A method of manufacturing a coating is provided, which includes applying a primer paint on a substrate, wherein the primer paint includes 100 parts by weight of a first PVF, 30-70 parts by weight of an assistance resin, 5-30 parts by weight of a curing agent, 100-120 parts by weight of a first latent solvent, 3-methoxy-3-methyl-1-butanol, and water. The first latent solvent, 3-methoxy-3-methyl-1-butanol, and water have a weight ratio of 60:10-20:40-60. The method also applies a finish paint on the primer paint, wherein the finish paint includes 100 parts by weight of a second PVF, 100-120 parts by weight of a second latent solvent, 3-methoxy-3-methyl-1-butanol, and water, wherein the second latent solvent, 3-methoxy-3-methyl-1-butanol, and water have a weight ratio of 50:10-20:30-60. The primer paint and the finish paint are baked and dried to form a coating.

The present disclosure relates to methods and systems for making thermoplastic resin materials and composite resin systems and materials made from the thermoplastic resins, by seeding one melted thermoplastic material with a second thermoplastic material in a crystalline state that comprises an amount of ferromagnetic material.

The present disclosure relates to methods and systems for making thermoplastic resin materials and composite resin systems and materials made from the thermoplastic resins, by seeding one melted thermoplastic material with a second thermoplastic material in a crystalline state that comprises an amount of ferromagnetic material.

A method of manufacturing a coating is provided, which includes applying a primer paint on a substrate, wherein the primer paint includes 100 parts by weight of a first PVF, 30-70 parts by weight of an assistance resin, 5-30 parts by weight of a curing agent, 100-120 parts by weight of a first latent solvent, 3-methoxy-3-methyl-1-butanol, and water. The first latent solvent, 3-methoxy-3-methyl-1-butanol, and water have a weight ratio of 60:10-20:40-60. The method also applies a finish paint on the primer paint, wherein the finish paint includes 100 parts by weight of a second PVF, 100-120 parts by weight of a second latent solvent, 3-methoxy-3-methyl-1-butanol, and water, wherein the second latent solvent, 3-methoxy-3-methyl-1-butanol, and water have a weight ratio of 50:10-20:30-60. The primer paint and the finish paint are baked and dried to form a coating.

Disclosed is a method for manufacturing a separator. The method includes (S1) preparing a porous planar substrate having a plurality of pores, (S2) preparing a slurry containing inorganic particles dispersed therein and a polymer solution including a first binder polymer and a second binder polymer in a solvent, and coating the slurry on at least one surface of the porous substrate, (S3) spraying a non-solvent incapable of dissolving the second binder polymer on the slurry, and (S4) simultaneously removing the solvent and the non-solvent by drying. According to the method, a separator with good bindability to electrodes can be manufactured in an easy manner. In addition, problems associated with the separation of inorganic particles in the course of manufacturing an electrochemical device can be avoided.

An anti-bacterial and flame-retardant wall covering structure is provided. The wall covering structure includes a fiber substrate, two polyolefin substrates, and an anti-bacterial layer. The two polyolefin substrates are formed on both side surfaces of the fiber substrate to form a sandwich laminate. A polyolefin composition of each of the polyolefin substrates includes a first polyolefin resin material, a second polyolefin resin material, and a flame-retardant additive material. The first polyolefin resin material is a polyethylene resin, and the second polyolefin resin material is a polypropylene resin that includes a propylene block copolymer. Based on a total weight of the polyolefin composition being 100 parts by weight, a content of the propylene block copolymer is not less than 5 parts by weight. The anti-bacterial layer is formed on a surface of the sandwich laminate and includes a fluorine-containing polymer.

An anti-bacterial and flame-retardant wall covering structure is provided. The wall covering structure includes a fiber substrate, two polyolefin substrates, and an anti-bacterial layer. The two polyolefin substrates are formed on both side surfaces of the fiber substrate to form a sandwich laminate. A polyolefin composition of each of the polyolefin substrates includes a first polyolefin resin material, a second polyolefin resin material, and a flame-retardant additive material. The first polyolefin resin material is a polyethylene resin, and the second polyolefin resin material is a polypropylene resin that includes a propylene block copolymer. Based on a total weight of the polyolefin composition being 100 parts by weight, a content of the propylene block copolymer is not less than 5 parts by weight. The anti-bacterial layer is formed on a surface of the sandwich laminate and includes a fluorine-containing polymer.