The present invention discloses a sound absorption material including an organic frame material; a binder; a thickener; and a plurality of sound absorption grains attached to the organic frame material via the binder, having a grain size in a range of 10-100 μm. The stability and the sound absorption performance of the sound absorption material have been effectively improved.

The present disclosure provides an aerogel comprising conductive polymers and cellulose nanofibrils (CNF). The present disclosure also provides a sensor comprising the aerogels of the present invention.

A method of melt blending a flame-retardant composition includes the steps: (a) heating a polymeric brominated flame retardant to a temperature of 5° C. or greater above the polymeric brominated flame retardants glass transition temperature as measured by Differential Scanning calorimetry, wherein the polymeric brominated flame retardant has a Temperature of 5% Mass Loss from 300° C. to 700° C. as measured according to Thermogravimetric Analysis; (b) mixing a polyolefin into the polymeric brominated flame retardant after step (a); and (c) mixing an inorganic filler into the polyolefin and polymeric brominated flame retardant after step (b) to form the flame-retardant composition.

A conductive film includes a cured material having a composition containing a conductive polymer and a binding resin, wherein a water content of the cured material after water absorption is 70% or less.

An object is to obtain a composition capable of: forming a uniform film even by spray coating or even when the composition is applied in the form of ink for inkjet printing; and preventing light emission from a portion other than an ITO electrode surface when the film is mounted on an organic EL device and light is emitted from the device. A conductive polymer composition contains: a composite containing a π-conjugated polymer (A) and a polymer (B) shown by a general formula (1); H.sub.2O (D) for dispersing the composite; a water-soluble organic solvent (C); and a compound (E) shown by a general formula (2). The electric conductivity of a film with a thickness of 20 to 200 nm formed from the conductive polymer composition is less than 1.00E-05 S/cm.

##STR00001##

Disclosed herein is a composite prepared by dispersing silver flakes in a polyvinyl alcohol (PVA), phosphoric acid (H.sub.3PO.sub.4), and poly(3,4-ethyl-ene-dioxythiophene) (PEDOT):poly(styrene sulfonic acid) (PSS) polymer mixture. The polymer blend can provides conductive pathways between the silver flakes, leading to superior electrical properties even at large deformations.

The present invention relates to a low-gloss heat-resistant ABS resin composition and its preparation method. The low-gloss heat-resistant ABS resin composition includes following components by weight: 100 parts of acrylonitrile-butadiene-styrene (ABS) resin, 5-30 parts of heat-resistant agent, 1-5 parts of matte masterbatch D, 0.2-1.0 parts of light stabilizer, and 0.5-2.0 parts of other additives. The preparation method includes steps of: stirring and fully mixing the above-mentioned raw materials in a high-speed mixer, and then feeding the raw materials into a twin-screw extruder through a metering device; melting and compounding the materials under the conveying, shearing and mixing of the screws, and then extruding, pulling, cooling and granulating, and finally obtaining the low-gloss heat-resistant ABS resin composition. The resin composition provided by the present invention not only has excellent mechanical properties, but also has an ultra-low gloss; therefore, it is very suitable for use in the field of automotive interior parts.

The present invention relates to a method for producing a polyelectrolyte complex (PEC) membrane having a predetermined porosity via salt dilution induced phase separation, in which a liquid polymer solution (P) containing polyanions (A) and polycations (C) dissolved in an aqueous medium at an overcritical salt concentration is exposed to an aqueous medium.

A crosslinked copolymer is provided, which includes a copolymer crosslinked by a crosslinking agent. The copolymer is copolymerized of (a) styrene-based monomer, (b) monomer having conjugated double bonds or acrylate ester monomer, and (c) ammonium-containing heterocyclic monomer. The crosslinking agent is (d) ##STR00001##
or the product of the reaction between ##STR00002##
and (e) ##STR00003##
or a combination thereof. Z is ##STR00004##
wherein each R.sup.1 is independently H or C.sub.1-4 alkyl group, each R.sup.2 is independently H or C.sub.1-4 alkyl group, R.sup.3 is single bond, —O—, —S—, —CH.sub.2—, or —NH—. n is a positive integer. x is 1 to 12, y is 1 to 5, and z is 1 to 5.

This disclosure provides systems, methods, and apparatus related to thermoelectric polymer aerogels. In one aspect, a method includes depositing a solution on a substrate. The solution comprises a thermoelectric polymer. Solvent of the solution is removed to form a layer of the thermoelectric polymer. The layer is placed in a polar solvent to form a gel comprising the thermoelectric polymer. The gel is cooled to freeze the polar solvent. The gel is placed in a vacuum environment to sublimate the polar solvent from the gel to form an aerogel comprising the thermoelectric polymer.