A plasticizer may be suitable for resins and contain an amorphous propylenic polymer having a weight-average molecular weight (Mw), measured according to a GPC method, in a range of from 5,000 to 30,000 and having a molecular weight distribution (Mw/Mn) of 3.0 or less. The amorphous propylenic polymer may be a propylene homopolymer

A heterophasic propylene ethylene copolymer composition having an MFR.sub.2 in the range from 1.0 to 55.0 g/10 min and a melting temperature in the range from 155 to 162° C., comprising: i) from 60 to 88 wt.-% of a xylene cold insoluble fraction (XCI) having an intrinsic viscosity iV(XCI) in the range from 1.40 to 2.50 dl/g, an isotactic pentad concentration [mmmm] of more than 97.0% and a content of 2,1-regiodefects in the range from 0.1 to 0.4 mol %, ii) from 12 to 40 wt.-% of a xylene cold soluble fraction (XCS) having an intrinsic viscosity iV(XCS) in the range from 1.80 to 3.20 dl/g and an ethylene content C2(XCS) in the range from 25 to 80 wt.-%, wherein the ratio of the intrinsic viscosities of the two fractions, iV(XCS)/iV(XCI), is in the range from 1.0 to 2.0.

The present disclosure relates to comb-block copolymers and methods thereof. In some embodiments, a copolymer includes a first block comprising an ethylene-propylene copolymer; and a second block comprising a high density polyethylene. In some embodiments, a polyethylene composition includes the copolymer and a branched vinyl/vinylidene-terminated high density polyethylene. In some embodiments, a process for producing a polyethylene composition includes polymerizing ethylene, at a temperature of at least 100° C., by introducing the ethylene to a first catalyst system having a first catalyst compound and a first activator to form a branched vinyl/vinylidene-terminated high density polyethylene. The process includes introducing the branched vinyl/vinylidene-terminated high density polyethylene to additional ethylene, propylene, and a second catalyst system having a second catalyst compound and a second activator. The process includes obtaining the polyethylene composition.

To provide an olefin polymerization catalyst having high catalytic activity (polymerization activity), an olefin polymerization catalyst production method, and an olefin polymer production method using the olefin polymerization catalyst. An olefin polymerization catalyst comprising the following components [A], [B] and [C]:

the component [A]: a metallocene complex having a specific indenyl structure,

the component [B]: a solid component containing one or more selected from the group consisting of (b-1) a fine particulate carrier on which an ionic compound or Lewis acid which can convert the component [A] into a cation by reaction with the component [A], is supported, (b-2) solid acid fine particles, and (b-3) an ion-exchange layered compound,

and

the component [C]: a specific silylacetylene compound.

This invention relates to a novel group 2, 3 or 4 transition metal metallocene catalyst compound having at least one arenyl ligand substituted with: 1) a cyclopropyl group and, optionally, 2) at least one other group, such as a hydrocarbyl, a heteroatom or a heteroatom containing group.

The present invention relates to a transition metal compound that may exhibit high activity in olefin polymerization, and easily control the properties of synthesized olefin polymer such as a chemical structure, molecular weight distribution, a mechanical property, and the like, a catalyst composition comprising the same, and a method for olefin polymerization using the catalyst composition.

This invention relates to a novel metallocene compound, a catalyst composition comprising the metallocene compound, and a method for preparing olefin polymer using the catalyst composition.

[Problem to be Solved]

There is provided a process for producing an olefin polymer that is capable of producing an olefin polymer having high heat resistance and high molecular weight with excellent catalytic activity.

[Solution to Problem]

The process for producing an olefin polymer includes a step of polymerizing at least one olefin selected from ethylene and α-olefins having 4 to 30 carbon atoms in the presence of an olefin polymerization catalyst containing a transition metal compound represented by the general formula [I], the olefin polymer including constituent units derived from ethylene and α-olefins having 4 to 30 carbon atoms in a total amount between more than 50 mol % and not more than 100 mol %,

##STR00001##

[in the formula [I], R.sup.1, R.sup.3 and R.sup.5 to R.sup.16 are each independently a hydrogen atom, a hydrocarbon group or the like; R.sup.2 is a hydrocarbon group or the like; R.sup.4 is a hydrogen atom; M is a transition metal of Group IV; Q is a halogen atom or the like; and j is an integer of 1 to 4].

This invention relates to high porosity (≧15%) and/or low pore diameter (PD<165 μm) propylene polymers and propylene polymerization processes using single site catalyst systems with supports having high surface area (SA≧400 m.sup.2/g), low pore volume (PV≦2 mL/g), a specific mean pore diameter range (PD=1-20 nm), and high average particle size (PS≧30 μm).

This invention relates to a compound represented by the formula: T.sub.yLAMX.sub.n-2 wherein: A is a substituted or unsubstituted tetrahydro-as-indacenyl group bonded to M; L is substituted or unsubstituted monocyclic or polycyclic arenyl ligand or monocyclic or polycyclic heteroarenyl ligand bonded to M; M is a group 3, 4, 5, or 6 transition metal (preferably group 4); T is a bridging group bonded to L and A; y is 0 or 1, indicating the absence or presence of T; X is a leaving group, typically a univalent anionic ligand, or two Xs are joined and bound to the metal atom to form a metallocycle ring, or two Xs are joined to form a chelating ligand, a diene ligand, or an alkylidene; n is the oxidation state of M and is 3, 4, 5, or 6.