A metering device (10) for withdrawing and dispensing a melt consisting of or containing an oxide fibre reinforced oxide ceramic composite material.

The present disclosure relates to a magnesium-based raw material and a preparation method thereof. According to the technical solution, 40-60 wt % fused magnesia particles, 30-40 wt % fine monoclinic zirconia powder, 5-20 wt % fine zirconium oxychloride powder, 0.5-1.5 wt % calcium hydroxide nanopowder, 0.2-0.5 wt % calcium hydroxide nanopowder, and 0.1-0.3 wt % maleic acid are stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder is mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 250-400° C. for 0.5-3 h, and finally cooled to room temperature.

A refractory has the form of a dry, mineral batch of fire-resistant mineral materials combined in such a way that refractories which are long-term resistant to fayalite-containing slags, sulfidic melts (mattes), sulfates and non-ferrous metal melts and are used for refractory linings in industrial non-ferrous metal melting furnaces can be manufactured. The refractory at least contains: —at least one coarse-grained olivine raw material as the main component; —magnesia (MgO) meal; —at least one fire-resistant reagent which, during the melting process, acts (in situ) in a reducing manner on non-ferrous metal oxide melts and/or non-ferrous metal iron oxide melts and converts same into non-ferrous metal melts.

A refractory has the form of a dry, mineral batch of fire-resistant mineral materials combined in such a way that refractories which are long-term resistant to fayalite-containing slags, sulfidic melts (mattes), sulfates and non-ferrous metal melts and are used for refractory linings in industrial non-ferrous metal melting furnaces can be manufactured. The refractory at least contains: —at least one coarse-grained olivine raw material as the main component; —magnesia (MgO) meal; —at least one fire-resistant reagent which, during the melting process, acts (in situ) in a reducing manner on non-ferrous metal oxide melts and/or non-ferrous metal iron oxide melts and converts same into non-ferrous metal melts.

Exemplary embodiments relate to a batch for producing an unshaped refractory ceramic product, to a method for producing a fired refractory ceramic product, to a fired refractory ceramic product and to the use of an unshaped refractory ceramic product.

Exemplary embodiments relate to a batch for producing an unshaped refractory ceramic product, to a method for producing a fired refractory ceramic product, to a fired refractory ceramic product and to the use of an unshaped refractory ceramic product.

Exemplary embodiments relate to a batch for producing an unshaped refractory ceramic product, to a method for producing a fired refractory ceramic product, to a fired refractory ceramic product and to the use of an unshaped refractory ceramic product.

The invention concerns a batch for the production of a refractory magnesia-carbon product or a refractory alumina-magnesia-carbon product, a process for the production of a refractory magnesia-carbon product or a refractory alumina-magnesia-carbon product, a refractory magnesia-carbon product or a refractory alumina-magnesia-carbon product as well as the use of a magnesia-carbon product or a refractory alumina-magnesia-carbon product.

A refractory material contains: 40 mass % or more of MgO; 4 to 30 mass % of a free carbon component; and one or more of B.sub.2O.sub.3, P.sub.2O.sub.5, SiO.sub.2 and TiO.sub.2, in a total amount of 0.3 to 3 mass %, with the remainder being at least one other type of additional refractory component. A void layer exists in an interface between a carbon-containing matrix microstructure residing at least on opposite sides of a maximum-size one of a plurality of MgO-containing particles in the refractory material, and the maximum-size MgO-containing particle. A sum of respective thicknesses of the void layer at two positions on the opposite sides is 0.2 to 3.0% of a ratio with respect to particle size of the maximum-size MgO-containing particle. An inorganic compound of MgO and the one or more of B.sub.2O.sub.3, P.sub.2O.sub.5, SiO.sub.2 and TiO.sub.2 exists entirety or partially in a surface of each of the MgO-containing particles.

A refractory material contains: 40 mass % or more of MgO; 4 to 30 mass % of a free carbon component; and one or more of B.sub.2O.sub.3, P.sub.2O.sub.5, SiO.sub.2 and TiO.sub.2, in a total amount of 0.3 to 3 mass %, with the remainder being at least one other type of additional refractory component. A void layer exists in an interface between a carbon-containing matrix microstructure residing at least on opposite sides of a maximum-size one of a plurality of MgO-containing particles in the refractory material, and the maximum-size MgO-containing particle. A sum of respective thicknesses of the void layer at two positions on the opposite sides is 0.2 to 3.0% of a ratio with respect to particle size of the maximum-size MgO-containing particle. An inorganic compound of MgO and the one or more of B.sub.2O.sub.3, P.sub.2O.sub.5, SiO.sub.2 and TiO.sub.2 exists entirety or partially in a surface of each of the MgO-containing particles.