A full-fiber burner brick and a preparation method thereof, comprising mixing alumina crystal fiber and amorphous ceramic fiber with both of them being a combination of fibers of different lengths gradations, and moreover adding fine powder fillers of different particle size gradations and supplementing other additives. This enables the internal structure of the product more uniform, increases the bulk density of the product, and also benefits the suction filterability of fiber cotton blank, and is conducive to forming and improving the strength of the blank. The surface of the brick body is further provided with a coating, which can effectively protect the cotton fiber of the brick body fiber from harsh environments, improve its high temperature resistance, and help to extend the service life of the burner brick.

A full-fiber burner brick and a preparation method thereof, comprising mixing alumina crystal fiber and amorphous ceramic fiber with both of them being a combination of fibers of different lengths gradations, and moreover adding fine powder fillers of different particle size gradations and supplementing other additives. This enables the internal structure of the product more uniform, increases the bulk density of the product, and also benefits the suction filterability of fiber cotton blank, and is conducive to forming and improving the strength of the blank. The surface of the brick body is further provided with a coating, which can effectively protect the cotton fiber of the brick body fiber from harsh environments, improve its high temperature resistance, and help to extend the service life of the burner brick.

A vegetal concrete masonry unit is provided which comprises cooked crop residues, binder and pulverized fuel ash in a mass ratio of 1:1:1.5 to 1:1.5:3.

Foundry casting elements and methods of forming the same, the methods including: forming an aqueous slurry including an inorganic binder precursor, shaping the slurry using a pattern, curing the shaped slurry using a low temperature solidification process to form a casting element, and removing the pattern from the casting element.

Foundry casting elements and methods of forming the same, the methods including: forming an aqueous slurry including an inorganic binder precursor, shaping the slurry using a pattern, curing the shaped slurry using a low temperature solidification process to form a casting element, and removing the pattern from the casting element.

One variation of a method for fabricating a dermal heatsink includes: fabricating a substrate defining an interior surface, an exterior surface opposite the interior surface, and an open network of pores extending between the interior surface and the exterior surface; activating surfaces of the substrate and walls of the open network of pores; applying a coating over the substrate to form a heatsink, the coating comprising a porous, hydrophilic material and defining a void network; removing an excess of the coating from the substrate to clear blockages within the open network of pores by the coating; hydrating the heatsink during a curing period; heating the heatsink during the curing period to increase porosity of the coating applied over surfaces of the substrate; and rinsing the heatsink with an acid to decarbonate the coating along walls of the open network of pores in the substrate.

The present disclosure provides a high-temperature nano-composite coating and a preparation method thereof, and a small bag flexible packaging coating. The high-temperature nano-composite coating provided by the present disclosure controls the fiber length. Moreover, high-temperature reinforcing filler and high-temperature expansion filler are introduced, to make the coating have ultra-high strength at high temperature without cracks caused by shrinkage at high-temperature. In addition, nanopowder, high-temperature skeleton filler and other additives are introduced to make the coating be uniform and stable and reach a slurry state similar to toothpaste. There is no precipitation and stratification during the placement process. Small packaging can be realized to facilitate construction and operation. Besides, the coating has a good bonding to furnace lining, and will not fall off from the furnace lining, thereby prolonging the service life of the furnace lining.

An insulating material, in particular a permeable fire-proof insulating material comprising water glass and polystyrene, consisting of a hardening mixture which contains 1 to 32.4 wt % of expanded polystyrene, 57.5 to 96.0 wt % of aqueous sodium silicate solution, 2 to 6 wt % of aluminium hydroxide, 0.8 to 2.6 wt % water glass hardener and 0.1 to 0.5 wt % of water glass stabilizer, while the surface of the expanded polystyrene is provided with carbon black, the carbon black making up 0.1 to 1 wt % of total weight. A method for the production of insulating material, in particular a method for the production of permeable fire-proof insulating material comprising water glass and polystyrene, according to which firstly the polystyrene beads are mixed with an aqueous solution of carbon black so as to coat their entire surface, then is added to the aqueous sodium silicate solution aluminium hydroxide and the whole is mixed so as to form an insulating mixture, and then a water glass stabilizer is added to the aqueous sodium silicate solution, and then to this solution is mixed water glass hardener, with this solution being further stirred for 1 to 10 minutes to form a binder solution, and the insulating mixture is added to the binder solution with constant stirring, and the whole is mixed, and the resulting mixture is then poured into the application site.

A cement composition for plugging a honeycomb body, a plugged honeycomb body, and methods of plugging a honeycomb body are provided. The cement composition includes a source of inorganic particles, an inorganic binder, an organic binder, and a crosslinking agent that is capable of reacting with the inorganic binder and the organic binder. The cement composition can be dried without firing to form water-resistant plugs in a honeycomb body.

A process for producing a ceramic catalyst involves the steps of: a) providing functional particles having a catalytically inactive pore former as a support surrounded by a layer of a catalytically active material, b) processing the functional particles with inorganic particles to form a catalytic composition, c) treating the catalytic composition thermally to form a ceramic catalyst, wherein the ceramic catalyst comprises at least porous catalytically inactive cells which are formed by the pore formers in the functional particles, which are embedded in a matrix comprising the inorganic particles, which form a porous structure and which are at least partly surrounded by an active interface layer comprising the catalytically active material of the layer of the functional particles.

An SCR catalyst produced in by this method has an improved NO.sub.x conversion rate compared to a conventionally produced SCR catalyst.