end surface of the front part are permanently bonded or brazed to each other by a joint.

A method for manufacturing an electrostatic chuck with multiple chucking electrodes made of ceramic pieces using metallic aluminum as the joining. The aluminum may be placed between two pieces and the assembly may be heated in the range of 770 C to 1200 C. The joining atmosphere may be non-oxygenated. After joining the exclusions in the electrode pattern may be machined by also machining through one of the plate layers. The machined exclusion slots may then be filled with epoxy or other material. An electrostatic chuck or other structure manufactured according to such methods.

A carrier substrate (1) for electrical components, in particular metal-ceramic substrate (1) for electrical components, comprising an insulation layer (10), the insulation layer (10) preferably having a material comprising a ceramic or a composite comprising at least one ceramic layer, a component metallization (20) which is formed on a component side (BS) and has a first primary structuring (21), and a cooling part metallization (30) which is formed on a cooling side (KS) opposite the component side (BS) and has a second primary structuring (31), wherein the insulation layer (10), the component metallization (20) and the cooling part metallization (30) are arranged one above the other along a stacking direction (S), and
wherein the first primary structuring (21) and the second primary structuring (31), as viewed in the stacking direction (S), run congruently at least in portions.

The invention relates to a method for producing a metal-ceramic substrate and to a furnace suitable for carrying out the method. With the method, a metal-ceramic substrate with increased thermal and current conductivity can be obtained. The method comprises the steps of providing a stack containing a ceramic body, a metal foil, and a solder material in contact with the ceramic body and the metal foil, the solder material comprising a metal having a melting point of at least 700° C., a metal having a melting point of less than 700° C., and an active metal, and heating the stack, the stack passing through a heating zone for heating.

The present invention relates to a method for producing a metal-ceramic substrate. The method has the following steps: providing a stack containing a ceramic body, a metal foil, and a solder material in contact with the ceramic body and the metal foil, wherein the solder material has: a metal having a melting point of at least 700° C., a metal having a melting point of less than 700° C., and an active metal; and heating the stack, wherein at least one of the following conditions is satisfied: the high temperature heating duration is no more than 60 min; the peak temperature heating duration is no more than 30 min; the heating duration is no more than 60 min.

A method for manufacturing a metal-ceramic substrate (1) includes providing a ceramic layer (10), a metal layer (20) and a solder layer (30) coating the ceramic layer (10) and/or the metal layer (20) and/or the solder layer (30) with an active metal layer (40), arranging the solder layer (30) between the ceramic layer (10) and the metal layer (20) along a stacking direction (S), forming a solder system (35) comprising the solder layer and the active metal layer (40), wherein a solder material of the solder layer (30) is free of a melting point lowering material and bonding the metal layer (20) to the ceramic layer (10) via the solder system (35) by means of an active solder process.

An electric circuit board includes an insulating substrate, a metal plate, and a brazing material with which the insulating substrate and the metal plate are joined together. The metal plate has a side surface over which recessed portions are scattered. The side surface of the metal plate has lines in regions around the recessed portions. The metal plate is made of copper or a copper alloy. The brazing material has a side surface that is continuous with the side surface of the metal plate. The brazing material is a silver-copper brazing alloy. A ratio of copper on the side surface of the brazing material is higher than a copper component ratio of the silver-copper brazing alloy.